Synthesis of an ordered nanoporous Cu/Ni/Au film for sensitive non-enzymatic glucose sensing.

ABSTRACT: Ordered nanoporous Cu/Ni/Au film was prepared by electrochemical deposition and magnetron sputtering using an anodic aluminium oxide template. The fabricated porous film has a uniform hexagonal pore size structure, a long-range ordered arrangement, and a pore diameter of approximately 40 nm. Following the dissolution of the template, the independent Cu/Ni/Au film is devolved to an ITO substrate as an effective non-enzyme glucose detection sensor. The sensor has good electrocatalytic performance with two specific linear ranges of 0.5 μM to 3.0 mM and 3.0-7.0 mM and high sensitivities of 4135 and 2972 μA mM^-1 cm^-2, respectively. The lower detection limit was 0.1 μM with a signal-to-noise ratio of 3. Additionally, the sensor features excellent selectivity and stability. These satisfactory results indicate that Cu/Ni/Au film is a promising platform for the development of non-enzymatic glucose sensors.

SUBMITTER: Liu G

PROVIDER: S-EPMC9051312 | biostudies-literature | 2020 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Synthesis of an ordered nanoporous Cu/Ni/Au film for sensitive non-enzymatic glucose sensing.

Liu Gang G Zhao Jianwei J Qin Lirong L Liu Song S Zhang Qitao Q Li Junxian J

RSC advances 20200331 22

Ordered nanoporous Cu/Ni/Au film was prepared by electrochemical deposition and magnetron sputtering using an anodic aluminium oxide template. The fabricated porous film has a uniform hexagonal pore size structure, a long-range ordered arrangement, and a pore diameter of approximately 40 nm. Following the dissolution of the template, the independent Cu/Ni/Au film is devolved to an ITO substrate as an effective non-enzyme glucose detection sensor. The sensor has good electrocatalytic performance ...[more]

PMID: 35492097

Similar Datasets

Controlled synthesized of ternary Cu-Co-Ni-S sulfides nanoporous network structure on carbon fiber paper: a superior catalytic electrode for highly-sensitive glucose sensing

Project description: Not available

| S-EPMC11210160 | biostudies-literature

Cu-Doped ZnO Nanoparticles for Non-Enzymatic Glucose Sensing.

Project description:Copper-doped zinc oxide nanoparticles (NPs) CuxZn1-xO (x = 0, 0.01, 0.02, 0.03, and 0.04) were synthesized via a sol-gel process and used as an active electrode material to fabricate a non-enzymatic electrochemical sensor for the detection of glucose. Their structure, composition, and chemical properties were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), Fourier-transform infrared (FTIR) and Raman spectroscopies, and zeta potential measurements. The electrochemical characterization of the sensors was studied using cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and differential pulse voltammetry (DPV). Cu doping was shown to improve the electrocatalytic activity for the oxidation of glucose, which resulted from the accelerated electron transfer and greatly improved electrochemical conductivity. The experimental conditions for the detection of glucose were optimized: a linear dependence between the glucose concentration and current intensity was established in the range from 1 nM to 100 μM with a limit of detection of 0.7 nM. The proposed sensor exhibited high selectivity for glucose in the presence of various interfering species. The developed sensor was also successfully tested for the detection of glucose in human serum samples.

| S-EPMC7916517 | biostudies-literature

Cu and Ni Co-sputtered heteroatomic thin film for enhanced nonenzymatic glucose detection.

Project description:In this work, we report a wafer-scale and chemical-free fabrication of nickel (Ni) and copper (Cu) heteroatomic Cu-Ni thin films using RF magnetron sputtering technique for non-enzymatic glucose sensing application. The as-prepared wafer-scale Cu-Ni thin films exhibits excellent electrocatalytic activity toward glucose oxidation with a 1.86 μM detection limit in the range of 0.01 mM to 20 mM range. The Cu-Ni film shows 1.3- and 5.4-times higher glucose oxidation activity in comparison to the Cu and Ni electrodes, respectively. The improved electrocatalytic activity is attributed to the synergistic effect of the bimetallic catalyst and high density of grain boundaries. The Cu-Ni electrodes also possessed excellent anti-interference characteristics. These results indicate that Cu-Ni heteroatomic thin film can be a potential candidate for the development of non-enzymatic glucose biosensor because of its chemical free synthesis, excellent reproducibility, reusability, and long-term stability.

| S-EPMC9079054 | biostudies-literature

Tunable Non-Enzymatic Glucose Electrochemical Sensing Based on the Ni/Co Bimetallic MOFs.

Project description:Constructing high-performance glucose sensors is of great significance for the prevention and diagnosis of diabetes, and the key is to develop new sensitive materials. In this paper, a series of Ni2Co1-L MOFs (L = H2BPDC: 4,4'-biphenyldicarboxylic acid; H2NDC: 2,6-naphthalenedicarboxylic acid; H2BDC: 1,4-benzenedicarboxylic acid) were synthesized by a room temperature stirring method. The effects of metal centers and ligands on the structure, compositions, electrochemical properties of the obtained Ni2Co1-L MOFs were characterized, indicating the successful preparation of layered MOFs with different sizes, stacking degrees, electrochemical active areas, numbers of exposed active sites, and glucose catalytic activity. Among them, Ni2Co1-BDC exhibits a relatively thin and homogeneous plate-like morphology, and the Ni2Co1-BDC modified glassy carbon electrode (Ni2Co1-BDC/GCE) has the highest electrochemical performance. Furthermore, the mechanism of the enhanced glucose oxidation signal was investigated. It was shown that glucose has a higher electron transfer capacity and a larger apparent catalytic rate constant on the Ni2Co1-BDC/GCE surface. Therefore, tunable non-enzymatic glucose electrochemical sensing was carried out by regulating the metal centers and ligands. As a result, a high-sensitivity enzyme-free glucose sensing platform was successfully constructed based on the Ni2Co1-BDC/GCE, which has a wide linear range of 0.5-2899.5 μM, a low detection limit of 0.29 μM (S/N = 3), and a high sensitivity of 3925.3 μA mM-1 cm-2. Much more importantly, it was also successfully applied to the determination of glucose in human serum with satisfactory results, demonstrating its potential for glucose detection in real samples.

| S-EPMC10420269 | biostudies-literature

Copper/reduced graphene oxide film modified electrode for non-enzymatic glucose sensing application.

Project description:Numerous studies suggest that modification with functional nanomaterials can enhance the electrode electrocatalytic activity, sensitivity, and selectivity of the electrochemical sensors. Here, a highly sensitive and cost-effective disposable non-enzymatic glucose sensor based on copper(II)/reduced graphene oxide modified screen-printed carbon electrode is demonstrated. Facile fabrication of the developed sensing electrodes is carried out by the adsorption of copper(II) onto graphene oxide modified electrode, then following the electrochemical reduction. The proposed sensor illustrates good electrocatalytic activity toward glucose oxidation with a wide linear detection range from 0.10 mM to 12.5 mM, low detection limit of 65 µM, and high sensitivity of 172 μA mM-1 cm-2 along with satisfactory anti-interference ability, reproducibility, stability, and the acceptable recoveries for the detection of glucose in a human serum sample (95.6-106.4%). The copper(II)/reduced graphene oxide based sensor with the superior performances is a great potential for the quantitation of glucose in real samples.

| S-EPMC8085015 | biostudies-literature

Tungsten oxide-Au nanosized film composites for glucose oxidation and sensing in neutral medium.

Project description:In this work, we report for the first time the use of tungsten oxide (WOx) as catalyst support for Au toward the direct electrooxidation of glucose. The nanostructured WOx/Au electrodes were synthesized by means of laser-ablation technique. Both micro-Raman spectroscopy and transmission electron microscopy showed that the produced WOx thin film is amorphous and made of ultrafine particles of subnanometer size. X-ray diffraction and X-ray photoelectron spectroscopy revealed that only metallic Au was present at the surface of the WOx/Au composite, suggesting that the WOx support did not alter the electronic structure of Au. The direct electrocatalytic oxidation of glucose in neutral medium such as phosphate buffered saline (pH 7.2) solution has been investigated with cyclic voltammetry, chronoamperometry, and square-wave voltammetry. Sensitivity as high as 65.7 μA cm(-2) mM(-1) up to 10 mM of glucose and a low detection limit of 10 μM were obtained with square-wave voltammetry. This interesting analytical performance makes the laser-fabricated WOx/Au electrode potentially promising for implantable glucose fuel cells and biomedical analysis as the evaluation of glucose concentration in biological fluids. Finally, owing to its unique capabilities proven in this work, it is anticipated that the laser-ablation technique will develop as a fabrication tool for chip miniature-sized sensors in the near future.

| S-EPMC4404941 | biostudies-literature

Self-Supported Cu/Fe<sub>3</sub>O<sub>4</sub> Hierarchical Nanosheets on Ni Foam for High-Efficiency Non-Enzymatic Glucose Sensing.

Project description:Electrochemical glucose sensors are vital for clinical diagnostics and the food industry, where accurate detection is essential. However, the limitations of glucose oxidase (GOx)-based sensors, such as complex preparation, high cost, and environmental sensitivity, highlight the need for non-enzymatic sensors that directly oxidize glucose at the electrode surface. In this study, a self-supporting hierarchical Cu/Fe3O4 nanosheet electrode was successfully fabricated by in situ growth on Ni Foam using a hydrothermal method, followed by annealing treatment. The Cu/Fe3O4 hierarchical nanosheet structure, with its large surface area, provides abundant active sites for electrocatalysis, while the strong interactions between Cu/Fe3O4 and Ni Foam enhance electron transfer efficiency. This novel electrode structure demonstrates exceptional electrochemical performance for non-enzymatic glucose sensing, with an ultrahigh sensitivity of 12.85 μA·μM-1·cm-2, a low detection limit of 0.71 μM, and a linear range extending up to 1 mM. Moreover, the Cu/Fe3O4/NF electrode exhibits excellent stability, a rapid response (~3 s), and good selectivity against interfering substances such as uric acid, ascorbic acid, H2O2, urea, and KCl. It also shows strong reliability in analyzing human serum samples. Therefore, Cu/Fe3O4/NF holds great promise as a non-enzymatic glucose sensor, and this work offers a valuable strategy for the design of advanced electrochemical electrodes.

| S-EPMC11857864 | biostudies-literature

General synthesis of hierarchical sheet/plate-like M-BDC (M = Cu, Mn, Ni, and Zr) metal-organic frameworks for electrochemical non-enzymatic glucose sensing.

Project description:Two-dimensional metal-organic frameworks (2D MOFs) are an attractive platform to develop new kinds of catalysts because of their structural tunability and large specific surface area that exposes numerous active sites. In this work, we report a general method to synthesize benzene dicarboxylic acid (BDC)-based MOFs with hierarchical 3D morphologies composed of 2D nanosheets or nanoplates. In our proposed strategy, acetonitrile helps solvate the metal ions in solution and affects the morphology, while polyvinylpyrrolidone (PVP) serves as a shape-control agent to assist in the nucleation and growth of MOF nanosheets. PVP also acts as a depletion agent to drive the assembly of the hierarchical sheet/plate-like M-BDC under solvothermal conditions. Further, we also demonstrate the flexibility of the proposed method using numerous coordinating metal ions (M = Cu, Mn, Ni, and Zr). The potential of these MOFs for electrochemical glucose sensing is examined using the hierarchical sheet-like Ni-BDC MOF as the optimum sample. It drives the electrocatalytic oxidation of glucose over a wide range (0.01 mM to 0.8 mM) with high sensitivity (635.9 μA mM-1 cm-2) in the absence of modification with carbon or the use of conductive substrates. It also demonstrates good selectivity with low limit of detection (LoD = 6.68 μM; signal/noise = 3), and fast response time (<5 s).

| S-EPMC8152586 | biostudies-literature

Tailoring Atomic Ordering Uniformity Enables Selectively Leached Nanoporous Pd-Ni-P Metallic Glass for Enhanced Glucose Sensing.

Project description:Constructing nanostructures, such as nanopores, within metallic glasses (MGs) holds great promise for further unlocking their electrochemical capabilities. However, the MGs typically exhibit intrinsic atomic-scale isotropy, posing a significant challenge in directly fabricating anisotropic nanostructures using conventional chemical synthesis. Herein a selective leaching approach, which focuses on tailoring the uniformity of atomic ordering, is introduced to achieve pore-engineered Pd-Ni-P MG. This innovative approach significantly boosts the number of exposed active sites, thereby enhancing the electrochemical sensitivity for glucose detection. Electrochemical tests reveal that the nanoporous Pd-Ni-P MG exhibits high sensitivity (3.19 mA mm⁻¹ cm⁻2) and remarkable stability (97.7% current retention after 1000 cycles). During electrochemical cycling, synchrotron X-ray pair distribution function and X-ray absorption fine structure analyses reveal that the distance between active sites decreases, enhancing electron transport efficiency, while the medium-range ordered structure of the Pd-Ni-P MG remains stable, contributing to its exceptional glucose sensing capabilities. A microglucose sensor is successfully developed by integrating the nanoporous Pd-Ni-P MG with a screen-printed electrode, demonstrating the practical applicability. This study not only offers a new avenue for the design of highly active nanoporous MGs but also sheds light on the mechanisms behind the high electrochemistry performance of MGs.

| S-EPMC11672269 | biostudies-literature

Highly sensitive non-enzymatic electrochemical glucose sensor based on dumbbell-shaped double-shelled hollow nanoporous CuO/ZnO microstructures.

Project description:A high-performance non-enzymatic glucose sensor based on hybrid metal-oxides is proposed. Dumbbell-shaped double-shelled hollow nanoporous CuO/ZnO microstructures (CuO/ZnO-DSDSHNM) were prepared via the hydrothermal method using pluronic F-127 as a surfactant. This structure is studied by various physicochemical characterizations such as scanning electron microscopy, X-ray diffraction spectroscopy, inductively coupled plasma atomic emission spectroscopy, elemental mapping techniques, X-ray photoelectron spectroscopy, and transmission electron microscopy. This unique CuO/ZnO-DSDSHNM provides both a large surface area and an easy penetrable structure facilitating improved electrochemical reactivity toward glucose oxidation. The prepared CuO/ZnO-DSDSHNM was used over the glassy carbon electrode (GCE) as the active material for glucose detection and then coated by Nafion to provide the proposed Nafion/CuO/ZnO-DSDSHNM/GCE. The fabricated glucose sensor exhibits an extremely wide dynamic range from 500 nM to 100 mM, a sensitivity of 1536.80 µA mM-1 cm-2, a low limit of detection of 357.5 nM, and a short response time of 1.60 s. The proposed sensor also showed long-term stability, good reproducibility, favorable repeatability, excellent selectivity, and satisfactory applicability for glucose detection in human serum samples. The achieved high-performance glucose sensing based on Nafion/CuO/ZnO-DSDSHNM/GCE shows that both the material synthesis and the sensor fabrication methods have been promising and they can be used in future researches.

| S-EPMC7801383 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data