Facile template-free synthesis of multifunctional 3D cellular carbon from edible rice paper.

ABSTRACT: Edible rice paper wrapper is found to be an interesting precursor of a porous and light-weight carbon material. During pyrolysis, material samples show significant differences in length change, displaying typical 20-25% shrinking in the in-plane directions, and strongly expanding (up to 500%) across their out-of-plane direction. This results in a template-free synthesis of a 3D network of cellular carbon material. The out-of-plane expansion also allows for fabrication of 3D shapes of cellular carbon material from the 2D precursor. The rice paper derived carbon material features a hierarchical porosity, resulting in a specific surface area ranging from 6 m² g^-1 to 239 m² g^-1 depending on the synthesis temperature. The carbon material has a density of 0.02-0.03 g cm^-3, and a higher modulus-density ratio than reported for other cellular carbon materials. It is mechanically stiff and exhibits excellent fire-resistant properties.

SUBMITTER: Islam M

PROVIDER: S-EPMC9053079 | biostudies-literature | 2020 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Facile template-free synthesis of multifunctional 3D cellular carbon from edible rice paper.

Islam Monsur M Weidler Peter G PG Heissler Stefan S Mager Dario D Korvink Jan G JG

RSC advances 20200427 28

Edible rice paper wrapper is found to be an interesting precursor of a porous and light-weight carbon material. During pyrolysis, material samples show significant differences in length change, displaying typical 20-25% shrinking in the in-plane directions, and strongly expanding (up to 500%) across their out-of-plane direction. This results in a template-free synthesis of a 3D network of cellular carbon material. The out-of-plane expansion also allows for fabrication of 3D shapes of cellular ca ...[more]

PMID: 35498854

Similar Datasets

Bacteria as Bio-Template for 3D Carbon Nanotube Architectures.

Project description:It is one of the most important needs to develop renewable, scalable and multifunctional methods for the fabrication of 3D carbon architectures. Even though a lot of methods have been developed to create porous and mechanically stable 3D scaffolds, the fabrication and control over the synthesis of such architectures still remain a challenge. Here, we used Magnetospirillum magneticum (AMB-1) bacteria as a bio-template to fabricate light-weight 3D solid structure of carbon nanotubes (CNTs) with interconnected porosity. The resulting porous scaffold showed good mechanical stability and large surface area because of the excellent pore interconnection and high porosity. Steered molecular dynamics simulations were used to quantify the interactions between nanotubes and AMB-1 via the cell surface protein MSP-1 and flagellin. The 3D CNTs-AMB1 nanocomposite scaffold is further demonstrated as a potential substrate for electrodes in supercapacitor applications.

| S-EPMC5575067 | biostudies-literature

Nitrogen-doped carbon paper with 3D porous structure as a flexible free-standing anode for lithium-ion batteries.

Project description:In this paper, a novel nitrogen-doped carbon paper (NCP) with both highly dense three-dimensional cellular structure and excellent bending flexibility is fabricated by pyrolyzing a melamine foam under compression. When serving as a free-standing anode for lithium-ion batteries, the NCP electrode delivers a reversible capacity up to 329.8 mA h g-1 after 200 cycles at 0.5 A g-1 (1.34 C) and 126.5 mA h g-1 after 500 cycles at 8.0 A g-1 (21.5 C). Such electrochemical performance is much higher than those of the counterparts prepared by pyrolysis without compression and can be mainly attributed to (a) the 3D highly dense interconnected carbon network with numerous junctions which can facilitate the efficient electron transfer and provide short transportation paths for lithium ions; and (b) the excellent mechanical flexibility and self-standing capability which exempt the use of binder, conductive additive and current collector. The NCP electrode implies a great promise of application in the high-performance Li-ion batteries for the flexible and wearable electronics.

| S-EPMC5552696 | biostudies-literature

Facile synthesis of dual-emission fluorescent carbon nanodots for a multifunctional probe.

Project description:In this study, we developed a facile method for synthesizing dual-emission carbon nanodots (CDs) through trimesic acid and o-phenylenediamine through electrolysis for 2 h. The synthesized CDs were mainly 3-7 nm in size, with an average size of 5.17 nm. The dual-emission fluorescent property of these CDs could be observed under two different excitation wavelengths. The green emission of the CDs could be quenched after the addition of mercury ions or copper ions, and the blue emission of the CDs could be inhibited using hydroxychloroquine (HCQ). Furthermore, the quenched fluorescence of CDs/Cu2+ could be recovered through the addition of glyphosate. We developed a multifunctional chemical sensor by using these special fluorescence materials. Under optimal conditions, the detection limits of mercury ions, glyphosate, and HCQ were 0.42 μM, 1.1 mg L-1, and 0.14 μM, respectively. Moreover, this method can be used to detect mercury ions, glyphosate, and HCQ in environmental water, cereals, and urine samples, respectively.

| S-EPMC9044676 | biostudies-literature

The facile synthesis of multifunctional PAMAM dendrimer conjugates through copper-free click chemistry.

Project description:The facile conjugation of three azido modified functionalities, namely a therapeutic drug (methotrexate), a targeting moiety (folic acid), and an imaging agent (fluorescein) with a G5 PAMAM dendrimer scaffold with cyclooctyne molecules at the surface through copper-free click chemistry is reported. Mono-, di-, and tri-functional PAMAM dendrimer conjugates can be obtained via combinatorial mixing of different azido modified functionalities simultaneously or sequentially with the dendrimer platform. Preliminary flow cytometry results indicate that the folic acid targeted nanoparticles are efficiently binding with KB cells.

| S-EPMC3331967 | biostudies-literature

Facile Fabrication of Fluorine-Free, Anti-Icing, and Multifunctional Superhydrophobic Surface on Wood Substrates.

Project description:Building superhydrophobic protective layers on the wood substrates is promising in terms of endowing them with multiple functions, including water-repellent, self-cleaning, anti-icing functions. In this study, multifunctional superhydrophobic wood was successfully fabricated by introducing SiO2 sol and superhydrophobic powder (PMHOS). The SiO2 sol was prepared using tetraethoxysilane as a precursor and ethanol was used as the dispersant. The PMHOS was synthesized using poly(methylhydrogen)siloxane (PMHS) and ethanol. As a result, the obtained superhydrophobic wood had a water contact angle (WCA) of 156° and a sliding angle (SA) of 6° at room temperature. The obtained superhydrophobic wood exhibited excellent repellency toward common liquid (milk, soy sauce, juice, and coffee). The superhydrophobic layer on the wood surface also exhibited good durability after a series of mechanical damages, including finger wiping, tape peeling, knife scratching, and sandpaper abrasion. In addition, the obtained superhydrophobic wood showed excellent anti-icing properties.

| S-EPMC9143972 | biostudies-literature

Facile and template-free synthesis of nano-macroporous LaCoO3 perovskite oxide for efficient diesel soot oxidation

Project description:The basic LaCoO3 perovskite oxides were prepared by the series of methods (reverse co-precipitation, citric acid aided sol–gel, glycine assisted solution combustion), underwent physicochemical characterization (XRD, FTIR, BET, XPS and SEM), followed by their soot oxidation activity tests in both “loose” and “tight” conditions of soot-catalyst contact. The activity tests revealed that the LaCoO3 catalyst formed using glycine assisted combustion synthesis gives the best performance with the T10, T50, and T90 at 361 °C, 404 °C and 445 °C, respectively, in loose contact conditions and T10, T50, and T90 at 306 °C, 330 °C and 355 °C, respectively, in tight contact conditions. Its outstanding performance can be attributed to its unique morphology consisting of scaffolds having an extensively interconnected macroporous network with macropores having nanoporous struts as walls as evidenced by SEM results. Such morphology makes the active sites of inner pores accessible to the gaseous (air) as well solid reactant (soot particles), thereby benefitting soot oxidation reaction. Supplementary Information The online version contains supplementary material available at 10.1007/s11144-022-02219-5.

| S-EPMC8981878 | biostudies-literature

Design and fabrication of hierarchically porous carbon with a template-free method.

Project description:Fabrication of hierarchically porous carbon materials (HPCs) with high surface area and pore volume has always been pursued. However, the currently effective template methods and acid/base activation strategies suffer from the drawbacks of either high costs or tedious steps. Herein, HPCs with 3D macro-mesopores and short-range meso-micropores were fabricated via an easy and sustainable two-step method from biomass. Macro-mesopores were constructed by slightly accumulation/aggregation of carbon spheres ranging from 60 nm to 80 nm, providing efficient mass diffusion pathways. Short-range mesopores and micropores with high electrolyte accessibility were developed in these spheres by air activation. The obtained HPCs showed surface area values up to 1306 m(2)/g and high mesopore volume proportion (63.9%). They demonstrated excellent capacitance and low equivalent series resistance (ESR) as supercapacitor electrode materials, suggesting the efficient diffusion and adsorption of electrolyte ions in the designed hierarchically porous structure.

| S-EPMC4162313 | biostudies-literature

Multifunctional auxetic and honeycomb composites made of 3D woven carbon fibre preforms.

Project description:Three dimensional (3D) woven composites started to find applications in various industrial sectors, mainly in aerospace and with a potential in automotive. 3D-woven fabrics can be architected to form complex and near-net-shape preforms ready for automated composites manufacturing. The 3D-woven honeycomb fabric is designed to include additional functionality into finished composites, such as positive and negative Poisson's ratios. In this study, complex honeycomb architectures were created using various weave designs to demonstrate the effects of auxetic behaviours when manufactured into a composite structure. A Staubli 3D-weaving system equipped with Jacquard UNIVAL 100 and creel of 3072 6 k carbon fibre tows were used to weave the designed honeycomb architecture. With the aid of hard polyester foam inserts, the 3D-woven fabrics were converted to honeycomb and auxetic preforms. These preforms were infused using epoxy resin to manufacture a set of honeycomb and auxetic composite structures. In comparison with the baseline honeycomb structure, it is proven that the developed auxetic composites exhibited negative Poisson's ratio of - 2.86 and - 0.12 in the case of tensile and compression tests respectively.

| S-EPMC9803643 | biostudies-literature

Post-Treatment-Free Dual-Interface Passivation via Facile 1D/3D Perovskite Heterojunction Construction.

Project description:For achieving high-efficiency perovskite solar cells, it is almost always necessary to substantially passivate defects and protect the perovskite structure at its interfaces with charge transport layers. Such a modification generally involves the post-treatment of the deposited perovskite film by spin coating, which cannot meet the technical demands of scaling up the production of perovskite photovoltaics. In this work, we demonstrate one-step construction of buried and capped double 1D/3D heterojunctions without the need for any post-treatment, which is achieved through facile tetraethylammonium trifluoroacetate (TEATFA) prefunctionalization on the SnO2 substrate. The functional TEATFA salt is first deposited onto the SnO2 substrate and reacts on this buried interface. Once the FAPbI3 perovskite precursor solution is dripped, a portion of the TEA+ cations spontaneously diffuse to the top surface over film crystallization. The TEATFA-based water-resistant 1D/3D TEAPbI3/FAPbI3 heterojunctions at both the buried and capped interfaces lead to much better photovoltaic performance and higher operational stability. Since this approach saves the need for any postsynthesis passivation, its feasibility for the fabrication of large-area perovskite photovoltaics is also showcased. Compared to ∼15% for a pristine 5 cm × 5 cm FAPbI3 mini-module without postsynthesis passivation, over 20% efficiency is achieved following the proposed route, demonstrating its great potential for larger-scale fabrication with fewer processing steps.

| S-EPMC10751777 | biostudies-literature

3D Polyaniline Nanofibers Anchored on Carbon Paper for High-Performance and Light-Weight Supercapacitors.

Project description:In the field of advanced energy storage, nanostructured Polyaniline (PANI) based materials hold a special place. Extensive studies have been done on the application of PANI in supercapacitors, however, the structure-property relationship of these materials is still not understood. This paper presents a detailed characterization of the novel sodium phytate doped 3D PANI nanofibers anchored on different types of carbon paper for application in supercapacitors. An excellent relationship between the structures and properties of the synthesized samples was found. Remarkable energy storage characteristics with low values of solution, charge transfer and polarization resistance and a specific capacitance of 1106.9 ± 1.5 F g-1 and 779 ± 2.6 F g-1 at current density 0.5 and 10 Ag-1, respectively, was achieved at optimized conditions. The symmetric supercapacitor assembly showed significant enhancement in both energy density and power density. It delivered an energy density of 95 Wh kg-1 at a power of 846 W kg-1. At a high-power density of 16.9 kW kg-1, the energy density can still be kept at 13 Wh kg-1. Cyclic stability was also checked for 1000 cycles at a current density of 10 Ag-1 having excellent retention, i.e., 96%.

| S-EPMC7696344 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data