Preparation of super-hydrophilic polyphenylsulfone nanofiber membranes for water treatment.

ABSTRACT: Electrospun nanofiber membrane-supported thin film composite (TFC) membranes exhibit great potential in water purification. In this work, electrospun polyphenylsulfone (PPSU) nanofiber membranes were prepared and modified by heat and plasma treatments. The resulting membranes were used as support layers for biomimetic TFC-based forward osmosis membranes. Thermal treatment transformed a loose non-woven nanofiber structure into a robust interconnected 3-dimensional PPSU network displaying a 930% increase in elastic modulus, 853% increase in maximum stress, and two-fold increase in breaking strain. Superior hydrophilicity of PPSU nanofiber membranes was achieved by low-pressure plasma treatment, changing the contact angle from 137° to 0°. The fabricated exemplary TFC-based forward osmosis membrane showed an osmotic water flux J _w > 14 L m^-2 h^-1 with a very low reserve salt flux J _s (J _s/J _w = 0.08 g L^-1) demonstrating the potential for making high quality membranes for water treatment using PPSU-based support layers for TFC membranes.

SUBMITTER: Wang Y

PROVIDER: S-EPMC9059319 | biostudies-literature | 2018 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Preparation of super-hydrophilic polyphenylsulfone nanofiber membranes for water treatment.

Wang Yan Y Górecki Radoslaw Pawel RP Stamate Eugen E Norrman Kion K Aili David D Zuo Min M Guo Weihong W Hélix-Nielsen Claus C Zhang Wenjing W

RSC advances 20181201 1

Electrospun nanofiber membrane-supported thin film composite (TFC) membranes exhibit great potential in water purification. In this work, electrospun polyphenylsulfone (PPSU) nanofiber membranes were prepared and modified by heat and plasma treatments. The resulting membranes were used as support layers for biomimetic TFC-based forward osmosis membranes. Thermal treatment transformed a loose non-woven nanofiber structure into a robust interconnected 3-dimensional PPSU network displaying a 930% i ...[more]

PMID: 35521605

Similar Datasets

Project description:Crystalline platinum nanoparticles supported on carbon nanofibers were synthesized for use as an electrocatalyst for polymer electrolyte membrane fuel cells. The nanofibers were prepared by a method of electrospinning from polymer solution with subsequent pyrolysis. Pt nanoneedles supported on polyacrylonitrile pyrolyzed electrospun nanofibers were synthesized by chemical reduction of H2[PtCl6] in aqueous solution. The synthesized electrocatalysts were investigated using scanning, high resolution transmission and scanning transmission electron microscopies, EDX analysis and electron diffraction. The shape and the size of the electrocatalyst crystal Pt nanoparticles were controled and found to depend on the method of H2[PtCl6] reduction type and on conditions of subsequent thermal treatment. Soft Pt reduction by formic acid followed by 100 °C thermal treatment produced needle-shape Pt nanoparticles with a needle length up to 25 nm and diameter up to 5 nm. Thermal treatment of these nanoparticles at 500 °C resulted in partial sintering of the Pt needles. When formic acid was added after 24 h from the beginning of platinization, Pt reduction resulted in small-size spherical Pt nanoparticle of less than 10 nm in diameter. Reduction of H2[PtCl6], preadsorbed on electrospun nanofibers in formic acid with further treatment in H2 flow at 500 °C, resulted in intensive sintering of platinum particles, with formation of conglomerates of 50 nm in size, however, individual particles still retain a size of less than 10 nm. Electrochemically active surface area (ECSA) of Pt/C catalyst was measured by electrochemical hydrogen adsorption/desorption measurements in 0.5 M H2SO4. ECSA of needle-shape Pt nanoparticles was 25 m2 g-1. It increased up to 31 m2 g-1 after thermal treatment at 500 °C, likely, due to amorphous structures removal from carbon nanofibers and retaining of Pt nanoneedle morphology. ECSA of small-size spherical Pt nanoparticles was 26 m2 g-1. Further thermal treatment at 500 °C in vacuum decreased ECSA down to 20 m2 g-1 due to Pt sintering and Pt active sites deactivation. The thermal treatment of small-size spherical Pt nanoparticles in H2 flow at 500 °C produced agglomerates of Pt nanoparticles with ECSA of 14 m2 g-1.

Dataset Information

Preparation of super-hydrophilic polyphenylsulfone nanofiber membranes for water treatment.

Publications

Preparation of super-hydrophilic polyphenylsulfone nanofiber membranes for water treatment.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets