Silicon/nitrogen synergistically reinforced flame-retardant PA6 nanocomposites with simultaneously improved anti-dripping and mechanical properties.

ABSTRACT: A facile route of 'copolymerization/blending' was proposed to fabricate silicon/nitrogen synergistically reinforced flame-retardant PA6 nanocomposites with simultaneously improved anti-dripping and mechanical properties. Firstly, a persistently inherent flame-retardant PA6 (FR-PA6), with 1,3-bis(3-aminopropyl)tetramethyl disiloxane (MSDS), was synthesized via controllable amidation and a polycondensation reaction. Melamine cyanurate (MCA) nanoparticles as a 'gas phase' synergistic agent were then added into FR-PA6 to further improve its flame retardancy. The primarily obtained FR-PA6 could be extinguished after a few melt droplets dropped as ignited, and passed the V-2 rating with enhanced mechanical properties, while PA6 had no rating (NR). The prepared FR-PA6/MCA nanocomposites could attain a limiting oxygen index (LOI) value of 32.7%, and passed the V-0 level with only 1 melting droplet with similar mechanical properties to PA6. Accordingly, the special 'condensed-gas phase' synergistic flame-retardant mechanism of FR-PA6/MCA nanocomposites was proposed through studying the residues and pyrolysis volatiles. This work provided a facile route as a model for developing functional PA6 for diverse engineering applications.

SUBMITTER: Fan S

PROVIDER: S-EPMC9061166 | biostudies-literature | 2019 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Silicon/nitrogen synergistically reinforced flame-retardant PA6 nanocomposites with simultaneously improved anti-dripping and mechanical properties.

Fan Shuo S Yuan Ruchao R Wu Dequn D Wang Xueli X Yu Jianyong J Li Faxue F

RSC advances 20190306 14

A facile route of 'copolymerization/blending' was proposed to fabricate silicon/nitrogen synergistically reinforced flame-retardant PA6 nanocomposites with simultaneously improved anti-dripping and mechanical properties. Firstly, a persistently inherent flame-retardant PA6 (FR-PA6), with 1,3-bis(3-aminopropyl)tetramethyl disiloxane (MSDS), was synthesized <i>via</i> controllable amidation and a polycondensation reaction. Melamine cyanurate (MCA) nanoparticles as a 'gas phase' synergistic agent w ...[more]

PMID: 35521176

Similar Datasets

Project description:In an effort to reduce the flammability of synthetic polymeric materials such as cotton fabrics and polyurethane foam (PUF), hybrid nanocoatings are prepared by layer-by-layer assembly. Multilayered nanocomposites of a cationic polyelectrolyte, poly(diallyldimethylammonium chloride) (PDDA), are paired with two kinds of clay nanoplatelets, montmorillonite (MMT) and vermiculite (VMT). The physical properties such as thickness and mass and thermal behaviors in clay-based nanocoatings with and without incorporation of tris buffer are compared to assess the effectiveness of amine salts on flame retardant (FR) performances. A PDDA-tris/VMT-MMT system, in which tris buffer is introduced into the cationic PDDA aqueous solution, produces a thicker and heavier coating. Three different systems, including PDDA/MMT, PDDA/VMT-MMT, and PDDA-tris/VMT-MMT, result in conformal coating, retaining the weave structure of the fabrics after being exposed to a vertical and horizontal flame test, while the uncoated sample is completely burned out. The synergistic effects of dual clay-based hybrid nanocoatings are greatly improved by adding amine salts. Cone calorimetry reveals that the PDDA-tris/VMT-MMT-coated PUF eliminates a second peak heat release rate and significantly reduces other FR performances, compared to those obtained from the clay-based multilayer films with no amine salts added. Ten bilayers of PDDA-tris/VMT-MMT (≈250 nm thick) maintain the shape of foam after exposure to a butane torch flame for 12 s. As for practical use of these nanocomposites in real fire disasters, spray-assisted PDDA-tris/VMT-MMT multilayers on woods exhibit high resistance over flammability. Improved fire resistance in PDDA-tris/VMT-MMT is believed to be due to the enhanced char yield through the addition of tris buffer that promotes the deposition of more clay particles while retaining a highly ordered deposition of a densely packed nanobrick wall structure. This work demonstrates the ability to impart significant fire resistance to synthetic polymer materials in a fully renewable nanocoating that uses environmentally benign chemistry.

Dataset Information

Silicon/nitrogen synergistically reinforced flame-retardant PA6 nanocomposites with simultaneously improved anti-dripping and mechanical properties.

Publications

Silicon/nitrogen synergistically reinforced flame-retardant PA6 nanocomposites with simultaneously improved anti-dripping and mechanical properties.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets