N-Enriched carbon nanofibers for high energy density supercapacitors and Li-ion batteries.

ABSTRACT: Nitrogen enriched carbon nanofibers have been obtained by one-step carbonization/activation of PAN-based nanofibers with various concentrations of melamine at 800 °C under a N₂ atmosphere. As synthesised carbon nanofibers were directly used as electrodes for symmetric supercapacitors. The obtained PAN-MEL fibers with 5% melamine stabilised at 280 °C and carbonized at 800 °C under a nitrogen atmosphere showed excellent electrochemical performance with a specific capacitance of up to 166 F g^-1 at a current density of 1A g^-1 using 6 M KOH electrolyte and a capacity retention of 109.7% after 3000 cycles. It shows a 48% increase as compared to pristine carbon nanofibers. Two electrode systems of the CNFM5 sample showed high energy densities of 23.72 to 12.50 W h kg^-1 at power densities from 400 to 30 000 W kg^-1. When used as an anode for Li-ion battery application the CNFM5 sample showed a high specific capacity up to 435.47 mA h g^-1 at 20 mA g^-1, good rate capacity and excellent cycling performance (365 mA h g^-1 specific capacity even after 200 cycles at 100 mA g^-1). The specific capacity obtained for these nitrogen enriched carbon nanofibers is higher than that for pristine carbon nano-fibers.

SUBMITTER: Kale SB 

PROVIDER: S-EPMC9075030 | biostudies-literature | 2019 Nov

REPOSITORIES: biostudies-literature