Sealing of anodized magnesium alloy AZ31 with MgAl layered double hydroxides layers.

ABSTRACT: In this work, anodized magnesium alloy AZ31 with and without boiling water sealing was pre-prepared, and then MgAl-layered double hydroxide (LDH) films were fabricated on it through hydrothermal chemical conversion of the pre-prepared anodic layer. The morphology, structure, and composition of the films were characterized by XRD, SEM, EDS, FT-IR, XPS and GDOES. It was found that the porosity of the films was reduced after in situ fabrication of the LDHs. The effects of boiling water sealing treatment on the anodized substrate were also discussed. Moreover, the polarization curve, EIS, and immersion tests showed that LDHs fabricated on the anodized substrate with boiling water sealing treatment exhibited a significant long period of protection for the substrate.

SUBMITTER: Zhang G

PROVIDER: S-EPMC9077258 | biostudies-literature | 2018 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Sealing of anodized magnesium alloy AZ31 with MgAl layered double hydroxides layers.

Zhang Gen G Wu Liang L Tang Aitao A Weng Bo B Atrens Andrej A Ma Shida S Liu Lei L Pan Fusheng F

RSC advances 20180109 5

In this work, anodized magnesium alloy AZ31 with and without boiling water sealing was pre-prepared, and then MgAl-layered double hydroxide (LDH) films were fabricated on it through hydrothermal chemical conversion of the pre-prepared anodic layer. The morphology, structure, and composition of the films were characterized by XRD, SEM, EDS, FT-IR, XPS and GDOES. It was found that the porosity of the films was reduced after in situ fabrication of the LDHs. The effects of boiling water seali ...[more]

PMID: 35541445

Similar Datasets

Effect of Drying on the Fabrication of MgAl Layered Double Hydroxides.

Project description:This study aimed to evaluate the synthesis of MgAl/LDH from the drying process perspective, evaluating the influence of temperature (75-90 °C) and time (16-20 h) in the drying process. The synthesis was performed, maintaining a ratio of 2:1 of Mg/Al, and the drying was conducted according to a 22 experimental design: four axial points and three repetitions at the central point. The surface area and pore diameter ranged from 4.09 to 18.55 m2/g and 12.50 to 24.46 nm. Fourier transform infrared (FTIR) analysis indicated the drying-caused variation of the LDH typical bands intensities. Scanning electron microscopy (SEM) images showed the tendency of the increase of agglomeration with the temperature elevation. The drying parameters' influence was evident for X-ray diffraction (XRD) analysis observing the crystallite size increment, from 13.10 to 38.94 nm, and basal spacing variation, from 7.52 to 7.64 Å. The statistical models for growing crystal and reduction of the basal spacing were physically consistent but with low values of R 2. The drying time and temperature had a considerable influence on the chemical, physical, structural, and morphological properties of LDH.

| S-EPMC8388087 | biostudies-literature

Intercalation and structural aspects of macroRAFT agents into MgAl layered double hydroxides.

Project description:Increasing attention has been devoted to the design of layered double hydroxide (LDH)-based hybrid materials. In this work, we demonstrate the intercalation by anion exchange process of poly(acrylic acid) (PAA) and three different hydrophilic random copolymers of acrylic acid (AA) and n-butyl acrylate (BA) with molar masses ranging from 2000 to 4200 g mol-1 synthesized by reversible addition-fragmentation chain transfer (RAFT) polymerization, into LDH containing magnesium(II) and aluminium(III) intralayer cations and nitrates as counterions (MgAl-NO3 LDH). At basic pH, the copolymer chains (macroRAFT agents) carry negative charges which allowed the establishment of electrostatic interactions with the LDH interlayer and their intercalation. The resulting hybrid macroRAFT/LDH materials displayed an expanded interlamellar domain compared to pristine MgAl-NO3 LDH from 1.36 nm to 2.33 nm. Depending on the nature of the units involved into the macroRAFT copolymer (only AA or AA and BA), the intercalation led to monolayer or bilayer arrangements within the interlayer space. The macroRAFT intercalation and the molecular structure of the hybrid phases were further characterized by Fourier transform infrared (FTIR) and solid-state 13C, 1H and 27Al nuclear magnetic resonance (NMR) spectroscopies to get a better description of the local structure.

| S-EPMC5238628 | biostudies-literature

Effect of SiC Nanoparticles on AZ31 Magnesium Alloy.

Project description:Magnesium alloys are attractive for the production of lightweight parts in modern automobile and aerospace industries due to their advanced properties. Their mechanical properties are usually enhanced by the incorporation with reinforcement particles. In the current study, reinforced AZ31 magnesium alloy was fabricated through the addition of bulk Al and the incorporation of SiC nanoparticles using a stir casting process to obtain AZ31-SiC nanocomposites. Scanning electron microscope (SEM) investigations revealed the formation of Mg17Al12 lamellar intermetallic structures and SiC clusters in the nanocomposites. Energy dispersive spectroscopy (EDS) detected the uniform distribution of SiC nanoparticles in the AZ31-SiC nanocomposites. Enhancements in hardness and yield strength (YS) were detected in the fabricated nanocomposites. This behavior was referred to a joint strengthening mechanisms which showed matrix-reinforcement coefficient of thermal expansion (CTE) and elastic modulus mismatches, Orowan strengthening, and load transfer mechanism. The mechanical properties and wear resistance were gradually increased with an increase in SiC content in the nanocomposite. The maximum values were obtained from nanocomposites containing 1 wt% of SiC (AZ31-1SiC). AZ31-1SiC nanocomposite YS and hardness were improved by 27% and 30%, respectively, compared to AZ31 alloy. This nanocomposite also exhibited the highest wear resistance; its wear mass loss and depth of the worn surface decreased by 26% and 15%, respectively, compared to AZ31 alloy.

| S-EPMC8839706 | biostudies-literature

AZ31 Magnesium Alloy Foils as Thin Anodes for Rechargeable Magnesium Batteries.

Project description:In recent decades, rechargeable Mg batteries (RMBs) technologies have attracted much attention because the use of thin Mg foil anodes may enable development of high-energy-density batteries. One of the most critical challenges for RMBs is finding suitable electrolyte solutions that enable efficient and reversible Mg cells operation. Most RMB studies concentrate on the development of novel electrolyte systems, while only few studies have focused on the practical feasibility of using pure metallic Mg as the anode material. Pure Mg metal anodes have been demonstrated to be useful in studying the fundamentals of nonaqueous Mg electrochemistry. However, pure Mg metal may not be suitable for mass production of ultrathin foils (<100 microns) due to its limited ductility. The metals industry overcomes this problem by using ductile Mg alloys. Herein, the feasibility of processing ultrathin Mg anodes in electrochemical cells was demonstrated by using AZ31 Mg alloys (3 % Al; 1 % Zn). Thin-film Mg AZ31 anodes presented reversible Mg dissolution and deposition behavior in complex ethereal Mg electrolytes solutions that was comparable to that of pure Mg foils. Moreover, it was demonstrated that secondary Mg battery prototypes comprising ultrathin AZ31 Mg alloy anodes (≈25 μm thick) and Mgx Mo6 S8 Chevrel-phase cathodes exhibited cycling performance equal to that of similar cells containing thicker pure Mg foil anodes. The possibility of using ultrathin processable Mg metal anodes is an important step in the realization of rechargeable Mg batteries.

| S-EPMC8596635 | biostudies-literature

Effect of Divalent Metals on the UV-Shielding Properties of MII/MgAl Layered Double Hydroxides.

Project description:Both the particle size and compositions have a strong influence on the UV-shielding performance of layered double hydroxides (LDHs), and they will interact with each other. To investigate the effects of divalent metal ions on the UV-shielding properties of layered double hydroxides (LDHs), MII/MgAl-CO3 LDHs (M = Mg, Co, Ni, Cu, or Zn) with the same primary and secondary particle size have been prepared and their UV-shielding performance have been studied in this work. The UV-vis spectra show that the ZnMgAl-LDHs exhibit the highest absorbance under the ultraviolet B and ultraviolet A rays among these LDH samples, but in the ultraviolet C region, the CuMgAl-LDHs show the highest absorbance and this result is in good accordance with the UV-shielding performance, which was examined by protecting the photocatalytic degradation of rhodamine B aqueous solution. Moreover, under UV rays, PP/ZnMgAl-LDH films show excellent resistance to UV aging, which can be attributed to the strong inhibition of ZnMgAl-LDHs during the production of free radicals in polypropene, as has been confirmed by electron spin resonance results.

| S-EPMC6648468 | biostudies-literature

Potential Sustainable Slow-Release Fertilizers Obtained by Mechanochemical Activation of MgAl and MgFe Layered Double Hydroxides and K₂HPO₄.

Project description:This study describes the behavior of potential slow-release fertilizers (SRF), prepared by the mechanochemical activation of calcined Mg₂Al-CO₃ or Mg₂Fe-CO₃ layered double hydroxides (LDH) mixed with dipotassium hydrogen phosphate (K₂HPO₄). The effects of LDH thermal treatment on P/K release behavior were investigated. Characterizations of the inorganic composites before and after release experiments combined X-Ray diffraction (XRD), Fourier-transform infra-red spectroscopy (FTIR), solid-state nuclear magnetic resonance (NMR), scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX). The best release profile (<75% in 28 days and at least 75% release) was obtained for MgAl/K₂HPO₄ (9 h milling, 2:1 molar ratio, MR). Compared to readily used K₂HPO₄, milling orthophosphate into LDH matrices decreases its solubility and slows down its release, with 60% and 5.4% release after 168 h for MgAl/K₂HPO₄ and MgFe/K₂HPO₄ composites, respectively. Mechanochemical addition of carboxymethylcellulose to the LDH/K₂HPO₄ composites leads to a noticeable improvement of P release properties.

| S-EPMC6410234 | biostudies-literature

Effect of Bi Addition on the Heat Resistance of As-Extruded AZ31 Magnesium Alloy.

Project description:In this work, we investigate the impact of Bi addition on the heat resistance of as-extruded AZ31 alloy during high-temperature annealing and hot compression. Electron backscattered diffraction (EBSD) technique and quasi in situ scanning electron microscopy (SEM) are used to analyze the evolution of microstructures during high-temperature annealing and hot compression, respectively. The test results show that with a prolonged annealing time, the as-extruded AZB313 alloy exhibited a lower grain growth rate, due to the pinning effect of Mg3Bi2 phases distributed at grain boundaries. On the other hand, as the compressive temperature increased, the downtrend of strength is delayed in the as-extruded AZB313 alloy. Thermally stable Mg3Bi2 phases dispersed within the grains act as barriers, hindering the motion of dislocations, which not only provides a more effective precipitation strengthening effect, but also increases the resistance to deformation of grains. Moreover, grain boundary sliding can also be restricted by Mg3Bi2 phases located at grain boundaries. This work provides a new idea for the development of heat-resistant wrought Mg alloys.

| S-EPMC9919633 | biostudies-literature

Ultrasonic-assisted preparation of ultrafine Pd nanocatalysts loaded on Cl--intercalated MgAl layered double hydroxides for the catalytic dehydrogenation of dodecahydro-N-ethylcarbazole.

Project description:N-ethylcarbazole/dodecahydro-N-ethylcarbazole (NEC/H12-NEC) is a promising LOHC, and the development of a catalyst with high activity and stability is the key to realizing its reversible hydrogen storage process. In this paper, ultrafine Pd nanocrystalline catalysts (Pd/LDHs-us) supported on Cl--intercalated MgAl LDHs were prepared by a simple ultrasonic-assisted reduction method and applied in the dehydrogenation of 12H-NEC. In the process of ultrasonic-assisted reduction, the instantaneous high temperature generated by cavitation decomposed part of the CO32- in LDHs interlayer, and promoted PdCl42- to enter the interlayer and become new intercalated ions. At the same time, hydroxyl groups on the surface of LDHs were excited to generate hydrogen radicals (•H) with strong reducibility, which reduced PdCl42- to Pd nanoparticles (PdNPs) in situ. The remaining Cl- ions continued to exist in the interlayer as intercalated ions. The agglomeration of PdNPs was effectively inhibited, and the average particle size was 1.8 nm, which was uniformly dispersed on LDHs, which improved the catalytic activity of Pd/LDHs-us. The coordination between PdNPs and oxygen in the hydroxyl groups on the surface of LDHs improved its catalytic stability. Using Pd/LDHs-us catalyst, the conversion rate of H12-NEC was 100.0 %, and the dehydrogenation efficiency was 99.3 % at 180℃. When the reaction temperature drops to 170℃, the dehydrogenation efficiency can still reach 94.6 %, showing excellent catalytic performance. The study of dehydrogenation kinetics shows that the apparent activation energy of Pd/LDHs-us catalyst is only 90.97 kJ/mol. This provides a new method and idea for the preparation of efficient dehydrogenation catalysts in the future.

| S-EPMC9310112 | biostudies-literature

Stability Trends in Mono-Metallic 3d Layered Double Hydroxides.

Project description:Layered double hydroxides (LDHs) constitute a unique group of 2D materials that can deliver exceptional catalytic, optical, and electronic performance. However, they usually suffer from low stability compared to their oxide counterparts. Using density functional calculations, we quantitatively demonstrate the crucial impact of the intercalants (i.e., water, lactate, and carbonate) on the stability of a series of common LDHs based on Mn, Fe, and Co. We found that intercalation with the singly charged lactate results in higher stability in all these LDH compounds, compared to neutral water and doubly charged carbonate. Furthermore, we show that the dispersion effect aids the stability of these LDH compounds. This investigation reveals that certain intercalants enhance LDH stability and alter the bandgap favourably.

| S-EPMC9029406 | biostudies-literature

Core-shell zeolite@aqueous miscible organic-layered double hydroxides.

Project description:We report a general method for the synthesis of core-shell hybrid materials containing a microporous zeolite core with an aqueous miscible organic-layered double hydroxide (AMO-LDH) shell using a simple in situ coprecipitation method. For example, zeolite-HY@AMO-Mg2Al-CO3-LDH contains a 150 nm hierarchical AMO-Mg2Al-CO3-LDH surface coating on zeolite-HY. It exhibits a similar BET surface area (698 m2 g-1) as the parent zeolite-HY but this surface area has been re-allocated between microspores and mesopores. We believe that surface aluminium sites act as nucleation sites for the formation of the LDH coating and so robustly links it into the zeolite lattice. We expect that this new hybrid structure with micropores dominating in the core and mesopores populating the shell will provide a desirable new hybrid structure type for adsorption or catalysis.

| S-EPMC5975924 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data