Preparation and Characterization of Magnetite Talc (Fe₃O₄@Talc) Nanocomposite as an Effective Adsorbent for Cr(VI) and Alizarin Red S Dye.

ABSTRACT: In this work, the adsorption of Cr(VI) ions and the organic dye Alizarin Red S (ARS) was investigated using magnetite talc (Fe₃O₄@Talc) nanocomposite. Different characterization techniques such as scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy, X-ray Diffraction (XRD), and thermogravimetric analysis (TGA) were used to demonstrate the physical and chemical properties of the fabricated Fe₃O₄@Talc nanocomposite. In addition, the adsorption isothermic, kinetic, and thermodynamic properties were illustrated. The results demonstrate that the investigated adsorption processes obeyed the Langmuir isotherm model for Cr(VI) and the Freundlich isotherm model for ARS dye, with a maximum adsorption capacity of 13.5 and 11.76 mg·g^-1, respectively, controlled by pseudo second-order kinetics. Regeneration and reusability studies demonstrated that the prepared Fe₃O₄@Talc nanocomposite is a promising and stable adsorbent with considerable reusability potential.

SUBMITTER: Nayl AA

PROVIDER: S-EPMC9105966 | biostudies-literature | 2022 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Preparation and Characterization of Magnetite Talc (Fe3O4@Talc) Nanocomposite as an Effective Adsorbent for Cr(VI) and Alizarin Red S Dye.

Nayl AbdElAziz A AA Abd-Elhamid Ahmed I AI Ahmed Ismail M IM Bräse Stefan S

Materials (Basel, Switzerland) 20220509 9

In this work, the adsorption of Cr(VI) ions and the organic dye Alizarin Red S (ARS) was investigated using magnetite talc (Fe3O4@Talc) nanocomposite. Different characterization techniques such as scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy, X-ray Diffraction (XRD), and thermogravimetric analysis (TGA) were used to demonstrate the physical and chemical properties of the fabricated Fe3O4@Talc nanocomposite. In addi ...[more]

PMID: 35591732

Similar Datasets

Project description:Heavy metal ions in water refer to significant risks to the biological system due to their high toxicity. Therefore, the decontamination of water polluted by heavy metal ions attracts significant interest of researchers. Adsorption by nanomaterials has been a widely used technique for removing heavy metal ions from water. Chitosan was extracted from shrimp shellfish and mixed with laboratory-prepared AgNPs/GO in the ratio of 3 : 1. A series of tests evaluates the best condition of pH, amount of adsorbent, retention time, stirring speed, temp, and initial concentration. The research was conducted under various conditions. Langmuir, Freundlich, Tempkin, and Dubinin-Radushkevich isotherms were also tested. Also, the column adsorption experiment was carried out on industrial wastewater at different flow rates and column bed heights. The optimal values of the contact time, pH, and adsorbent dose of Cr(vi) were found to be 80 min, 4, and 0.1 g 100 mL-1, respectively, at room temperature (30 °C), agitation at 150 rpm, and initial concentration of 50 ppm. On the other hand, the optimal value of contact time, pH, and adsorbent dose of Fe(iii) were found to be 30 min, 6, and 0.02 g 100 mL-1, respectively, at room temp (30 °C) with a stirring speed of 250 rpm and an initial concentration of 40 ppm. For Cr(vi) and Fe(iii), equilibrium studies show that the data fit the Freundlich isotherm well (correlation coefficient, R 2 = 0.98) (III). A link between the pseudo-second order active model and data fitting the pseudo-first order active models were made. Within the intraparticle diffusion model, there are four stages that the mechanism must go through before it is at equilibrium. The adsorbent was tested in an industrial adsorbent column. This test proves that the nanocomposite's adsorption capacity can be restored by washing it with 0.1 M HCl, as shown by the periodicity test. After four cycles, the amount of Cr(vi) adsorbed on AgNPs/GO/chitosan was just 20%, which is insufficient for further adsorption experiments. Cr(vi) removal rates (%R) decreased slightly.

Dataset Information

Preparation and Characterization of Magnetite Talc (Fe₃O₄@Talc) Nanocomposite as an Effective Adsorbent for Cr(VI) and Alizarin Red S Dye.

Publications

Preparation and Characterization of Magnetite Talc (Fe<sub>3</sub>O<sub>4</sub>@Talc) Nanocomposite as an Effective Adsorbent for Cr(VI) and Alizarin Red S Dye.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets