Investigation of Microstructures and Mechanical Properties of SiC/AA2024 Nanocomposites Processed by Powder Metallurgy and T6 Heat Treatment.

ABSTRACT: SiC/AA2024 nanocomposites with 1 and 5 vol.% SiC nanoparticles have been prepared by a powder metallurgy route involving high-energy ball-milling (HEBM), spark plasma sintering (SPS), and hot extrusion. The microstructures and mechanical properties of the nanocomposite samples before and after T6 heat treatment were investigated. The samples exhibited a bimodal microstructure with SiC nanoparticles being dispersed in it. With increasing the SiC nanoparticle content from 1 to 5 vol.%, the yield strength (YS) and ultimate tensile strength (UTS) increased and the elongation to fracture (El) slightly decreased. After T6 heat treatment, a simultaneous improvement of the strength and ductility was observed, with the YS, UTS, and El increasing from 413 MPa, 501 MPa, and 5.4% to 496 MPa, 572 MPa,