Enhanced Photocatalytic Activity and Photoluminescence of ZnO Nano-Wires Coupled with Aluminum Nanostructures.

ABSTRACT: In this study, we fabricated a hybrid plasmonic/semiconductor material by combining the chemical bath deposition of zinc oxide nanowires (ZnONWs) with the physical vapor deposition of aluminum nanostructures (AlNSs) under controlled temperature and atmosphere. The morphological and the optical properties of the ZnONWs/AlNSs hybrid material fabricated at different temperatures (250, 350, and 450 °C) and thicknesses (5, 7, and 9 nm) of Al layers were investigated. By adjusting the deposition and annealing parameters, it was possible to tune the size distribution of the AlNSs. The resonant coupling between the plasmonic AlNSs and ZnONWs leads to an enhanced photoluminescence response. The photocatalytic activity was studied through photodegradation under UV-light irradiation of methylene blue (MB) adsorbed at the surface of ZnO. The MB photodegradation experiment reveals that the ZnONWs covered with 7 nm aluminum film and annealed at 450 °C exhibit the highest degradation efficiency. The comparison between ZnONws and ZnONws/AlNSs shows a photoluminescence enhancement factor of 1.7 and an increase in the kinetics constant of photodegradation with a factor of 4.

SUBMITTER: Rtimi M

PROVIDER: S-EPMC9182769 | biostudies-literature | 2022 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Enhanced Photocatalytic Activity and Photoluminescence of ZnO Nano-Wires Coupled with Aluminum Nanostructures.

Rtimi Mondher M Beydoun Nour N Movsesyan Artur A Akil Suzanna S Kostcheev Sergei S Gassmann Xavier X Lajnef Mohamed M Chtourou Radhouane R Jradi Safi S

Nanomaterials (Basel, Switzerland) 20220606 11

In this study, we fabricated a hybrid plasmonic/semiconductor material by combining the chemical bath deposition of zinc oxide nanowires (ZnONWs) with the physical vapor deposition of aluminum nanostructures (AlNSs) under controlled temperature and atmosphere. The morphological and the optical properties of the ZnONWs/AlNSs hybrid material fabricated at different temperatures (250, 350, and 450 °C) and thicknesses (5, 7, and 9 nm) of Al layers were investigated. By adjusting the deposition and a ...[more]

PMID: 35683800

Similar Datasets

Project description:Heterogeneous photocatalysis has been considered one of the most effective and efficient techniques to remove organic contaminants from wastewater. The present work was designed to examine the photocatalytic performance of metal (Cu and Ni) doped ZnO nanocomposites in methyl orange (MO) dye degradation under UV light illumination. The wurtzite hexagonal structure was observed for both undoped/doped ZnO and a crystalline size ranging between 8.84 ± 0.71 to 12.91 ± 0.84 nm by X-ray diffraction (XRD) analysis. The scanning electron microscope (SEM) and energy dispersive X-ray (EDX) revealed the irregular spherical shape with particle diameter (34.43 ± 6.03 to 26.43 ± 4.14 nm) and ensured the purity of the individual elemental composition respectively. The chemical bonds (O-H group) and binding energy (1021.8 eV) were identified by Fourier transform infrared (FTIR) and X-ray photoelectron spectroscopy (XPS) results respectively. The bandgap energy was decreased from 3.44 to 3.16 eV when Ni dopant was added to the ZnO lattice. The comparative photocatalytic activity was observed in undoped and doped nanocomposites and found to be 76.31%, 81.95%, 89.30%, and 83.39% for ZnO, Cu/ZnO, Ni/ZnO, and Cu/Ni/ZnO photocatalysts, respectively, for a particular dose (0.210 g) and dye concentration (10 mg L-1) after 180 min illumination of UV light. The photocatalytic performance was increased up to 94.40% with the increase of pH (12.0) whereas reduced (35.12%) with an increase in initial dye concentration (40 mg L-1) using Ni/ZnO nanocomposite. The Ni/ZnO nanocomposite showed excellent reusability and was found 81% after four consecutive cycles. The best-fitted reaction kinetics was followed by pseudo-first-order and found reaction rate constant (0.0117 min-1) using Ni/ZnO nanocomposite. The enhanced photodegradation efficiency was observed due to decreases in bandgap energy and the crystalline size of the photocatalyst. Therefore, Ni/ZnO nanocomposite could be used as an emerging photocatalyst to degrade bio-persistent organic dye compounds from textile wastewater.

Dataset Information

Enhanced Photocatalytic Activity and Photoluminescence of ZnO Nano-Wires Coupled with Aluminum Nanostructures.

Publications

Enhanced Photocatalytic Activity and Photoluminescence of ZnO Nano-Wires Coupled with Aluminum Nanostructures.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets