Direct Air Capture Using Electrochemically Regenerated Anion Exchange Resins.

ABSTRACT: Direct air capture (DAC) aims to remove CO₂ directly from the atmosphere. In this study, we have demonstrated proof-of-concept of a DAC process combining CO₂ adsorption in a packed bed of amine-functionalized anion exchange resins (AERs) with a pH swing regeneration using an electrochemical cell (EC). The resin bed was regenerated using the alkaline solution produced in the cathodic compartment of the EC, while high purity CO₂ (>95%) was desorbed in the acidifying compartment. After regenerating the AERs, some alkaline solution remained on the surface of the resins and provided additional CO₂ capture capacity during adsorption. The highest CO₂ capture capacity measured was 1.76 mmol·g^-1 dry resins. Moreover, as the whole process was operated at room temperature, the resins did not show any apparent degradation after 150 cycles of adsorption-desorption. Furthermore, when the relative humidity of the air source increased from 33 to 84%, the water loss of the process decreased by 63%, while CO₂ capture capacity fell 22%. Finally, although the pressure drop of the adsorption column (5 ± 1 kPa) and the energy consumption of the EC (537 ± 33 kJ·mol^-1 at 20 mA·cm^-2) are high, we have discussed the potential improvements toward a successful upscaling.

SUBMITTER: Shu Q

PROVIDER: S-EPMC9386902 | biostudies-literature | 2022 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Direct Air Capture Using Electrochemically Regenerated Anion Exchange Resins.

Shu Qingdian Q Haug Marina M Tedesco Michele M Kuntke Philipp P Hamelers Hubertus V M HVM

Environmental science & technology 20220804 16

Direct air capture (DAC) aims to remove CO2 directly from the atmosphere. In this study, we have demonstrated proof-of-concept of a DAC process combining CO2 adsorption in a packed bed of amine-functionalized anion exchange resins (AERs) with a pH swing regeneration using an electrochemical cell (EC). The resin bed was regenerated using the alkaline solution produced in the cathodic compartment of the EC, while high purity CO2 (>95%) was desorbed in the acidifyin ...[more]

PMID: 35925794

Similar Datasets

Project description:Direct air capture (DAC) removal of anthropogenic CO2 from the atmosphere is imperative to slow the catastrophic effects of global climate change. Numerous materials are being investigated, including various alkaline inorganic metal oxides that form carbonates via DAC. Here we explore metastable early d0 transition metal peroxide molecules that undergo stabilization via multiple routes, including DAC. Specifically here, we describe via experiment and computation the mechanistic conversion of A3V(O2)4 (tetraperoxovanadate, A = K, Rb, Cs) to first a monocarbonate VO(O2)2(CO3)3-, and ultimately HKCO3 plus KVO4. Single crystal X-ray structures of rubidium and cesium tetraperoxovanadate are reported here for the first time, likely prior-challenged by instability. Infrared spectroscopy (FTIR), powder X-ray diffraction (PXRD), 51V solid state NMR (nuclear magnetic resonance), tandem thermogravimetry-mass spectrometry (TGA-MS) along with calculations (DFT, density functional theory) all converge on mechanisms of CO2 capture and release that involve the vanadium centre, despite the end product of a 300 days study being bicarbonate and metavanadate. Electron Paramagnetic Resonance (EPR) Spectroscopy along with a wet chemical assay and computational studies evidence the presense of ∼5% adventitous superoxide, likely formed by peroxide reduction of vanadium, which also stabilizes via the reaction with CO2. The alkalis have a profound effect on the stability of the peroxovanadate compounds, stability trending K > Rb > Cs. While this translates to more rapid CO2 capture with heavier alkalis, it does not necessarily lead to capture of more CO2. All compounds capture approximately two equivalents CO2 per vanadium centre. We cannot yet explain the reactivity trend of the alkali peroxovanadates, because any change in speciation of the alkalis from reactions to product is not quantifiable. This study sets the stage for understanding and implementing transition metal peroxide species, including peroxide-functionalized metal oxides, for DAC.

Project description:Rising CO2 emissions are responsible for increasing global temperatures causing climate change. Significant efforts are underway to develop amine-based sorbents to directly capture CO2 from air (called direct air capture (DAC)) to combat the effects of climate change. However, the sorbents' performances have usually been evaluated at ambient temperatures (25 °C) or higher, most often under dry conditions. A significant portion of the natural environment where DAC plants can be deployed experiences temperatures below 25 °C, and ambient air always contains some humidity. In this study, we assess the CO2 adsorption behavior of amine (poly(ethyleneimine) (PEI) and tetraethylenepentamine (TEPA)) impregnated into porous alumina at ambient (25 °C) and cold temperatures (-20 °C) under dry and humid conditions. CO2 adsorption capacities at 25 °C and 400 ppm CO2 are highest for 40 wt% TEPA-incorporated γ-Al2O3 samples (1.8 mmol CO2/g sorbent), while 40 wt % PEI-impregnated γ-Al2O3 samples exhibit moderate uptakes (0.9 mmol g-1). CO2 capacities for both PEI- and TEPA-incorporated γ-Al2O3 samples decrease with decreasing amine content and temperatures. The 40 and 20 wt % TEPA sorbents show the best performance at -20 °C under dry conditions (1.6 and 1.1 mmol g-1, respectively). Both the TEPA samples also exhibit stable and high working capacities (0.9 and 1.2 mmol g-1) across 10 cycles of adsorption-desorption (adsorption at -20 °C and desorption conducted at 60 °C). Introducing moisture (70% RH at -20 and 25 °C) improves the CO2 capacity of the amine-impregnated sorbents at both temperatures. The 40 wt% PEI, 40 wt % TEPA, and 20 wt% TEPA samples show good CO2 uptakes at both temperatures. The results presented here indicate that γ-Al2O3 impregnated with PEI and TEPA are potential materials for DAC at ambient and cold conditions, with further opportunities to optimize these materials for the scalable deployment of DAC plants at different environmental conditions.

Dataset Information

Direct Air Capture Using Electrochemically Regenerated Anion Exchange Resins.

Publications

Direct Air Capture Using Electrochemically Regenerated Anion Exchange Resins.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets