Structural modification of salt-promoted MgO sorbents for intermediate temperature CO₂ capture.

ABSTRACT: MgO-based sorbents are a promising option for CO₂ capture at intermediate temperatures. MgO-based sorbents are often hybridized with alkali metal salts to promote the CO₂ capture performance. However, MgO-based sorbents often suffer a rapid decrement of CO₂ capture performance during multicycle carbonation-calcination reactions due to the reduction of active sites. In this study, we attempted to enhance the durability of MgO-based sorbents by modifying their morphology. A tubular-shaped MgO-based sorbent was synthesized using a carbon nanotube template. Various characterization experiments and evaluations were performed with the synthesized MgO-based materials. The MgO sample with modified structure exhibited a specific morphology consisting of elongated plate-like structures separated by empty spaces. This separation is expected to prevent MgO agglomeration and preserve the modified morphology during iterative CO₂ capture reactions. The MgO with modified structure achieved higher cycling stability with four times slower performance decay than the control MgO, even though identical chemical compositions were applied.

SUBMITTER: Choi D

PROVIDER: S-EPMC9417095 | biostudies-literature | 2022 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Structural modification of salt-promoted MgO sorbents for intermediate temperature CO2 capture.

Choi Dasol D Park Youngjune Y

Nanoscale advances 20220610 14

MgO-based sorbents are a promising option for CO2 capture at intermediate temperatures. MgO-based sorbents are often hybridized with alkali metal salts to promote the CO2 capture performance. However, MgO-based sorbents often suffer a rapid decrement of CO2 capture performance during multicycle carbonation-calcination reactions due to the reduction of active sites. In this study, we attempted to enhance the durability of MgO-based sorbents by modifying their morp ...[more]

PMID: 36133521

Similar Datasets

Project description:Rising CO2 emissions are responsible for increasing global temperatures causing climate change. Significant efforts are underway to develop amine-based sorbents to directly capture CO2 from air (called direct air capture (DAC)) to combat the effects of climate change. However, the sorbents' performances have usually been evaluated at ambient temperatures (25 °C) or higher, most often under dry conditions. A significant portion of the natural environment where DAC plants can be deployed experiences temperatures below 25 °C, and ambient air always contains some humidity. In this study, we assess the CO2 adsorption behavior of amine (poly(ethyleneimine) (PEI) and tetraethylenepentamine (TEPA)) impregnated into porous alumina at ambient (25 °C) and cold temperatures (-20 °C) under dry and humid conditions. CO2 adsorption capacities at 25 °C and 400 ppm CO2 are highest for 40 wt% TEPA-incorporated γ-Al2O3 samples (1.8 mmol CO2/g sorbent), while 40 wt % PEI-impregnated γ-Al2O3 samples exhibit moderate uptakes (0.9 mmol g-1). CO2 capacities for both PEI- and TEPA-incorporated γ-Al2O3 samples decrease with decreasing amine content and temperatures. The 40 and 20 wt % TEPA sorbents show the best performance at -20 °C under dry conditions (1.6 and 1.1 mmol g-1, respectively). Both the TEPA samples also exhibit stable and high working capacities (0.9 and 1.2 mmol g-1) across 10 cycles of adsorption-desorption (adsorption at -20 °C and desorption conducted at 60 °C). Introducing moisture (70% RH at -20 and 25 °C) improves the CO2 capacity of the amine-impregnated sorbents at both temperatures. The 40 wt% PEI, 40 wt % TEPA, and 20 wt% TEPA samples show good CO2 uptakes at both temperatures. The results presented here indicate that γ-Al2O3 impregnated with PEI and TEPA are potential materials for DAC at ambient and cold conditions, with further opportunities to optimize these materials for the scalable deployment of DAC plants at different environmental conditions.

Project description:Aminopolymer-based sorbents are preferred materials for extraction of CO2 from ambient air [direct air capture (DAC) of CO2] owing to their high CO2 adsorption capacity and selectivity at ultra-dilute conditions. While those adsorptive properties are important, the stability of a sorbent is a key element in developing high-performing, cost-effective, and long-lasting sorbents that can be deployed at scale. Along with process upsets, environmental components such as CO2, O2, and H2O may contribute to long-term sorbent instability. As such, unraveling the complex effects of such atmospheric components on the sorbent lifetime as they appear in the environment is a critical step to understanding sorbent deactivation mechanisms and designing more effective sorbents and processes. Here, a poly(ethylenimine) (PEI)/Al2O3 sorbent is assessed over continuous and cyclic dry and humid conditions to determine the effect of the copresence of CO2 and O2 on stability at an intermediate temperature of 70 °C. Thermogravimetric and elemental analyses in combination with in situ horizontal attenuated total reflection infrared (HATR-IR) spectroscopy are performed to measure the extent of deactivation, elemental content, and molecular level changes in the sorbent due to deactivation. The thermal/thermogravimetric analysis results reveal that incorporating CO2 with O2 accelerates sorbent deactivation using these sorbents in dry and humid conditions compared to that using CO2-free air in similar conditions. The in situ HATR-IR spectroscopy results of PEI/Al2O3 sorbent deactivation under a CO2-air environment show the formation of primary amine species in higher quantity (compared to that in conditions without O2 or CO2), which arises due to the C-N bond cleavage at secondary amines due to oxidative degradation. We hypothesize that the formation of bound CO2 species such as carbamic acids catalyzes C-N cleavage reactions in the oxidative degradation pathway by shuttling protons, resulting in a low activation energy barrier for degradation, as probed by metadynamics simulations. In the cyclic experiment after 30 cycles, results show a gradual loss in stability (dry: 29%, humid: 52%) under CO2-containing air (0.04% CO2/21% O2 balance N2). However, the loss in capacity during cyclic studies is significantly less than that during continuous deactivation, as expected.

Dataset Information

Structural modification of salt-promoted MgO sorbents for intermediate temperature CO₂ capture.

Publications

Structural modification of salt-promoted MgO sorbents for intermediate temperature CO<sub>2</sub> capture.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets