First observation on emergence of strong room-temperature ferroelectricity and multiferroicity in 2D-Ti₃C₂T _x free-standing MXene film.

ABSTRACT: Two-dimensional (2D) multiferroics are key candidate materials towards advancement of smart technology. Here, we employed a simple synthesis approach to address the long-awaited dream of developing ferroelectric and multiferroic 2D materials, especially in the new class of materials called MXenes. The etched Ti₃C₂T _x MXene was first synthesized after HF-treatment followed by a delamination process for successful synthesis of free-standing Ti₃C₂T _x film. The free-standing film was then exposed to air at room-temperature and heated at different temperatures to form a TiO₂ layer derived from the Ti₃C₂T _x MXene itself. The ferroelectric measurement showed a clear polarization hysteresis loop at room-temperature. Also, due to the reported ferromagnetic behavior of Ti₃C₂T _x MXene, our composite could show multiferroic properties at room-temperature. The magnetoelectric coupling test was also performed that showed a clear, switchable spontaneous polarization under applied magnetic field. TiO₂ is reported to be an incipient ferroelectric that assumes a ferroelectric phase in composite form. The structural and morphological analysis confirmed successful synthesis of free-standing film and the Raman spectroscopy revealed the formation of different phases of TiO₂ and the observed ferroelectricity could be due to structural deformation as a result of the formation of this new phase. The measured value of remanent polarization is 0.5 μC cm^-2. This is the first report on the existence of a ferroelectric phase and multiferroic coupling in 2D free-standing MXene film at room-temperature which opens-up the possibility of 2D material-based electric and magnetic data storage applications at room-temperature.

SUBMITTER: Tahir R 

PROVIDER: S-EPMC9426648 | biostudies-literature | 2022 Aug

REPOSITORIES: biostudies-literature