Nanosized (Ni_1-x Zn _x )Fe₂O₄ for water oxidation.

ABSTRACT: Performing water splitting for H₂ production is an interesting method to store different energies. For water splitting, an efficient and stable water-oxidizing catalyst is important. Ni-Fe (hydr)oxides are among the best catalysts for water oxidation in alkaline electrolytes. An Fe amount higher than 50% in Ni-Fe (hydr)oxides increases the overpotential for water oxidation. Thus, Ni-Fe (hydr)oxides with a high ratio of Fe to Ni have rarely been focused on for water oxidation. Herein, we report water oxidation using nanosized (Ni_1-x Zn _x )Fe₂O₄. The catalyst was characterized via some methods and tested at pH values of 3, 7 and 11 in phosphate buffer. Nanosized (Ni_1-x Zn _x )Fe₂O₄ is a good catalyst for water oxidation only under alkaline conditions. In the next step, amperometry studies showed current densities of 3.50 mA cm^-2 and 11.50 mA cm^-2 at 1.25 V in 0.10 M and 1.0 M KOH solution, respectively. The amperometric measurements indicated high catalyst stability in both 0.10 M and 1.0 M KOH. Tafel plots were obtained in KOH solution at concentrations of both 0.10 M and 1.0 M. At pH = 13 in KOH solution (0.10 M), linearity of lg(j) vs. potential was shown, with two slopes relating to both relatively low (170.9 mV per decade) and high overpotentials (484.2 mV per decade). In 1.0 M KOH solution, the Tafel plot showed linearity of lg(j) vs. potential, with two slopes relating to both relatively low (192.5 mV per decade) and high overpotentials (545.7 mV per decade). After water oxidation, no significant change was observed in the catalyst.

SUBMITTER: Mehrabani S

PROVIDER: S-EPMC9473301 | biostudies-literature | 2019 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Nanosized (Ni1-x Zn x )Fe2O4 for water oxidation.

Mehrabani Somayeh S Singh Jitendra Pal JP Bagheri Robabeh R Wattoo Abdul Ghafar AG Song Zhenlun Z Chae Keun Hwa KH Najafpour Mohammad Mahdi MM

Nanoscale advances 20181022 2

Performing water splitting for H2 production is an interesting method to store different energies. For water splitting, an efficient and stable water-oxidizing catalyst is important. Ni-Fe (hydr)oxides are among the best catalysts for water oxidation in alkaline electrolytes. An Fe amount higher than 50% in Ni-Fe (hydr)oxides increases the overpotential for water oxidation. Thus, Ni-Fe (hydr)oxides with a high ratio of Fe to Ni have rarely been focused on for water oxidation. Herein, ...[more]

PMID: 36132275

Similar Datasets

Project description:Layered double hydroxides (LDHs) are an ideal platform to host catalytic metal centers for water oxidation (WO) owing to the high accessibility of water to the interlayer region, which makes all centers potentially reachable and activated. Herein, we report the syntheses of three iridium-doped zinc-aluminum LDHs (Ir-LDHs) nanomaterials (1-3, with about 80 nm of planar size and a thickness of 8 nm as derived by field emission scanning electron microscopy and powder X-ray diffraction studies, respectively), carried out in the confined aqueous environment of reverse micelles, through a very simple and versatile procedure. These materials exhibit excellent catalytic performances in WO driven by NaIO4 at neutral pH and 25 °C, with an iridium content as low as 0.5 mol % (∼0.8 wt %), leading to quantitative oxygen yields (based on utilized NaIO4, turnover number up to ∼10,000). Nanomaterials 1-3 display the highest ever reported turnover frequency values (up to 402 min-1) for any heterogeneous and heterogenized catalyst, comparable only to those of the most efficient molecular iridium catalysts, tested under similar reaction conditions. The boost in activity can be traced to the increased surface area and pore volume (>5 times and 1 order of magnitude, respectively, higher than those of micrometric materials of size 0.3-1 μm) estimated for the nanosized particles, which guarantee higher noble metal accessibility. X-ray absorption spectroscopy (XAS) studies suggest that 1-3 nanomaterials, as-prepared and after catalysis, contain a mixture of isolated, single octahedral Ir(III) sites, with no evidence of Ir-Ir scattering from second-nearest neighbors, excluding the presence of IrO2 nanoparticles. The combination of the results obtained from XAS, elemental analysis, and ionic chromatography strongly suggests that iridium is embedded in the brucite-like structure of LDHs, having four hydroxyls and two chlorides as first neighbors. These results demonstrate that nanometric LDHs can be successfully exploited to engineer efficient WOCs, minimizing the amount of iridium used, consistent with the principle of the noble-metal atom economy.

Dataset Information

Nanosized (Ni_1-x Zn _x )Fe₂O₄ for water oxidation.

Publications

Nanosized (Ni<sub>1-<i>x</i></sub> Zn <sub><i>x</i></sub> )Fe<sub>2</sub>O<sub>4</sub> for water oxidation.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets