Al2O3/HfO2 Nanolaminate Dielectric Boosting IGZO-Based Flexible Thin-Film Transistors.
Ontology highlight
ABSTRACT:
SUBMITTER: Shi Q
PROVIDER: S-EPMC9515270 | biostudies-literature | 2022 Sep
REPOSITORIES: biostudies-literature
Publications
Al<sub>2</sub>O<sub>3</sub>/HfO<sub>2</sub> Nanolaminate Dielectric Boosting IGZO-Based Flexible Thin-Film Transistors.
Shi Qiuwei Q Aziz Izzat I Ciou Jin-Hao JH Wang Jiangxin J Gao Dace D Xiong Jiaqing J Lee Pooi See PS
Nano-micro letters 20220927 1
Similar Datasets
Project description:Solution-processed metal oxides have been investigated as an alternative to vacuum-based oxides to implement low-cost, high-performance electronic devices on flexible transparent substrates. However, their electrical properties need to be enhanced to apply at industrial scale. Amorphous indium-gallium-zinc oxide (a-IGZO) is the most-used transparent semiconductor metal oxide as an active channel layer in thin-film transistors (TFTs), due to its superior electrical properties. The present work evaluates the influence of composition, thickness and ageing on the electrical properties of solution a-IGZO TFTs, using solution combustion synthesis method, with urea as fuel. After optimizing the semiconductor properties, low-voltage TFTs were obtained by implementing a back-surface passivated 3-layer In:Ga:Zn 3:1:1 with a solution-processed high-к dielectric; AlOx. The devices show saturation mobility of 3.2 cm2 V-1 s-1, IOn/IOff of 106, SS of 73 mV dec-1 and VOn of 0.18 V, thus demonstrating promising features for low-cost circuit applications.
| S-EPMC6781023 | biostudies-literature
Project description:Radiating amorphous In-Ga-Zn-O (a-IGZO) thin-film transistors (TFTs) with deep ultraviolet light (λ = 175 nm) is found to induce rigid negative threshold-voltage shift, as well as a subthreshold hump and an increase in subthreshold-voltage slope. These changes are attributed to the photo creation and ionization of oxygen vacancy states (VO), which are confined mainly to the top surface of the a-IGZO film (backchannel). Photoionization of these states generates free electrons and the transition from the neutral to the ionized VO is accompanied by lattice relaxation, which raises the energy of the ionized VO. This and the possibility of atomic exchange with weakly bonded hydrogen leads to metastability of the ionized VO, consistent with the rigid threshold-voltage shift and increase in subthreshold-voltage slope. The hump is thus a manifestation of the highly conductive backchannel and its formation can be suppressed by reduction of the a-IGZO film thickness or application of a back bias after radiation. These results support photo creation and ionization of VO as the main cause of light instability in a-IGZO TFTs and provide some insights on how to minimize the effect.
| S-EPMC8285384 | biostudies-literature
Project description:We report the fabrication of a solution-processed n-type Thin Film Transistor (TFT) with current on/off ratios of 104, a turn-on voltage (V ON) of 1.2 V and a threshold voltage (V T) of 6.2 V. The TFT incorporates an insoluble and intractable dielectric layer (k = 7-9) prepared in situ from solution-processed and then photopolymerised ligand-stabilised, inorganic/organic TiO2 nanorods. A solution processed zinc oxide (ZnO) layer acts as the semiconductor. The new surface-modified TiO2 nanorods were synthesised using a ligand replacement process with a monolayer coating of photopolymerisable 10-undecynylphosphonic acid (10UCYPA) to render them both soluble in common organic solvents and be photopolymerisable using UV-illumination after having been deposited on substrate surfaces from solution and drying.
| S-EPMC9055251 | biostudies-literature
Project description:Oxide semiconductors are regarded as promising materials for large-area and/or flexible electronics. In this work, a ring oscillator based on n-type indium-gallium-zinc-oxide (IGZO) and p-type tin monoxide (SnO) is presented. The IGZO thin-film transistor (TFT) shows a linear mobility of 11.9 cm²/(V∙s) and a threshold voltage of 12.2 V. The SnO TFT exhibits a mobility of 0.51 cm²/(V∙s) and a threshold voltage of 20.1 V which is suitable for use with IGZO TFTs to form complementary circuits. At a supply voltage of 40 V, the complementary inverter shows a full output voltage swing and a gain of 24 with both TFTs having the same channel length/channel width ratio. The three-stage ring oscillator based on IGZO and SnO is able to operate at 2.63 kHz and the peak-to-peak oscillation amplitude reaches 36.1 V at a supply voltage of 40 V. The oxide-based complementary circuits, after further optimization of the operation voltage, may have wide applications in practical large-area flexible electronics.
| S-EPMC5503323 | biostudies-literature
Project description:In this paper, high-performance indium gallium oxide (IGO) thin-film transistor (TFT) with a double-gate (DG) structure was developed using an atomic layer deposition route. The device consisting of 10-nm-thick IGO channel and 2/48-nm-thick SiO2/HfO2 dielectric was designed to be suitable for a display backplane in augmented and virtual reality applications. The fabricated DG TFTs exhibit outstanding device performances with field-effect mobility (μFE) of 65.1 ± 2.3 cm2V-1 s-1, subthreshold swing of 65 ± 1 mVdec-1, and threshold voltage (VTH) of 0.42 ± 0.05 V. Both the (μFE) and SS are considerably improved by more than two-fold in the DG IGO TFTs compared to single-gate (SG) IGO TFTs. Important finding was that the DG mode of IGO TFTs exhibits the nearly temperature independent μFE variations in contrast to the SG mode which suffers from the severe remote Coulomb scattering. The rationale for this disparity is discussed in detail based on the potential distribution along the vertical direction using technology computer-aided design simulation. Furthermore, the DG IGO TFTs exhibit a greatly improved reliability with negligible VTH shift of - 0.22 V under a harsh negative bias thermal and illumination stress condition with an electric field of - 2 MVcm-1 and blue light illumination at 80 °C for 3600 s. It could be attributed to the increased electrostatic potential that results in fast re-trapping of the electrons generated by the light-induced ionization of deep level oxygen vacancy defects.
| S-EPMC10984952 | biostudies-literature
Project description:Very thin (2.3-5.5 nm) self-assembled organic dielectric multilayers have been integrated into organic thin-film transistor structures to achieve sub-1-V operating characteristics. These new dielectrics are fabricated by means of layer-by-layer solution phase deposition of molecular silicon precursors, resulting in smooth, nanostructurally well defined, strongly adherent, thermally stable, virtually pinhole-free, organosiloxane thin films having exceptionally large electrical capacitances (up to approximately 2,500 nF.cm(-2)), excellent insulating properties (leakage current densities as low as 10(-9) A.cm(-2)), and single-layer dielectric constant (k)of approximately 16. These 3D self-assembled multilayers enable organic thin-film transistor function at very low source-drain, gate, and threshold voltages (<1 V) and are compatible with a broad variety of vapor- or solution-deposited p- and n-channel organic semiconductors.
| S-EPMC555722 | biostudies-literature
Project description:Low-temperature giant-dielectric-constant thin films (In0.0025Nb0.0025Ti0.995O2) fabricated with simple radio frequency (RF) sputtering on glass substrates are employed as the gate dielectrics for thin-film transistors (TFTs) for the first time. The 380 nm-thick In0.0025Nb0.0025Ti0.995O2 film exhibited a quasi-static capacitance of as high as 36 156 nF cm-2 with a quasi-static permittivity of 15 525 (and 7607 nF cm-2 at 1 kHz). Indium zinc oxide (IZO) TFTs with In0.0025Nb0.0025Ti0.995O2 gate dielectrics exhibited high output current at low operation voltage and little hysteresis in the transfer curves between forward and reverse sweeps. The subthreshold swing (SS) of the IZO TFTs is 0.068 V dec-1, very close to the lowest limit of the SS of the field-effect transistors (0.06 V dec-1). The results also proves that the lowest limit of the SS (0.06 V dec-1) cannot be broken no matter how high the gate dielectric capacitance is (except for negative capacitors). The TFTs demonstrate the potential for the applications in low-power circuits or flat-panel displays.
| S-EPMC9070635 | biostudies-literature
Project description:Employing CO2-based polymer in electronic applications should boost the consumption of CO2 feedstocks and provide the potential for non-permanent CO2 storage. In this study, polypropylene carbonate (PPC) is utilized as a dielectric and substrate material for organic thin film transistors (OTFTs) and organic inverter. The PPC dielectric film exhibits a surface energy of 47 mN m-1, a dielectric constant of 3, a leakage current density of less than 10-6 A cm-2, and excellent compatibility with pentacene and PTCDI-C8 organic semiconductors. Bottom-gate top-contact OTFTs are fabricated using PPC as a dielectric; they exhibits good electrical performance at an operating voltage of 60 V, with electron and hole mobilities of 0.14 and 0.026 cm2 V-1 s-1, and on-to-off ratios of 105 and 103, respectively. The fabricated p- and n-type transistors were connected to form a complementary inverter that operated at supply voltages of 20 V with high and low noise margins of 85 and 69%, respectively. The suitability of PPC as a substrate is demonstrated through the preparation of PPC sheets by casting method. The fabricated PPC sheets has a transparency of 92% and acceptable mechanical properties, yet they biodegraded rapidly through enzymatic degradation when using the lipase from Rhizhopus oryzae.
| S-EPMC5970150 | biostudies-literature
Project description:The key impact and significance of a multilayer polymer-based dielectric system on the remarkable photoresponse properties of zinc phthalocyanine (ZnPc)-based photosensitive organic field-effect transistors (PS-OFETs) have been systematically analyzed at various incident optical powers. A combination of inorganic aluminum oxide (Al2O3) and organic nonpolar poly(methyl methacrylate) (PMMA) is used as the bilayer dielectric configuration, whereas in the trilayer dielectric system, a bilayer polymer dielectric, consisting of PMMA, as the low-k dielectric polymer, on top of poly(vinyl alcohol) (PVA), the high-k polar dielectric, has been fabricated along with Al2O3 as the third layer. Before fabricating the OFETs, a systematic optimization of the nature of growth of the ZnPc molecules, deposited on PMMA-coated glass substrates at different substrate temperatures (T s) was performed and examined by atomic-force microscopy, field-emission scanning electron microscopy, X-ray diffraction, and Raman analysis. At 90 °C, the fabricated PS-OFETs with the Al2O3/PVA/PMMA trilayer dielectric configuration showed the best p-channel behavior, with an enhanced and remarkable photoresponsivity of R ∼ 9689.39 A W-1 compared to that of the Al2O3/PMMA bilayer dielectric system (R ∼ 2679.40 A W-1) due to the polarization of the dipoles inside the polar PVA dielectric, which increases the charge transport through the channel. The charge carrier mobility of the device also improved by one order (μh ∼ 1.3 × 10-2 cm2 V-1 s-1) compared to that of the bilayer dielectric configuration (μh ∼ 3.5 × 10-3 cm2 V-1 s-1). The observed specific detectivity (D*) and NEP values of the bilayer dielectric system were 6.01 × 1013 Jones and 2.655 × 10-17 W Hz-1/2, whereas for the trilayer dielectric system, the observed D* and NEP values were 5.13 × 1014 Jones and 1.043 × 10-17 W Hz-1/2, respectively. Additionally, the operating voltage of each of the fabricated devices was also very low (-10 V) due to the influence of the inorganic high-k Al2O3 dielectric layer. The electrical stability of all of the fabricated devices was also investigated by bias stress analysis under both light and dark conditions in vacuum. To the best of our knowledge, the photoresponsivity (R) reported here with an Al2O3/PVA/PMMA trilayer dielectric configuration is the highest reported value for thin film-based PS-OFETs, at a remarkably low operating voltage of -10 V, on low-cost glass substrates without indium tin oxide or/and Si/SiO2.
| S-EPMC6641034 | biostudies-literature
Project description:Top-gate structured thin film transistors (TFTs) using In-Ga-Zn-O (IGZO) and In-Ga-O (IGO) channel compositions were investigated to reveal a feasible origin for degradation phenomenon under drain bias stress (DBS). DBS-driven instability in terms of V(TH) shift, deviation of the SS value, and increase in the on-state current were detected only for the IGZO-TFT, in contrast to the IGO-TFT, which did not demonstrate V(TH) shift. These behaviors were visually confirmed via nanoscale transmission electron microscopy and energy-dispersive x-ray spectroscopy observations. To understand the degradation mechanism, we performed ab initio molecular dynamic simulations on the liquid phases of IGZO and IGO. The diffusivities of Ga and In atoms were enhanced in IGZO, confirming the degradation mechanism to be increased atomic diffusion.
| S-EPMC4298721 | biostudies-literature