Segregated Structure Copolymer of Vinylidene Fluoride and Tetrafluoroethylene Composites Filled with rGO, SWCNTs and Their Mixtures.

ABSTRACT: This work is devoted to the formation and study of polymer composites with a segregated structure filled with single-walled carbon nanotubes (SWCNTs), reduced graphene oxide (rGO), and their mixtures. For the first time, polymer composites with a segregated structure filled with rGO/SWCNTs mixtures were obtained. A copolymer of vinylidene fluoride and tetrafluoroethylene (P(VDF-TFE)) was used as a polymer matrix. At a fixed value of the total mass fraction of carbon nanofillers (0.5, 1, and 1.5 wt%), the rGO/SWCNTs ratio was varied. The composites were examined using scanning electron microscopy, wide-range dielectric spectroscopy, and tested for the compression. The effect of the rGO/SWCNTs ratio on the electrical conductivity and mechanical properties of the composites was evaluated. It was shown that, with a decrease in the rGO/SWCNTs ratio, the electrical conductivity increased and reached the maximum at the 1 wt% filling, regardless of the samples' composition. The maximum value of electrical conductivity from the entire data set was 12.2 S/m. The maximum of elastic modulus was 378.7 ± 3.5 MPa for the sample with 1 wt% SWCNTs, which is 14% higher than the P(VDF-TFE) elastic modulus. The composite filled with a mixture of 0.5 wt% rGO and 0.5 wt% SWCNTs reflected 70% of the electromagnetic wave energy from the front boundary, which is 14% and 50% more than for composites with 1 wt% SWCNTs and with 1 wt% rGO, respectively. The lowest transmission coefficient of ultra-high frequencies waves was obtained for a composite sample with a mixture of 0.5 wt% rGO and 0.5 wt% SWCNTs and amounted to less than 1% for a 2 mm thickness sample.

SUBMITTER: Shiyanova K

PROVIDER: S-EPMC9570613 | biostudies-literature | 2022 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Segregated Structure Copolymer of Vinylidene Fluoride and Tetrafluoroethylene Composites Filled with rGO, SWCNTs and Their Mixtures.

Shiyanova Kseniya K Gudkov Maksim M Torkunov Mikhail M Ryvkina Natalia N Chmutin Igor I Goncharuk Galina G Gulin Alexander A Bazhenov Sergey S Melnikov Valery V

Polymers 20220930 19

This work is devoted to the formation and study of polymer composites with a segregated structure filled with single-walled carbon nanotubes (SWCNTs), reduced graphene oxide (rGO), and their mixtures. For the first time, polymer composites with a segregated structure filled with rGO/SWCNTs mixtures were obtained. A copolymer of vinylidene fluoride and tetrafluoroethylene (P(VDF-TFE)) was used as a polymer matrix. At a fixed value of the total mass fraction of carbon nanofillers (0.5, 1, and 1.5 ...[more]

PMID: 36236053

Similar Datasets

Project description:Polymer dielectric composites have widespread applications in many fields ranging from energy storage, microelectronic devices, and sensors to power driven systems, etc. and attract much attention of researchers. However, it is still challenging to prepare advanced polymer dielectric composites with a high dielectric constant (ε'), low dielectric loss (tan δ) and simultaneously high breakdown strength (E bd). In this work, conductive polypyrrole (PPy) nanoparticles were in situ synthesized in a reaction system containing the common barium titanate (BaTiO3, BT) or hydroxylated BaTiO3 (BTOH) particles, and then the PPy@BT and PPy@BTOH composite particles were incorporated into poly(vinylidene fluoride) (PVDF) to prepare the composites. The morphologies and microstructures of the PPy@BT and PPy@BTOH composite particles and the corresponding PVDF composites were comparatively investigated. The results showed that the PPy@BTOH composite particles had a 'mulberry'-like morphology with a rough surface and the self-assembled structure could be maintained in the PVDF composites, which was apparently different from the PVDF/PPy@BT composites, in which most of the PPy nanoparticles dissociatively dispersed in the PVDF matrix. Electrical conductivity measurements showed that at high particle content (≥20 wt%), the PPy@BTOH composite particles endowed the composites with lower electrical conductivity compared with the PPy@BT composite particles. Dielectric property measurements showed that the 'mulberry'-like PPy@BTOH composite particles endowed the PVDF composites with extremely high ε', ultralow tan δ and high E bd compared with the PVDF/PPy@BT composites with dissociatively dispersed PPy nanoparticles and BaTiO3 particles. The polarization and loss mechanisms of the composites were then proposed based on the morphologies and the microstructures of the composites. This work provides an alternative way to fabricate functional dielectric particles through trace functional groups inducing in situ polymerization of conductive polymers, and these particles can be used to fabricate advanced dielectric composites.

Project description:The formation of a segregated network structure (wittingly uneven distribution of a filler) is one of the most promising strategies for the fabrication of electrically conductive polymer composites at present. However, the simultaneous achievement of high values of electrical conductivity with the retention of well mechanical properties within this approach remains a great challenge. Here, by means of X-ray photoelectron spectra (XPS), near-edge X-ray absorption fine structure (NEXAFS) spectra, scanning electron microscopy (SEM), dielectric spectroscopy, and compression engineering stress-strain curve analysis, we have studied the effect of a segregated network structure on the electrical conductivity and mechanical properties of a set of polymer composites. The composites were prepared by applying graphene oxide (GO) with ultralarge basal plane size (up to 150 μm) onto the surface of polymer powder particles, namely, poly(vinyl chloride) (PVC), poly(vinylidene fluoride-co-tetrafluoroethylene) (P(VDF-TFE)), and ultrahigh-molecular-weight poly(ethylene) (UHMWPE) with the subsequent GO reduction and composite hot pressing. A strong dependence of the segregated network polymer composites' physical properties on the polymer matrix was demonstrated. Particularly, 12 orders of magnitude rise of the polymers' electrical conductivity up to 0.7 S/m was found upon the incorporation of the reduced GO (rGO). A 17% increase in the P(VDF-TFE) elastic modulus filled by 1 wt % of rGO was observed. Fracture strength of PVC/rGO at 0.5 wt % content of the filler was demonstrated to decrease by fourfold. At the same time, the change in strength was not significant for P(VDF-TFE) and UHMWPE composites in comparison with pure polymers. Our results show a promise to accelerate the development of new composites for energy applications, such as metal-free supercapacitor plates and current collectors of lithium-ion batteries, bipolar plates of proton-exchange membrane fuel cells, antistatic elements of various electronic devices, etc.

Project description:To develop novel mineral-filled composites and assess their enhanced properties (stiffness, a good balance between mechanical strength and impact resistance, greater temperature stability), a high-impact polypropylene copolymer (PPc) matrix containing an elastomeric discrete phase was melt mixed with natural CaSO4 β-anhydrite II (AII) produced from gypsum rocks. First, in a prior investigation, the PPc composites filled with AII (without any modification) displayed enhanced stiffness, which is correlated with the relative content of the filler. The tensile and impact strengths dramatically decreased, especially at high filling (40 wt.%). Therefore, two key methods were considered to tune up their properties: (a) the ionomeric modification of PPc composites by reactive extrusion (REx) with zinc diacrylate (ZA), and (b) the melt mixing of PPc with AII surface modified with ethylenebis(stearamide) (EBS), which is a multifunctional processing/dispersant additive. The properties of composites produced with twin-screw extruders (TSEs) were deeply assessed in terms of morphology, mechanical, and thermal performance, including characterizations under dynamic mechanical solicitations at low and high temperatures. Two categories of products with distinct properties are obtained. The ionomeric modification by Rex (evaluated by FTIR) led to composites characterized by remarkable thermal stability, a higher temperature of crystallization, stronger interfacial interactions, and therefore noticeable mechanical properties (high tensile strength (i.e., 28 MPa), increased stiffness, moderate (3.3 kJ/m2) to good (5.0 kJ/m2) impact resistance) as well as advanced heat deflection temperature (HDT). On the other hand, the surface modification of AII with EBS facilitated the dispersion and debonding of microparticles, leading to composites revealing improved ductility (strain at break from 50% to 260%) and enhanced impact properties (4.3-5.3 kJ/m2), even at high filling. Characterized by notable mechanical and thermal performances, high whiteness, and a good processing ability, these new PPc-AII composites may be tailored to meet the requirements of end-use applications, ranging from packaging to automotive components.

Dataset Information

Segregated Structure Copolymer of Vinylidene Fluoride and Tetrafluoroethylene Composites Filled with rGO, SWCNTs and Their Mixtures.

Publications

Segregated Structure Copolymer of Vinylidene Fluoride and Tetrafluoroethylene Composites Filled with rGO, SWCNTs and Their Mixtures.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets