Synthesis, Experimental, and Theoretical Study of Co3–xNixO4 Mixed Oxides: Potential Candidates for Hydrogen Production via Solar Redox Cycles
Ontology highlight
ABSTRACT:
SUBMITTER: Nassereddine Y
PROVIDER: S-EPMC9835082 | biostudies-literature | 2022 Dec
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:Herein, we have demonstrated a facile electroless Ni coated nanostructured TiO2 photocatalyst for the first time. More significantly the photocatalytic water splitting shows excellent performance for hydrogen production which is hitherto unattempted. The structural study exhibits majorly the anatase phase along with the minor rutile phase of TiO2. Interestingly, electroless nickel deposited on the TiO2 nanoparticles of size 20 nm shows a cubic structure with nanometer scale Ni coating (1-2 nm). XPS supports the existence of Ni without any oxygen impurity. The FTIR and Raman studies support the formation of TiO2 phases without any other impurities. The optical study shows a red shift in the band gap due to optimum nickel loading. The emission spectra show variation in the intensity of the peaks with Ni concentration. The vacancy defects are pronounced in lower concentrations of Ni loading which shows the formation of a huge number of charge carriers. The electroless Ni loaded TiO2 has been used as a photocatalyst for water splitting under solar light. The primary results manifest that the hydrogen evolution of electroless Ni plated TiO2 is 3.5 times higher (1600 μmol g-1 h-1) than pristine TiO2 (470 μmol g-1 h-1). As shown in the TEM images, nickel is completely electroless plated on the TiO2 surface, which accelerates the fast transport of electrons to the surface. It suppresses the electron-hole recombination drastically which is responsible for higher hydrogen evolution using electroless Ni plated TiO2. The recycling study exhibits a similar amount of hydrogen evolution at similar conditions which shows the stability of the Ni loaded sample. Interestingly, Ni powder loaded TiO2 did not show any hydrogen evolution. Hence, the approach of electroless plating of nickel over the semiconductor surface will have potential as a good photocatalyst for hydrogen evolution.
| S-EPMC10318574 | biostudies-literature
Project description:Developing electrocatalytic nanomaterials for green H2 energy is inseparable from the exploration of novel materials and internal mechanisms for catalytic enhancement. In this work, nano-petal N-doped bi-metal (Ni, Co) and bi-valence (+2, +3) (Ni1-x Co x )2+Co2 3+O4 compounds have been in situ grown on the surface of Ni foam. The N3- atoms originate from the amino group in urea and doped in the compound during annealing. The as-synthesized N-doped (Ni1-x Co x )2+Co2 3+O4 nano-petals demonstrate commendable hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) bi-functional catalytic efficiency and stability. Electrochemical measurements confirm that the nitrogen doping significantly improves the catalytic kinetics and the surface area. Density functional theory calculations reveal that the improved HER and OER kinetics is not only due to the synergistic effect of bi-metal and bi-valence, as well as the introduction of defects such as oxygen vacancies, but also it more depends on the shortened bond length between the nitrogen N3- atoms and the metal atoms, and the increased electron density of the metal atoms attached to the N3- atoms. In other words, the change of lattice parameters caused by nitrogen doping is more conducive to the catalytic enhancement than the synergistic effect brought by bi-metal. This study provides an experimental and theoretical reference for the design of bi-functional electrocatalytic nanomaterials.
| S-EPMC8693244 | biostudies-literature
Project description:In this Part 1 of this series of articles, two iterative cycles are proposed to accurately determine the shunt resistance ( Rsh ), the series resistance ( Rs ), the ideality factor (n), the light current ( Ilig ), and the saturation current ( Isat ) of solar cells, within the one diode model. First, Rs and n are obtained linearly fitting ∂V∂lnI' vs. I' , where I' is a new defined current I'=I+Isat+Ilig-V-IRsRsh+nkTRsh . Then, Rsh and Isat are obtained using Procedure A and B proposed in [2]. Once these four solar cell parameters are obtained, a correction to Ilig is deduced and applied. The deduction of these five solar cell parameters is reused to recalculate I' and the iterative cycles are redone till some convergence criteria is achieved. The accuracy and number of cycles necessary to achieve reasonable results are tested and discussed on ideal (noiseless) current voltage (IV) curves with measured points per voltage of PV=11 , 21, 51 and 101 measured pointsV . These two cycles are compared with two different common parameter extraction methods. The results given in this Part 1 are used in Part 2 to calculate the five solar cell parameters of IV curves found in the literature.
| S-EPMC9494249 | biostudies-literature
Project description:Herein, we demonstrate the bottom-up synthesis of 2D cyano-bridged Cu-Ni coordination polymer (CP) nanoflakes through a controlled crystallization process and their conversion to Cu-Ni mixed oxides via a thermal treatment in air. The chelating effect of citrate anions effectively prevents the rapid coordination reaction between Cu2+ and K₂[Ni(CN)₄], resulting in the deceleration of the crystallization process of CPs. Specifically, with addition of trisodium citrate dehydrate, the number of nuclei formed at the early stage of the reaction is decreased. Less nuclei undergo a crystal growth by interacting with [Ni(CN)₄]2-, leading to the formation of larger Cu-Ni CP nanoflakes. Following heat treatment in air, the -CN- groups present within the CP nanoflakes are removed and nanoporous Cu-Ni mixed oxide nanoflakes are generated. When tested as an electrode material for supercapacitors using a three-electrode system, the optimum Cu-Ni mixed oxide sample shows a maximum specific capacitance of 158 F g-1 at a current density of 1 A g-1. It is expected that the proposed method will be useful for the preparation of other types of 2D and 3D CPs as precursors for the creation of various nanoporous metal oxides.
| S-EPMC6315628 | biostudies-literature
Project description:Ceria-based catalysts are widely used in oxidation or oxidation-reduction reactions in the field of environmental science. Their catalytic functions are determined by their ability to exchange oxygen species with oxidants. The enhancement of oxygen release is desired since it is often the rate-determining step in redox cycles. Herein, we developed a lattice oxygen distortion method to enhance oxygen activation by quenching the Ce-Zr oxide nanoparticles formed from an extremely high temperature. This process can ensure the formation of solid solutions as well as avoiding atomic rearrangement during calcination, retaining the lattice oxygen at a metastable and disordered state without vacancies. Reduction, vacuum or metal deposition will easily induce oxygen release accompanied by vacancy creation. The metastable oxides can provide about 19 times more oxygen vacancies than traditional ones in a CO atmosphere. CO oxidation rates increased with increasing Zr content from 25 to 75% and achieved a new level, which is attributed to the acceleration of oxygen circulation via promoting oxygen release and supplying plenty of oxygen vacancies for redox cycles. This strategy is expected to be applied in the design and fabrication of improved oxygen storage materials.
| S-EPMC5933218 | biostudies-literature
Project description:LaFe x Ni1- x O3 perovskite oxides were prepared by the sol-gel method under various conditions, including different pH values (pH 0 and pH 7) and different calcination temperatures (500-800 °C) as well as different Fe/Ni ratios (1/9, 3/7, 5/5, 7/3, 9/1). The samples were examined by XRD, DRS, BET, and SEM to reveal their crystallinity, light-absorption ability, specific surface area, and surface features, respectively. The photocatalytic Fenton reaction was conducted using various LaFe x Ni1- x O3 perovskite oxides to decompose the methylene blue molecules. Accordingly, the synthesis condition of pH 0, calcination temperature at 700 °C, and Fe/Ni ratio = 7/3 could form LaFe0.7Ni0.3O3 perovskite oxides as highly efficient photocatalysts. Moreover, various conditions during the photocatalytic degradation were verified, such as pH value, catalyst dosage, and the additional amount of H2O2. LaFe0.7Ni0.3O3 perovskite oxides could operate efficiently under pH 3.5, catalyst dosage of 50 mg/150 mL, and H2O2 concentration of 133 ppm to decompose the MB dye in the 1st order kinetic rate constant of 0.0506 s-1.
| S-EPMC9475182 | biostudies-literature
Project description:Photoactivation of M-X bonds is a challenge for photochemical HX splitting, particularly with first-row transition metal complexes because of short intrinsic excited state lifetimes. Herein, we report a tandem H2 photocycle based on combination of a non-basic photoredox phosphine mediator and nickel metal catalyst. Synthetic studies and time-resolved photochemical studies have revealed that phosphines serve as photochemical H-atom donors to Ni(ii) trihalide complexes to deliver a Ni(i) centre. The H2 evolution catalytic cycle is closed by sequential disproportionation of Ni(i) to afford Ni(0) and Ni(ii) and protolytic H2 evolution from the Ni(0) intermediate. The results of these investigations suggest that H2 photogeneration proceeds by two sequential catalytic cycles: a photoredox cycle catalyzed by phosphines and an H2-evolution cycle catalyzed by Ni complexes to circumvent challenges of photochemistry with first-row transition metal complexes.
| S-EPMC5811117 | biostudies-literature
Project description:Dry methane reforming (DRM) presents a viable pathway for converting greenhouse gases into useful syngas. Nevertheless, the procedure requires robust and reasonably priced catalysts. This study explored using cost-effective cobalt and nickel combined into a single catalyst with different metal ratios. The reaction was conducted in a fixed reactor at 700 °C. The findings indicate that the incorporation of cobalt significantly enhances catalyst performance by preventing metal sintering, improving metal dispersion, and promoting beneficial metal-support interactions. The best-performing catalyst (3.75Ni+1.25Co-ScCeZr) achieved a good conversion rate of CH4 and CO2 at 46.8 %, and 60 % respectively after 330 minutes while maintaining good stability. The TGA and CO2-TPD analysis results show that the addition of Co to Ni reduces carbon formation, and increases the amount of strong basic sites and isolated O2- species, and the total amount of CO2 desorbed. These results collectively highlight the potential of cobalt-nickel catalysts for practical DRM applications and contribute to developing sustainable energy technologies.
| S-EPMC11625958 | biostudies-literature
Project description:The data presented in this article are related to the research article entitled "NiRh Nanosponges with Highly Efficient Electrocatalytic Performance for Hydrogen Evolution Reaction (N.-A. Nguyen et al., 2019) [1]. This article reports a facile method to prepare various NixRhy nanosponges while using NaBH4 as a reducing agent without using any surfactant. The structural and chemical properties of the obtained NixRhy nanosponges are investigated.
| S-EPMC6502737 | biostudies-literature
Project description:Ammonia decomposition has attracted increasing attention as a promising process for the on-site generation of hydrogen. In this study, Ni catalysts supported on perovskite-type oxides (ABO3) were prepared and the activity for ammonia decomposition was examined. The Ni/ANbO3 (A = Na and K) and Ni/AEMnO3 (AE = Ca, Sr, and Ba) catalysts were less effective for this reaction. Meanwhile, the Ni/REAlO3 (RE = La, Sm, and Gd) catalysts exhibited relatively high activity. For Ni/AETiO3 and Ni/AEZrO3, the performance strongly depended on the A-site element of the perovskite-type oxides, and the Sr and Ba elements were more effective than the Ca one in the respective series. The catalytic activity for Ni/AEZrO3 was higher than Ni/AETiO3 in the case of the same alkaline earth element, and Ni/BaZrO3 was the most active among the samples investigated in this work. For these series, the order in the performance corresponded well with that in the basic property. The nitrogen desorption profiles revealed that the evolution of nitrogen atoms, which is one of the kinetically slow steps, effectively proceeded for Ni/SrZrO3 and Ni/BaZrO3 compared with the conventional Ni catalysts. This promotion effect would be ascribed to the strong basic properties of the SrZrO3 and BaZrO3 supports, resulting in the high activity of Ni/SrZrO3 and Ni/BaZrO3 for ammonia decomposition.
| S-EPMC9085908 | biostudies-literature