3D printing of thermosets with diverse rheological and functional applicabilities.

ABSTRACT: Thermosets such as silicone are ubiquitous. However, existing manufacturing of thermosets involves either a prolonged manufacturing cycle (e.g., reaction injection molding), low geometric complexity (e.g., casting), or limited processable materials (e.g., frontal polymerization). Here, we report an in situ dual heating (ISDH) strategy for the rapid 3D printing of thermosets with complex structures and diverse rheological properties by incorporating direct ink writing (DIW) technique and a heating-accelerated in situ gelation mechanism. Enabled by an integrated Joule heater at the printhead, extruded thermosetting inks can quickly cure in situ, allowing for DIW of various thermosets with viscosities spanning five orders of magnitude, printed height over 100 mm, and high resolution of 50 μm. We further demonstrate DIW of a set of heterogenous thermosets using multiple functional materials and present a hybrid printing of a multilayer soft electronic circuit. Our ISDH strategy paves the way for fast manufacturing of thermosets for various emerging fields.

SUBMITTER: Sun Y

PROVIDER: S-EPMC9842742 | biostudies-literature | 2023 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

3D printing of thermosets with diverse rheological and functional applicabilities.

Sun Yuxuan Y Wang Liu L Ni Yangyang Y Zhang Huajian H Cui Xiang X Li Jiahao J Zhu Yinbo Y Liu Ji J Zhang Shiwu S Chen Yong Y Li Mujun M

Nature communications 20230116 1

Thermosets such as silicone are ubiquitous. However, existing manufacturing of thermosets involves either a prolonged manufacturing cycle (e.g., reaction injection molding), low geometric complexity (e.g., casting), or limited processable materials (e.g., frontal polymerization). Here, we report an in situ dual heating (ISDH) strategy for the rapid 3D printing of thermosets with complex structures and diverse rheological properties by incorporating direct ink writing (DIW) technique and a heatin ...[more]

PMID: 36646723

Similar Datasets

Project description:The mechanical and rheological characterizations of flexible investment casting patterns capable of 3D printing are reported. The wax pattern was composed of microcrystalline hydrocarbon wax (DMW7478), Piccotex 75 (a copolymer of α-methyl-styrene and vinyl toluene with a 75/25 molar ratio, respectively) and Escorene (a copolymer of ethylene and vinyl acetate with a 72/28 mass ratio, respectively). It was found that in order to obtain a wax pattern with appreciable mechanical properties, the content of the microcrystalline hydrocarbon wax in these blends should not exceed 30% (m/m). Thus, a series of patterns with 28% (m/m) wax and varying Piccotex and Escorene contents spanning from 0 to 72% (m/m) was prepared. The dependence of the dynamic viscosities of the wax patterns on the composition was described using a stretched exponential model, whereas their variations with the temperature were interpreted in terms of the Arrhenius-Guzman equation. Furthermore, the slopes of the lines fitted to the viscosity versus temperature curves at the pour point decreased linearly with the Piccotex content. Non-Newtonian changes in the shear stress with the shear rate and shear stress crystallization were observed at temperatures near the pour points. The mechanical properties were evaluated using the uniaxial tensile mode and by three-point bending experiments. It was found that the stress (σ) versus the relative elongation (ε) curves can effectively be rendered by means of the standard linear solid (SLS) viscoelastic model. In addition, it was also established that the Young's modulus varied according to a sigmoid-type curve with the piccotex content, while the yield stress decreased linearly with the concentration of Piccotex. In addition, based on the spooling suitability and printability, the patterns were rated and it was found that the most appropriate wax pattern compositions for 3D printing were those which contained 30% (m/m) and 35% (m/m) Piccotex.

Dataset Information

3D printing of thermosets with diverse rheological and functional applicabilities.

Publications

3D printing of thermosets with diverse rheological and functional applicabilities.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets