ZnO/Graphene Composite from Solvent-Exfoliated Few-Layer Graphene Nanosheets for Photocatalytic Dye Degradation under Sunlight Irradiation.

ABSTRACT: ZnO/graphene nanocomposites were prepared using a facile approach. Graphene nanosheets were prepared by ultrasonication-based liquid phase exfoliation of graphite powder in a low boiling point organic solvent, 1,2-Dichloroethane, for the preparation of ZnO/graphene nanocomposites. Structural properties of the synthesized ZnO/graphene nanocomposites were studied through powder XRD and micro-Raman analysis. The characteristic Raman active modes of ZnO and graphene present in the micro-Raman spectra ensured the formation of ZnO/graphene nanocomposite and it is inferred that the graphene sheets in the composites were few layers in nature. Increasing the concentration of graphene influenced the surface morphology of the ZnO nanoparticles and a flower shape ZnO was formed on the graphene nanosheets of the composite with high graphene concentration. The efficiencies of the samples for the photocatalytic degradation of Methylene Blue dye under sunlight irradiation were investigated and 97% degradation efficiency was observed. The stability of the nanocomposites was evaluated by performing five cycles, and 92% degradation efficiency was maintained. The observed results were compared with that of ZnO/graphene composite derived from other methods.

SUBMITTER: Venkidusamy V

PROVIDER: S-EPMC9860591 | biostudies-literature | 2023 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

ZnO/Graphene Composite from Solvent-Exfoliated Few-Layer Graphene Nanosheets for Photocatalytic Dye Degradation under Sunlight Irradiation.

Venkidusamy Vasanthi V Nallusamy Sivanantham S Nammalvar Gopalakrishnan G Veerabahu Ramakrishnan R Thirumurugan Arun A Natarajan Chidhambaram C Dhanabalan Shanmuga Sundar SS Pabba Durga Prasad DP Abarzúa Carolina Venegas CV Kamaraj Sathish-Kumar SK

Micromachines 20230112 1

ZnO/graphene nanocomposites were prepared using a facile approach. Graphene nanosheets were prepared by ultrasonication-based liquid phase exfoliation of graphite powder in a low boiling point organic solvent, 1,2-Dichloroethane, for the preparation of ZnO/graphene nanocomposites. Structural properties of the synthesized ZnO/graphene nanocomposites were studied through powder XRD and micro-Raman analysis. The characteristic Raman active modes of ZnO and graphene present in the micro-Raman spectr ...[more]

PMID: 36677250

Similar Datasets

Project description:Photocatalysts suffer from a lack of separation of photogenerated excitons due to the fast recombination of charge carriers, so a strong synergistic effect exhibited by photocatalysts is promising for effective photocatalysis. Herein, we have synthesized efficient visible light functionalized graphene oxide nanosheet (FGS)/ZnO nanocomposite photocatalysts via a simple and economical approach with large scale production for practical applications. A series of nanocomposites (FGS/ZnO NCs) with different amounts by weight of graphene oxide (GO) have been synthesized via a facile solution route followed by calcination under environmental conditions. The phase, purity and morphological studies of the synthesized FGS/ZnO NCs were carried out using powder X-ray diffraction (XRD) and transmission electron microscopy (TEM). The optical properties were studied using UV-visible diffuse reflectance spectroscopy (DRS) and photoluminescence spectroscopy (PL). XRD results confirm the formation of a pure phase of ZnO in the FGS/ZnO NCs and TEM results show strongly adhered ZnO NPs on the surface of the FGS. DRS results confirm the extension of light absorption in the visible region while PL results confirm the effective separation of charge carriers in 0.09 wt% FGS/ZnO NCs. The synthesized photocatalyst efficiently degrades carcinogenic safranin-T dye under visible light illumination which is reported for the first time using FGS/ZnO nanocomposites. Photocatalytic studies confirm the higher photocatalytic activity of 0.09 wt% FGS/ZnO NCs (about 94.5%) towards the photodegradation of safranin-T dye in aqueous solution under visible light. The improved photocatalytic activity of 0.09 wt% FGS/ZnO NCs can be ascribed to the integrative synergistic effects of the enhanced adsorption capacity of safranin-T dye, effective separation of photogenerated excitons and effective interfacial hybridization of FGS and ZnO NCs. The generation of reactive oxygen species was confirmed using terephthalic acid as a probe molecule and a scavenger test was conducted in presence of histidine.

Project description:In this study, a variety of ZnO-based heterojunctions with disparate wt.% doping of WO3 and BiOI have been prepared for the photodestruction of methyl orange (MO) dye in aqueous solution. The composites were analysed by scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction, optical studies, and nitrogen adsorption-desorption isotherms. The SEM images revealed non-uniform surfaces of the ZnO-BiOI based composites while mostly nodular morphology was observed for all three samples of ZnO-WO3. As the WO3 loading increased, more clustering was detected. The analysed samples exhibited characteristic peaks representative of the triclinic phase of WO3 and the hexagonal wurtzite structure of ZnO, while the diffractogram observed from the materials displayed distinct peaks corresponding to the crystalline phases of both BiOI and ZnO in their pure forms. Further evidence of the samples' characteristics includes the presence of distinct crystalline patterns without any impurity peaks, a red shift in the absorption spectra of the heterostructure, the detection of only the reference elements, and mostly Type IV isotherm adsorption. This study identified the ZnO-[10%]BiOI and ZnO-[10%]WO3 heterojunctions as the best performing photocatalysts, as MO was completely destroyed in 120 and 90 min, respectively. Thus, confirming 10% wt. as the optimal doping concentration for the best photo-activity in this study. The impact of varying process parameters demonstrates that at an elevated photocatalyst mass of 40 mg, both heterojunctions effectively degraded MO. The photodegradation efficiency of MO was more pronounced in strong acidic conditions (pH 2) when compared to high alkaline conditions (pH 11) for the ZnO-[10%]BiOI heterostructure. However, a decrease in performance was observed for both strong acidic and high alkaline pH values when the ZnO-[10%]WO3 heterostructure was applied. The kinetic analysis of the photodegradation study reveals that all the photodegradation experiments can be represented by the pseudo-first-order kinetic model. The findings from this investigation propose that the ZnO-[10%]BiOI heterojunction photocatalyst holds significant potential for the effective treatment of dye-contaminated wastewater.

Dataset Information

ZnO/Graphene Composite from Solvent-Exfoliated Few-Layer Graphene Nanosheets for Photocatalytic Dye Degradation under Sunlight Irradiation.

Publications

ZnO/Graphene Composite from Solvent-Exfoliated Few-Layer Graphene Nanosheets for Photocatalytic Dye Degradation under Sunlight Irradiation.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets