Separation Mechanisms and Anti-Fouling Properties of a Microporous Polyvinylidene Fluoride-Polyacrylic Acid-Graphene Oxide (PVDF-PAA-GO) Composite Membrane with Salt and Protein Solutions.

ABSTRACT: This research demonstrates the preparation of composite membranes containing graphene oxide (GO) and investigates the separation mechanisms of various salts and bovine serum albumin (BSA) solutions. A microporous polyvinylidene fluoride-polyacrylic acid-GO (PVDF-PAA-GO) separation layer was fabricated on non-woven support. The GO-incorporating composite resulted in enlarged pore size (0.16 μm) compared with the control membrane (0.12 μm). The zeta potential of the GO composite was reduced to -31 from -19 mV. The resulting membranes with and without GO were examined for water permeability and rejection efficiency with single salt and BSA solutions. Using the non-woven/PVDF-PAA composite, the permeance values were 88-190 kg/m²hMPa, and the salt rejection coefficients were 9-28% fo

SUBMITTER: Wang LT 

PROVIDER: S-EPMC9860620 | biostudies-literature | 2022 Dec

REPOSITORIES: biostudies-literature