Mechanistic Model with Empirical Pitting Onset Approach for Detailed and Efficient Virtual Analysis of Atmospheric Bimetallic Corrosion.

ABSTRACT: A mechanistic model of atmospheric bimetallic corrosion with a simplified empirical approach to the onset of localized corrosion attacks is presented. The model was built for a typical bimetallic sample containing aluminum alloy 1050 and stainless steel 316L sheets. A strategy was developed that allowed the model to be calibrated against the measured galvanic current, geometrical corrosion attack properties, and corrosion products. The pitting-onset simplification sets all pits to be formed at a position near the nobler metal and treated all pits as being of the same shape and size. The position was based on the location of the highest pitting events and the pit attributes on an average of the deepest pits. For 5 h exposure at controlled RH (85%, 91%, and 97%) and salt load (86 μg NaCl/cm²), the model was shown to be promising: both for analysis of local bimetallic corrosion chemistry, such as pH and corrosion products, and for efficient assessment of pitting damage by computing a single largest pit depth. Parametric studies indicated that the pitting-onset approximation deviated the most at the beginning of exposure and when RH was below 91%.

SUBMITTER: Zavalis TG

PROVIDER: S-EPMC9917702 | biostudies-literature | 2023 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Mechanistic Model with Empirical Pitting Onset Approach for Detailed and Efficient Virtual Analysis of Atmospheric Bimetallic Corrosion.

Zavalis Tommy G TG Ström Mats M Persson Dan D Wendel Erik E Ahlström Johan J Törne Karin Beaussant KB Taxén Claes C Rendahl Bo B Voltaire Joakim J Eriksson Katarina K Thierry Dominique D Tidblad Johan J

Materials (Basel, Switzerland) 20230118 3

A mechanistic model of atmospheric bimetallic corrosion with a simplified empirical approach to the onset of localized corrosion attacks is presented. The model was built for a typical bimetallic sample containing aluminum alloy 1050 and stainless steel 316L sheets. A strategy was developed that allowed the model to be calibrated against the measured galvanic current, geometrical corrosion attack properties, and corrosion products. The pitting-onset simplification sets all pits to be formed at a ...[more]

PMID: 36769928

Similar Datasets

Project description:Despite observations of steel corrosion in nitrate-reducing environments, processes of nitrate-dependent microbially influenced corrosion (MIC) remain poorly understood and difficult to identify. We evaluated carbon steel corrosion by Shewanella oneidensis MR-1 under nitrate-reducing conditions using a split-chamber/zero-resistance ammetry (ZRA) technique. This approach entails the deployment of two metal (carbon steel 1018 in this case) electrodes into separate chambers of an electrochemical split-chamber unit, where the microbiology or chemistry of the chambers can be manipulated. This approach mimics the conditions of heterogeneous metal coverage that can lead to uniform and pitting corrosion. The current between working electrode 1 (WE1) and WE2 can be used to determine rates, mechanisms, and, we now show, extents of corrosion. When S. oneidensis was incubated in the WE1 chamber with lactate under nitrate-reducing conditions, nitrite transiently accumulated, and electron transfer from WE2 to WE1 occurred as long as nitrite was present. Nitrite in the WE1 chamber (without S. oneidensis) induced electron transfer in the same direction, indicating that nitrite cathodically protected WE1 and accelerated the corrosion of WE2. When S. oneidensis was incubated in the WE1 chamber without an electron donor, nitrate reduction proceeded, and electron transfer from WE2 to WE1 also occurred, indicating that the microorganism could use the carbon steel electrode as an electron donor for nitrate reduction. Our results indicate that under nitrate-reducing conditions, uniform and pitting carbon steel corrosion can occur due to nitrite accumulation and the use of steel-Fe(0) as an electron donor, but conditions of sustained nitrite accumulation can lead to more-aggressive corrosive conditions.IMPORTANCE Microbially influenced corrosion (MIC) causes damage to metals and metal alloys that is estimated to cost over $100 million/year in the United States for prevention, mitigation, and repair. While MIC occurs in a variety of settings and by a variety of organisms, the mechanisms by which microorganisms cause this damage remain unclear. Steel pipe and equipment may be exposed to nitrate, especially in oil and gas production, where this compound is used for corrosion and "souring" control. In this paper, we show uniform and pitting MIC under nitrate-reducing conditions and that a major mechanism by which it occurs is via the heterogeneous cathodic protection of metal surfaces by nitrite as well as by the microbial oxidation of steel-Fe(0).

Dataset Information

Mechanistic Model with Empirical Pitting Onset Approach for Detailed and Efficient Virtual Analysis of Atmospheric Bimetallic Corrosion.

Publications

Mechanistic Model with Empirical Pitting Onset Approach for Detailed and Efficient Virtual Analysis of Atmospheric Bimetallic Corrosion.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets