Highly Efficient Recovery and Recycling of Cobalt from Spent Lithium-Ion Batteries Using an N-Methylurea–Acetamide Nonionic Deep Eutectic Solvent
Ontology highlight
ABSTRACT:
SUBMITTER: Suriyanarayanan S
PROVIDER: S-EPMC9948188 | biostudies-literature | 2023 Feb
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:The application of deep eutectic solvents (DESs) to dissolve metal oxides in lithium-ion batteries (LIBs) recycling represents a green technological alternative to the mineral acids employed in hydrometallurgical recycling processes. However, DESs are much more expensive than mineral acids and must be reused to ensure economic feasibility of LIB recycling. To evaluate DES reusability, the role of the choline chloride-ethylene glycol DES decomposition products on metal oxides dissolution was investigated. The temperatures generally applied to carry on this DES leaching induced the formation of decomposition products that ultimately improved the ability to dissolve LIB metal oxides. The characterization of DES decomposition products revealed that the improved metal dissolution was mainly determined by the formation of Cl3 - , which was proposed to play a pivotal role in the oxidative dissolution of LIB metal oxides.
| S-EPMC9804844 | biostudies-literature
Project description:The transition to a circular economy vision must handle the increasing request of metals required to satisfy the battery industry; this can be obtained by recycling and feeding back secondary raw materials recovered through proper waste management. Here, a novel and green proof-of-concept was developed, based on deep eutectic solvents (DESs) to fully and easily recover valuable metals from various cathode active materials, including LiMn2 O4 , LiNi0.5 Mn1.5 O4 , and LiNi0.8 Co0.2 O2 . DES composed of choline chloride and lactic acid could leach Li, Mn, Co, and Ni, achieving efficiency of 100 % under much milder conditions with respect to the previous literature. For the first time, to our best knowledge, a two-step approach was reported in the case of LiNi0.8 Co0.2 O2 for selective recovery of Li, Co, and Ni with high yield and purity. Furthermore, other cathode components, namely aluminum current collector and binder, were found to be not dissolved by the proposed DES, thus making a simple separation from the active material possible. Finally, this strategy was designed to easily regenerate and reuse the leaching solvents for more than one extraction, thus further boosting process sustainability.
| S-EPMC9305586 | biostudies-literature
Project description:Deep eutectic solvents (DESs) have attracted extensive research for their potential applications as leaching solvent to recycle valuable metal elements from spent lithium ion batteries (LIBs). Despite various advantages like being economical and green, the full potential of conventional binary DES has not yet been harnessed because of the kinetics during leaching. Herein, we consider the fundamental rate-determining-step (RDS) in conventional binary DES and attempt to design ternary DES, within which the chemical reaction kinetics and diffusion kinetics can be regulated to maximize the overall leaching rate. As a proof of concept, we show that the ternary choline chloride/succinic acid/ethylene glycol (ChCl/SA/EG) type ternary DES can completely dissolve LCO powder at 140 °C in 16 h. By systematically studying the leaching process at various conditions, the energy barrier during leaching can be calculated to be 11.77 kJ/mol. Furthermore, we demonstrate that the extraction of the cobalt ions from the leaching solution can be directly achieved by adding oxalic ions without neutralizing the solution. The precipitate can be used to regenerate LCO with high purity. The recycled materials show comparable electrochemical performance with commercial LCO. Our design strategy of ternary DES with regulated RDS is expected to have both scientific and technological significance in the field of hydrometallurgical recycling of LIBs.
| S-EPMC8992278 | biostudies-literature
Project description:Recycling lithium from spent batteries is challenging because of problems with poor purity and contamination. Here, we propose a green and sustainable lithium recovery strategy for spent batteries containing LiFePO4, LiCoO2, and LiNi0.5Co0.2Mn0.3O2 electrodes. Our proposed configuration of "lithium-rich electrode || LLZTO@LiTFSI+P3HT || LiOH" system achieves double-side and roll-to-roll recycling of lithium-containing electrode without destroying its integrity. The LiTFSI+P3HT-modified LLZTO membrane also solves the H+/Li+ exchange problem and realizes a waterproof protection of bare LLZTO in the aqueous working environment. On the basis of these advantages, our system shows high Li selectivity (97%) and excellent Faradaic efficiency (≥97%), achieving high-purity (99%) LiOH along with the production of H2. The Li extraction processes for spent LiFePO4, LiNi0.5Co0.2Mn0.3O2, and LiCoO2 batteries is shown to be economically feasible. Therefore, this study provides a previously unexplored technology with low energy consumption as well as high economic and environmental benefits to realize sustainable lithium recycling from spent batteries.
| S-EPMC9534500 | biostudies-literature
Project description:The recycling of spent lithium-ion batteries can effectively mitigate the environmental and resource challenges arising from the escalating generation of battery waste and the soaring demand for battery metals. The existing mixing-then-separating recycling process is confronted with high entropy-increasing procedures, including crushing and leaching, which result in irreversible entropy production due to the decrease in material orderliness or heavy chemical consumption, thereby hindering its thermodynamic efficiency and economic viability of the entire recycling process. Herein, we propose a galvanic leaching strategy that leverages the self-assembly of LiNi0.6Co0.2Mn0.2O2 particles with their inherent aluminium foil current collectors in spent lithium-ion batteries, creating a primary cell system capable of recovering battery metals without pre-crushing or additional reductants. Under the theoretical potential difference of up to 3.84 V, the electrons flow and charge aggregation effectively achieve the valence state reduction, crystal phase transition and coordination environment change of the hard-to-dissolve metal components, contributing to over 90% battery metals recovery and a nearly 30-fold increase in leaching kinetics. Environmental-economic assessments further indicate that this strategy reduces energy consumption and carbon emissions by 11.36%-21.10% and 5.08%-23.18%, respectively, compared to conventional metallurgical methods, while enhancing economic benefits by 21.14%-49.18%.
| S-EPMC11897126 | biostudies-literature
Project description:Development of effective recycling strategies for cathode materials in spent lithium-ion batteries are highly desirable but remain significant challenges, among which facile separation of Al foil and active material layer of cathode makes up the first important step. Here, we propose a reaction-passivation driven mechanism for facile separation of Al foil and active material layer. Experimentally, >99.9% separation efficiency for Al foil and LiNi0.55Co0.15Mn0.3O2 layer is realized for a 102 Ah spent cell within 5 mins, and ultrathin, dense aluminum-phytic acid complex layer is in-situ formed on Al foil immediately after its contact with phytic acid, which suppresses continuous Al corrosion. Besides, the dissolution of transitional metal from LiNi0.55Co0.15Mn0.3O2 is negligible and good structural integrity of LiNi0.55Co0.15Mn0.3O2 is well-maintained during the processing. This work demonstrates a feasible approach for Al foil-active material layer separation of cathode and can promote the green and energy-saving battery recycling towards practical applications.
| S-EPMC10397256 | biostudies-literature
Project description:Cation separation under extreme pH is crucial for lithium recovery from spent batteries, but conventional polyamide membranes suffer from pH-induced hydrolysis. Preparation of high performance nanofiltration membranes with excellent pH-resistance remains a challenge. Here we synthesize a high performance nanofiltration membrane (1,4,7,10-Tetraazacyclododecane (TAD)-1,3,5-Tris(bromomethyl)benzene (TBMB) thin film composite membranes (TFCMs)) with excellent pH-stability through interfacial quaternization reaction between TAD and TBMB. Due to the high stability of "C-N" bonds in TAD-TBMB TFCMs, its separation performance is stable even after 70 days immersion in concentrated acid (3 M H2SO4, HNO3, or HCl) and base (3 M NaOH), which is at least 15 times more stable than benchmark commercial membranes. The membrane shows an overall separation performance (11.3 L m-2 h-1 bar-1 (LMHB), RCo2+: 97% in 2 M H2SO4) due to the size sieving and the intensified charge repulsion, outperforming many of the state-of-the-art membranes. Finally, the TAD-TBMB TFCM remains stable during 30-days continuous nanofiltration of 2 M H2SO4 and leachate (2 M H2SO4, ions: 6.2 g L-1) from spent batteries.
| S-EPMC11603373 | biostudies-literature
Project description:To reduce the exploitation of mine resources and decrease the harm to the environment caused by urban electronic wastes, the recovery of critical metals in secondary resources is crucial. In this study, we have successfully developed an eco-friendly process to integrate the leaching and separation of cobalt (Co) from a spent lithium-ion battery (LIB) cathode using an amino acid-based aqueous biphasic system (ABS). We, for the first time, demonstrated a simple method for leaching a LIB cathode using only amino acids. In addition, we have investigated the leaching mechanism using the typical cathode active material lithium cobalt oxide (LiCoO2). Then, the Co was selectively extracted by a biphasic system (amino acid-PPG400-H2O). This novel process has an excellent prospect in the field of spent-battery recycling because of its eco-friendly and process-simplified advantages.
| S-EPMC9878538 | biostudies-literature
Project description:Olivine-type LiMnPO₄/C nanorods were successfully synthesized in a chloride/ethylene glycol-based deep eutectic solvent (DES) at 130 °C for 4 h under atmospheric pressure. As-synthesized samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Raman spectroscopy, Fourier transform infrared spectroscopy (FTIR) and electrochemical tests. The prepared LiMnPO₄/C nanorods were coated with a thin carbon layer (approximately 3 nm thick) on the surface and had a length of 100-150 nm and a diameter of 40-55 nm. The prepared rod-like LiMnPO₄/C delivered a discharge capacity of 128 mAh·g-1 with a capacity retention ratio of approximately 93% after 100 cycles at 1 C. Even at 5 C, it still had a discharge capacity of 106 mAh·g-1, thus exhibiting good rate performance and cycle stability. These results demonstrate that the chloride/ethylene glycol-based deep eutectic solvents (DES) can act as a new crystal-face inhibitor to adjust the oriented growth and morphology of LiMnPO₄. Furthermore, deep eutectic solvents provide a new approach in which to control the size and morphology of the particles, which has a wide application in the synthesis of electrode materials with special morphology.
| S-EPMC5459138 | biostudies-other
Project description:Reducing the number of stages, energy costs and carbon footprint of recycling processes is essential to overcome environmental challenges. The interest in replacing the acids used in traditional hydrometallurgical methods with deep eutectic solvents (DES), which are less toxic and more environmentally friendly, has been growing. The aim of this study is to estimate the potential use of this class of solvents in an ionometallurgical process of leaching and electrodeposition to recover silver as part of the recycling of solar panels, a major challenge of the years to come. In the present work, a circular recycling concept based on an iron redox shuttle was studied to leach and recover silver via electrodeposition. Different DESs were evaluated in combination with a hexahydrated iron(iii) chloride oxidizing agent. Ethaline DES has gained significant interest as it can attain a high silver leaching efficiency of 99.9% on crystallized silicon cell scraps at 75 °C. The promising results led to a comprehensive study of limits of this chemical system, focusing on the relation between the concentration of species (iron and water), the interfacial potential of silver (electrochemical measurements), and surface evolution (X-ray photoelectron spectroscopy analysis). Silver leaching was determined as a mixed control mechanism involving chemical and species diffusion dependence. The concentration of iron(iii) chloride appeared crucial, determining the kinetic of formation of a poorly soluble AgCl layer. Electrodeposition from leachate highlighted the need to use an oxygen-free atmosphere to produce high-quality silver. Finally, leaching at 75 °C and electrodeposition at 50 °C of silver from crystallized silicon cell scraps were demonstrated using Ethaline (1 : 2) + FeCl3·6H2O (0.12 mol L-1) under an argon atmosphere.
| S-EPMC11411502 | biostudies-literature