Easy Fabrication of Highly Thermal-Stable Cellulose Nanocrystals Using Cr(NO₃)₃ Catalytic Hydrolysis System: A Feasibility Study from Macro- to Nano-Dimensions.

ABSTRACT: This study reported on the feasibility and practicability of Cr(NO₃)₃ hydrolysis to isolate cellulose nanocrystals (CNCCr(NO3)3) from native cellulosic feedstock. The physicochemical properties of CNCCr(NO3)3 were compared with nanocellulose isolated using sulfuric acid hydrolysis (CNCH2SO4). In optimum hydrolysis conditions, 80 °C, 1.5 h, 0.8 M Cr(NO₃)₃ metal salt and solid-liquid ratio of 1:30, the CNCCr(NO3)3 exhibited a network-like long fibrous structure with the aspect ratio of 15.7, while the CNCH2SO4 showed rice-shape structure with an aspect ratio of 3.5. Additionally, Cr(NO₃)₃-treated CNC rendered a higher crystallinity (86.5% ± 0.3%) with high yield (83.6% ± 0.6%) as compared to the H₂SO₄-treated CNC (81.4% ± 0.1% and 54.7% ± 0.3%, respectively). Furthermore, better thermal stability of CNCCr(NO3)3 (344 °C) compared to CNCH2SO4 (273 °C) rendered a high potential for nanocomposite application. This comparable effectiveness of Cr(NO₃)₃ metal salt provides milder hydrolysis conditions for highly selective depolymerization of cellulosic fiber into value-added cellulose nanomaterial, or useful chemicals and fuels in the future.

SUBMITTER: Chen YW

PROVIDER: S-EPMC5344559 | biostudies-other | 2017 Jan

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:It is common knowledge that pure alginate hydrogel is more likely to have weak mechanical strength, a lack of cell recognition sites, extensive swelling and uncontrolled degradation, and thus be unable to satisfy the demands of the ideal scaffold. To address these problems, we attempted to fabricate alginate/bacterial cellulose nanocrystals-chitosan-gelatin (Alg/BCNs-CS-GT) composite scaffolds using the combined method involving the incorporation of BCNs in the alginate matrix, internal gelation through the hydroxyapatite-d-glucono-δ-lactone (HAP-GDL) complex, and layer-by-layer (LBL) electrostatic assembly of polyelectrolytes. Meanwhile, the effect of various contents of BCNs on the scaffold morphology, porosity, mechanical properties, and swelling and degradation behavior was investigated. The experimental results showed that the fabricated Alg/BCNs-CS-GT composite scaffolds exhibited regular 3D morphologies and well-developed pore structures. With the increase in BCNs content, the pore size of Alg/BCNs-CS-GT composite scaffolds was gradually reduced from 200 μm to 70 μm. Furthermore, BCNs were fully embedded in the alginate matrix through the intermolecular hydrogen bond with alginate. Moreover, the addition of BCNs could effectively control the swelling and biodegradation of the Alg/BCNs-CS-GT composite scaffolds. Furthermore, the in vitro cytotoxicity studies indicated that the porous fiber network of BCNs could fully mimic the extracellular matrix structure, which promoted the adhesion and spreading of MG63 cells and MC3T3-E1 cells on the Alg/BCNs-CS-GT composite scaffolds. In addition, these cells could grow in the 3D-porous structure of composite scaffolds, which exhibited good proliferative viability. Based on the effect of BCNs on the cytocompatibility of composite scaffolds, the optimum BCNs content for the Alg/BCNs-CS-GT composite scaffolds was 0.2% (w/v). On the basis of good merits, such as regular 3D morphology, well-developed pore structure, controlled swelling and biodegradation behavior, and good cytocompatibility, the Alg/BCNs-CS-GT composite scaffolds may exhibit great potential as the ideal scaffold in the bone tissue engineering field.

Dataset Information

Easy Fabrication of Highly Thermal-Stable Cellulose Nanocrystals Using Cr(NO₃)₃ Catalytic Hydrolysis System: A Feasibility Study from Macro- to Nano-Dimensions.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets