The Influence of Stored Energy on Grain Boundary Chemistry and Intergranular Corrosion Development in AA2024-T3 Alloy.

ABSTRACT: Following our previous research, the correlation between the micro-chemistry of grain boundary and the distribution of stored energy in AA2024-T3 alloy is investigated, using the combination of transmission Kikuchi diffraction and transmission electron microscopy. It is found that the difference of dislocation density, namely stored energy, between two neighboring grains significantly affects the micro-chemistry of the grain boundary. Further, it is revealed that intergranular corrosion development in the AA2024-T3 alloy is mainly attributed to the combined effect of grain boundary chemistry and stored energy distribution.

SUBMITTER: Zhang X

PROVIDER: S-EPMC6265874 | biostudies-other | 2018 Nov

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Publications

The Influence of Stored Energy on Grain Boundary Chemistry and Intergranular Corrosion Development in AA2024-T3 Alloy.

Zhang Xinxin X Zhou Xiaorong X Cai Guangyi G Yu Yang Y Lu Xueqin X Jiao Yanbin Y Dong Zehua Z

Materials (Basel, Switzerland) 20181116 11

Following our previous research, the correlation between the micro-chemistry of grain boundary and the distribution of stored energy in AA2024-T3 alloy is investigated, using the combination of transmission Kikuchi diffraction and transmission electron microscopy. It is found that the difference of dislocation density, namely stored energy, between two neighboring grains significantly affects the micro-chemistry of the grain boundary. Further, it is revealed that intergranular corrosion developm ...[more]

PMID: 30453489

Similar Datasets

Learning grain boundary segregation energy spectra in polycrystals.

Project description:The segregation of solute atoms at grain boundaries (GBs) can profoundly impact the structural properties of metallic alloys, and induce effects that range from strengthening to embrittlement. And, though known to be anisotropic, there is a limited understanding of the variation of solute segregation tendencies across the full, multidimensional GB space, which is critically important in polycrystals where much of that space is represented. Here we develop a machine learning framework that can accurately predict the segregation tendency-quantified by the segregation enthalpy spectrum-of solute atoms at GB sites in polycrystals, based solely on the undecorated (pre-segregation) local atomic environment of such sites. We proceed to use the learning framework to scan across the alloy space, and build an extensive database of segregation energy spectra for more than 250 metal-based binary alloys. The resulting machine learning models and segregation database are key to unlocking the full potential of GB segregation as an alloy design tool, and enable the design of microstructures that maximize the useful impacts of segregation.

| S-EPMC7733488 | biostudies-literature

Tailoring grain boundary stability of zinc-titanium alloy for long-lasting aqueous zinc batteries.

Project description:The detrimental parasitic reactions and uncontrolled deposition behavior derived from inherently unstable interface have largely impeded the practical application of aqueous zinc batteries. So far, tremendous efforts have been devoted to tailoring interfaces, while stabilization of grain boundaries has received less attention. Here, we demonstrate that preferential distribution of intermetallic compounds at grain boundaries via an alloying strategy can substantially suppress intergranular corrosion. In-depth morphology analysis reveals their thermodynamic stability, ensuring sustainable potency. Furthermore, the hybrid nucleation and growth mode resulting from reduced Gibbs free energy contributes to the spatially uniform distribution of Zn nuclei, promoting the dense Zn deposition. These integrated merits enable a high Zn reversibility of 99.85% for over 4000 cycles, steady charge-discharge at 10 mA cm-2, and impressive cyclability for roughly 3500 cycles in Zn-Ti//NH4V4O10 full cell. Notably, the multi-layer pouch cell of 34 mAh maintains stable cycling for 500 cycles. This work highlights a fundamental understanding of microstructure and motivates the precise tuning of grain boundary characteristics to achieve highly reversible Zn anodes.

| S-EPMC10625522 | biostudies-literature

Kinetic Modeling of Grain Boundary Diffusion: The Influence of Grain Size and Surface Processes.

Project description:Based on rate equations, the kinetics of atom adsorption, desorption, and diffusion in polycrystalline materials is analyzed in order to understand the influence of grain boundaries and grain size. The boundary conditions of the proposed model correspond with the real situation in the electrolytes of solid oxide hydrogen fuel cells (SOFC). The role of the ratio of grain boundary and grain diffusion coefficients in perpendicular and parallel (to the surface) concentration profiles is investigated. In order to show the influence of absolute values of grain and grain boundary diffusion coefficients, we select four different cases in which one of the diffusion coefficients is kept constant while the others vary. The influence of grain size on diffusion processes is investigated using different geometrical models. The impact of kinetic processes taking place on the surface is analyzed by comparing results obtained assuming the first layer as a constant source and then involving in the model the processes of adsorption and desorption. It is shown that surface processes have a significant influence on the depth distribution of diffusing atoms and cannot be ignored. The analytical function of overall concentration dependence on grain and grain boundary volume ratio (Vg/Vgb) is found. The solution suggests that the concentration increases as a complementary error function while Vg/Vgb decreases.

| S-EPMC7084621 | biostudies-literature

Improve sensitization and corrosion resistance of an Al-Mg alloy by optimization of grain boundaries.

Project description:The sensitization and subsequent intergranular corrosion of Al-5.3 wt.% Mg alloy has been shown to be an important factor in stress corrosion cracking of Al-Mg alloys. Understanding sensitization requires the review of grain boundary character on the precipitation process which can assist in developing and designing alloys with improved corrosion resistance. This study shows that the degree of precipitation in Al-Mg alloy is dependent on grain boundary misorientation angle, adjacent grain boundary planes and grain boundary types. The results show that the misorientation angle is the most important factor influencing precipitation in grain boundaries of the Al-Mg alloy. Low angle grain boundaries (≤15°) have better immunity to precipitation and grain boundary acid attack. High angle grain boundaries (>15°) are vulnerable to grain boundary acid attack. Grain boundaries with adjacent plane orientations near to {100} have potential for immunity to precipitation and grain boundary acid attack. This work shows that low Σ (Σ ≤ 29) coincident site lattice (CSL) grain boundaries have thinner β precipitates. Modified nitric acid mass loss test and polarization test demonstrated that the global corrosion resistance of sputtered Al-Mg alloy is enhanced. This may be attributed to the increased fractions of low Σ (Σ ≤ 29) CSL grain boundaries after sputtering.

| S-EPMC4882518 | biostudies-literature

Effect of Grain Structure and Quenching Rate on the Susceptibility to Exfoliation Corrosion in 7085 Alloy.

Project description:The influence of grain structure and quenching rates on the exfoliation corrosion (EXCO) susceptibility of 7085 alloy was studied using immersion tests, optical microscopy (OM), scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), and scanning transmission electron microscopy (STEM). The results show that as the cooling rate decreases from 1048 °C/min to 129 °C/min; the size of grain boundary precipitates (GBPs); the width of precipitate-free zones (PFZ); and the content of Zn, Mg, and Cu in GBPs rise, leading to an increase in EXCO depth and consequently higher EXCO susceptibility. Meanwhile, there is a linear relationship between the average corrosion depth and the logarithm of the cooling rate. Corrosion cracks initiate at the grain boundaries (GBs) and primarily propagate along the HAGBs. In the bar grain (BG) sample at lower cooling rates, crack propagation along the sub-grain boundaries (SGBs) was observed. Compared to equiaxed grain (EG) samples, the elongated grain samples exhibit larger GBPs, a wider PFZ, and minor compositional differences in the GBPs, resulting in higher EXCO susceptibility.

| S-EPMC10574189 | biostudies-literature

Effects of Deformation Texture and Grain Size on Corrosion Behavior of Mg-3Al-1Zn Alloy Sheets.

Project description:Effects of deformation texture and grain size on mechanical properties and corrosion behavior of the Mg-3Al-1Zn (AZ31) alloys were systematically investigated. The results revealed that the ultimate tensile strength (UTS) and fracture elongation (FE) significantly increased from 232 to 273 MPa and 12.5 to 26.4%, respectively. According to the immersion and electrochemical measurements, the results indicated that the corrosion resistance of the alloy was improved obviously. Via electron backscattered diffraction (EBSD), corrosion morphology showed that the propagation of local pitting corrosion was suppressed, which is ascribed to grain refinement, higher texture intensity, and lower dislocation density after rolling and subsequent annealing.

| S-EPMC6990418 | biostudies-literature

Influence of grain boundary characteristics on thermal stability in nanotwinned copper.

Project description:High density grain boundaries provide high strength, but may introduce undesirable features, such as high Fermi levels and instability. We investigated the kinetics of recovery and recrystallization of Cu that was manufactured to include both nanotwins (NT) and high-angle columnar boundaries. We used the isothermal Johnson-Mehl-Avrami-Kolmogorov (JMAK) model to estimate activation energy values for recovery and recrystallization and compared those to values derived using the non-isothermal Kissinger equation. The JMAK model hinges on an exponent that expresses the growth mechanism of a material. The exponent for this Cu was close to 0.5, indicating low-dimensional microstructure evolution, which is associated with anisotropic twin coarsening, heterogeneous recrystallization, and high stability. Since this Cu was of high purity, there was a negligible impurity-drag-effect on boundaries. The twin coarsening and heterogeneous recrystallization resulted from migration of high-angle columnar boundaries with their triple junctions in one direction, assisted by the presence of high concentration vacancies at boundaries. Analyses performed by electron energy loss spectroscopy of atomic columns at twin boundaries (TBs) and in the interior showed similar plasma peak shapes and L3 edge positions. This implies that values for conductivity and Fermi level are equal for atoms at TBs and in the interior.

| S-EPMC4981844 | biostudies-literature

Standard Deviation Effect of Average Structure Descriptor on Grain Boundary Energy Prediction.

Project description:The structural complexities of grain boundaries (GBs) result in their complicated property contributions to polycrystalline metals and alloys. In this study, we propose a GB structure descriptor by linearly combining the average two-point correlation function (PCF) and standard deviation of PCF via a weight parameter, to reveal the standard deviation effect of PCF on energy predictions of Cu, Al and Ni asymmetric tilt GBs (i.e., Σ3, Σ5, Σ9, Σ11, Σ13 and Σ17), using two machine learning (ML) methods; i.e., principal component analysis (PCA)-based linear regression and recurrent neural networks (RNN). It is found that the proposed structure descriptor is capable of improving GB energy prediction for both ML methods. This suggests the discriminatory power of average PCF for different GBs is lifted since the proposed descriptor contains the data dispersion information. Meanwhile, we also show that GB atom selection methods by which PCF is evaluated also affect predictions.

| S-EPMC9919491 | biostudies-literature

Revealing Grain Boundary Sliding from Textures of a Deformed Nanocrystalline Pd-Au Alloy.

Project description:Employing a recent modeling scheme for grain boundary sliding [Zhao et al. Adv. Eng. Mater.2017, doi:10.1002/adem.201700212], crystallographic textures were simulated for nanocrystalline fcc metals deformed in shear compression. It is shown that, as grain boundary sliding increases, the texture strength decreases while the signature of the texture type remains the same. Grain boundary sliding affects the texture components differently with respect to intensity and angular position. A comparison of a simulation and an experiment on a Pd-10 atom % Au alloy with a 15 nm grain size reveals that, at room temperature, the predominant deformation mode is grain boundary sliding contributing to strain by about 60%.

| S-EPMC5848887 | biostudies-other

Influence of Temperature on Corrosion Behavior of 2A02 Al Alloy in Marine Atmospheric Environments.

Project description:The corrosion behavior of 2A02 Al alloy under 4 mg/cm² NaCl deposition at different temperatures (from 30 to 80 °C) has been studied. This corrosion behavior was researched using mass-gain, scanning electron microscopy-SEM, laser scanning confocal microscopy-LSCM, X-ray photoelectron spectroscopy-XPS and other techniques. The results showed and revealed that the corrosion was maximal at 60 °C after 200 h of exposure. The increase of temperature not only affected the solubility of oxygen gas in the thin film, but also promoted the transport of ions (such as Cl-), and the formation of protective AlO(OH), which further affects the corrosion speed.

| S-EPMC5848932 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data