Facile Synthesis of Nanoporous Pt-Y alloy with Enhanced Electrocatalytic Activity and Durability.

ABSTRACT: Recently, Pt-Y alloy has displayed an excellent electrocatalytic activity for oxygen reduction reaction (ORR), and is regarded as a promising cathode catalyst for fuel cells. However, the bulk production of nanoscaled Pt-Y alloy with outstanding catalytic performance remains a great challenge. Here, we address the challenge through a simple dealloying method to synthesize nanoporous Pt-Y alloy (NP-PtY) with a typical ligament size of ~5?nm. By combining the intrinsic superior electrocatalytic activity of Pt-Y alloy with the special nanoporous structure, the NP-PtY bimetallic catalyst presents higher activity for ORR and ethanol oxidation reaction, and better electrocatalytic stability than the commercial Pt/C catalyst and nanoporous Pt alloy. The as-made NP-PtY holds great application potential as a promising electrocatalyst in proton exchange membrane fuel cells due to the advantages of facile preparation and excellent catalytic performance.

PROVIDER: S-EPMC5288775 | BioStudies |

REPOSITORIES: biostudies

ACCESS DATA

Json Xml

Similar Datasets

Highly Active and Stable Pt-Pd Alloy Catalysts Synthesized by Room-Temperature Electron Reduction for Oxygen Reduction Reaction.

Project description:Carbon-supported platinum (Pt) and palladium (Pd) alloy catalyst has become a promising alternative electrocatalyst for oxygen reduction reaction (ORR) in proton exchange membrane fuel cells. In this work, the synthesis of highly active and stable carbon-supported Pt-Pd alloy catalysts is reported with a room-temperature electron reduction method. The alloy nanoparticles thus prepared show a particle size around 2.6 nm and a core-shell structure with Pt as the shell. With this structure, the breaking of O-O bands and desorption of OH are both promoted in electrocatalysis of ORR. In comparison with the commercial Pt/C catalyst prepared by conventional method, the mass activity of the Pt-Pd/C catalyst for ORR is shown to increase by a factor of ?4. After 10 000-cycle durability test, the Pt-Pd/C catalyst is shown to retain 96.5% of the mass activity, which is much more stable than that of the commercial Pt/C catalyst.

2017-01-01 | S-EPMC5396164 | BioStudies

Enhancement of Electrocatalytic Oxygen Reduction Activity and Durability of Pt-Ni Rhombic Dodecahedral Nanoframes by Anchoring to Nitrogen-Doped Carbon Support.

Project description:Pt-based nanostructured electrocatalysts supported on carbon black have been widely studied for the oxygen reduction reaction (ORR), which occurs at the cathode in polymer electrolyte fuel cells. Because sluggish ORR kinetics are known to govern the cell performance, there is a need to develop highly active and durable electrocatalysts. The ORR activity of Pt-based electrocatalysts can be improved by controlling their morphology and alloying Pt with transition metals such as Ni. Improving the catalyst durability remains challenging and there is a lack of catalyst design concepts and synthetic strategies. We report the enhancement of the ORR activity and durability of a nanostructured Pt-Ni electrocatalyst by strong metal/support interactions with a nitrogen-doped carbon (NC) support. Pt-Ni rhombic dodecahedral nanoframes (NFs) were immobilized on the NC support and showed higher ORR electrocatalytic activity and durability in acidic media than that supported on a nondoped carbon black. Durability tests demonstrated that NF/NC showed almost no activity loss even after 50?000 potential cycles under catalytic conditions, and the Ni dissolution from the NFs was suppressed at the NC support, as confirmed by energy dispersive X-ray spectroscopy analysis. Physicochemical measurements including surface-enhanced infrared absorption spectroscopy of surface-adsorbed CO revealed that the strong metal/support interactions of the NF with the NC support caused the downshift of the d-band center position of the surface Pt. Our findings demonstrate that tuning the electronic structure of nanostructured Pt alloy electrocatalysts via the strong metal/support interactions with heteroatom-doped carbon supports will allow the development of highly active and robust electrocatalysts.

| S-EPMC6644736 | BioStudies

Nafion-stabilised bimetallic Pt-Cr nanoparticles as electrocatalysts for proton exchange membrane fuel cells (PEMFCs).

Project description:The current study investigated the unique combination of alloying (Pt with Cr) and Nafion stabilisation to reap the benefits of catalyst systems with enhanced catalytic activity and improved durability in PEMFCs. Pt-Cr alloy nanoparticles stabilised with Nafion were chosen in the current study owing to their higher stability in acidic and oxidising media at high temperatures compared to other Pt-transition metal alloys (e.g. Pt-Ni, Pt-Co). Two different precursor?:?reducing agent (1?:?10 and 1?:?20) ratios were used in order to prepare two different alloys, denoted as Pt-Cr 10 and Pt-Cr 20. The Pt-Cr 20 alloy system (with composition Pt80Cr20) demonstrated higher electrocatalytic activity for the oxygen reduction reaction compared to commercial Pt/C (TKK) catalysts. Accelerated stress tests and single cell tests revealed that Nafion stabilised alloy catalyst systems displayed significantly enhanced durability (only ?20% loss of ECSA) compared with Pt/C (50% loss of ECSA) due to improved catalyst-ionomer interaction. Furthermore, the Pt-Cr 20 alloy system demonstrated a current density comparable to that of Pt/C making them promising potential electrocatalysts for proton exchange membrane fuel cells.

| S-EPMC5059791 | BioStudies

Inexpensive Ipomoea aquatica Biomass-Modified Carbon Black as an Active Pt-Free Electrocatalyst for Oxygen Reduction Reaction in an Alkaline Medium.

Project description:The development of inexpensive and active Pt-free catalysts as an alternative to Pt-based catalysts for oxygen reduction reaction (ORR) is an essential prerequisite for fuel cell commercialization. In this paper, we report a strategy for the design of a new Fe-N/C electrocatalyst derived from the co-pyrolysis of Ipomoea aquatica biomass, carbon black (Vulcan XC-72R) and FeCl₃·6H₂O at 900 °C under nitrogen atmosphere. Electrochemical results show that the Fe-N/C catalyst exhibits higher electrocatalytic activity for ORR, longer durability and higher tolerance to methanol compared to a commercial Pt/C catalyst (40 wt %) in an alkaline medium. In particular, Fe-N/C presents an onset potential of 0.05 V (vs. Hg/HgO) for ORR in an alkaline medium, with an electron transfer number (n) of ~3.90, which is close to that of Pt/C. Our results confirm that the catalyst derived from I. aquatica and carbon black is a promising non-noble metal catalyst as an alternative to commercial Pt/C catalysts.

2015-01-01 | S-EPMC5455408 | BioStudies

Cyanogel-Derived Synthesis of Porous PdFe Nanohydrangeas as Electrocatalysts for Oxygen Reduction Reaction.

Project description:It is important to develop cost-efficient electrocatalysts used in the oxygen reduction reaction (ORR) for widespread applications in fuel cells. Palladium (Pd) is a promising catalyst, due to its more abundant reserves and lower price than platinum (Pt), and doping an earth-abundant 3d-transition metal M into Pd to form Pd-M bimetallic alloys may not only further reduce the use of expensive Pd but also promote the electrocatalytic performance of ORR, owing to the synergistic effect between Pd and M. Here we report a cyanogel-derived synthesis of PdFe alloys with porous nanostructure via a simple coinstantaneous reduction reaction by using K2PdIICl4/K4FeII(CN)6 cyanogel as precursor. The synthesized PdFe alloys possess hydrangea-like morphology and porous nanostructure, which are beneficial to the electrochemical performance in ORR. The onset potential of the porous PdFe nanohydrangeas is determined to be 0.988 V, which is much more positive than that of commercial Pt/C catalyst (0.976 V) and Pd black catalyst (0.964 V). Resulting from the unique structural advantages and synergetic effect between bimetals, the synthesized PdFe nanohydrangeas with porous structure have outstanding electrocatalytic activity and stability for ORR, compared with the commercial Pd black and Pt/C.

| S-EPMC8708350 | BioStudies

In Situ X-ray Absorption Spectroscopy of PtNi-Nanowire/Vulcan XC-72R under Oxygen Reduction Reaction in Alkaline Media.

Project description:Studying the oxygen reduction reaction (ORR) in the alkaline electrolyte has proven to promote better catalytic responses and accessibility to commercialization. Ni-nanowires (NWs) were synthesized via the solvothermal method and modified with Pt using the spontaneous galvanic displacement method to obtain PtNi-NWs. Carbon Vulcan XC-72R (V) was used as the catalyst support, and they were doped with NH3 to obtain PtNi-NWs/V and PtNi-NWs/V-NH3. Their electrocatalytic response for the ORR was tested and PtNi-NWs/V provided the highest specific activity with logarithmic values of 0.707 and 1.01 (mA/cm2 Pt) at 0.90 and 0.85 V versus reversible hydrogen electrode (RHE), respectively. PtNi-NWs showed the highest half-wave potential (E 1/2 = 0.89 V) at 1600 rpm and 12 μgPt/cm2 in 0.1 M KOH at 25.00 ± 0.01 °C. Additionally, the catalysts followed a four-electron pathway according to the Koutecký-Levich analysis. Moreover, durability experiments demonstrated that the PtNi-NW/V performance loss was like that of commercial Pt/V along 10,000 cycles. Electrochemical ORR in situ X-ray absorption spectroscopy results showed that the Pt L3 edge white line in the PtNi-NW catalysts changed while the electrochemical potential was lowered to negatives values, from 1.0 to 0.3 V versus RHE. The Pt/O region in the in situ Fourier transforms remained the same as the potentials were applied, suggesting an alloy formation between Pt and Ni, and Pt/Pt contracted in the presence of Ni. These results provide a better understanding of PtNi-NWs in alkaline electrolytes, suggesting that they are active catalysts for ORR and can be tuned for fuel cell studies.

| S-EPMC8280705 | BioStudies

Enhancing electrocatalytic oxygen reduction on nitrogen-doped graphene by active sites implantation.

Project description:The shortage of nitrogen active sites and relatively low nitrogen content result in unsatisfying eletrocatalytic activity and durability of nitrogen-doped graphene (NG) for oxygen reduction reaction (ORR). Here we report a novel approach to substantially enhance electrocatalytic oxygen reduction on NG electrode by the implantation of nitrogen active sites with mesoporous graphitic carbon nitride (mpg-C3N4). Electrochemical characterization revealed that in neutral electrolyte the resulting NG (I-NG) exhibited super electrocatalytic activity (completely 100% of four-electron ORR pathway) and durability (nearly no activity change after 100,000 potential cyclings). When I-NG was used as cathode catalyst in microbial fuel cells (MFCs), power density and its drop percentage were also much better than the NG and Pt/C ones, demonstrating that the current I-NG was a perfect alternative to Pt/C and offered a new potential for constructing high-performance and less expensive cathode which is crucial for large-scale application of MFC technology.

| S-EPMC3837309 | BioStudies

Novel VN/C nanocomposites as methanol-tolerant oxygen reduction electrocatalyst in alkaline electrolyte.

Project description:A novel VN/C nanostructure consisting of VN nanoparticles and graphite-dominant carbon layers is synthesized by nitridation of V2O5 using melamine as reductant under inert atmosphere. High crystalline VN nanoparticles are observed to be uniformly distributed in carbon layers with an average size of ca13.45?nm. Moreover, the electrocatalytic performance of VN/C towards oxygen reduction reaction (ORR) in alkaline electrolyte is fascinating. The results show that VN/C has a considerable ORR activity, including a 75 percent value of the diffusion-limited current density and a 0.11?V smaller value about the onset potential with respect to Pt/C catalyst. Moreover, the excellent methanol-tolerance performance of VN/C has also been verified with 3?M methanol. Combined with the competitive prices, this VN/C nanocomposite can serve as an appropriate non-precious methanol-tolerant ORR catalyst for alkaline fuel cells.

2015-01-01 | S-EPMC4477409 | BioStudies

High-performance Platinum-free oxygen reduction reaction and hydrogen oxidation reaction catalyst in polymer electrolyte membrane fuel cell.

Project description:The integration of polymer electrolyte membrane fuel cell (PEMFC) stack into vehicles necessitates the replacement of high-priced platinum (Pt)-based electrocatalyst, which contributes to about 45% of the cost of the stack. The implementation of high-performance and durable Pt metal-free catalyst for both oxygen reduction reaction (ORR) and hydrogen oxidation reaction (HOR) could significantly enable large-scale commercialization of fuel cell-powered vehicles. Towards this goal, a simple, scalable, single-step synthesis method was adopted to develop palladium-cobalt alloy supported on nitrogen-doped reduced graphene oxide (Pd3Co/NG) nanocomposite. Rotating ring-disk electrode (RRDE) studies for the electrochemical activity towards ORR indicates that ORR proceeds via nearly four-electron mechanism. Besides, the mass activity of Pd3Co/NG shows an enhancement of 1.6 times compared to that of Pd/NG. The full fuel cell measurements were carried out using Pd3Co/NG at the anode, cathode in conjunction with Pt/C and simultaneously at both anode and cathode. A maximum power density of 68?mW/cm2 is accomplished from the simultaneous use of Pd3Co/NG as both anode and cathode electrocatalyst with individual loading of 0.5?mg/cm2 at 60?°C without any backpressure. To the best of our knowledge, the present study is the first of its kind of a fully non-Pt based PEM full cell.

| S-EPMC5827662 | BioStudies

B, N Codoped and Defect-Rich Nanocarbon Material as a Metal-Free Bifunctional Electrocatalyst for Oxygen Reduction and Evolution Reactions.

Project description:The development of highly active, inexpensive, and stable bifunctional oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) catalysts to replace noble metal Pt and RuO2 catalysts remains a considerable challenge for highly demanded reversible fuel cells and metal-air batteries. Here, a simple approach for the facile construction of a defective nanocarbon material is reported with B and N dopants (B,N-carbon) as a superior bifunctional metal-free catalyst for both ORR and OER. The catalyst is prepared by pyrolyzing the composites of ethyl cellulose and high-boiling point 4-(1-naphthyl)benzeneboronic acid in NH3 atmosphere with an inexpensive Zn-based template. The obtained porous B,N-carbon with rich carbon defects exhibits excellent ORR and OER performances, including high activity and stability. In alkaline medium, B,N-carbon material shows high ORR activity with an onset potential (Eonset) reaching 0.98 V versus reversible hydrogen electrode (RHE), very close to that of Pt/C, a high electron transfer number and excellent stability. This catalyst also presents the admirable ORR activity in acidic medium with a high Eonset of 0.81 V versus RHE and a four-electron process. The OER activity of B,N-carbon is superior to that of the precious metal RuO2 and Pt/C catalysts. A Zn-air battery using B,N-carbon as the air cathode exhibits a low voltage gap between charge and discharge and long-term stability. The excellent electrocatalytic performance of this porous nanocarbon material is attributed to the combined positive effects of the abundant carbon defects and the heteroatom codopants.

| S-EPMC6051395 | BioStudies

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data