Effect of Industrial By-Products on Unconfined Compressive Strength of Solidified Organic Marine Clayey Soils.


ABSTRACT: The use of industrial by-products as admixture to ASTM Type I cement (ordinary Portland cement (OPC)) was investigated with the objective of improving the solidification of organic marine clayey soils. The industrial by-products considered in this paper were oyster-shell powder (OSP), steelmaking slag dust (SMS) and fuel-gas-desulfurized (FGD) gypsum. The industrial by-products were added to OPC at a ratio of 5% based on dry weight to produce a mixture used to solidify organic marine clayey soils. The dosage ratios of mixtures to organic marine clayey soils were 5, 10 and 15% on a dry weight basis. Unconfined compressive strength (UCS) test after 28 days revealed that the highest strength was obtained with the OPC + SMS 15% mixing ratio. The UCS of specimens treated with this mixture was >500 kPa, compared with 300 kPa for specimens treated with a 15% OPC + OSP mixture and 200 kPa when 15% of OPC was used alone. These results were attributed to the more active hydration and pozzolanic reaction of the OPC + SMS mixture. This hypothesis was verified through X-ray diffraction (XRD) and scanning electron microscopy (SEM) analyses, and was confirmed by variations in the calcium carbonate (CaCO₃) content of the materials during curing.

SUBMITTER: Park CG 

PROVIDER: S-EPMC5455510 | BioStudies | 2015-01-01

SECONDARY ACCESSION(S): 10.3390/ma8085098

REPOSITORIES: biostudies

Similar Datasets

2017-01-01 | S-EPMC5537427 | BioStudies
2020-01-01 | S-EPMC7254802 | BioStudies
2017-01-01 | S-EPMC5524413 | BioStudies
2017-01-01 | S-EPMC5443863 | BioStudies
2007-01-01 | S-EPMC2180180 | BioStudies
2020-01-01 | S-EPMC7579171 | BioStudies
2020-01-01 | S-EPMC7037547 | BioStudies
2014-01-01 | S-EPMC3929488 | BioStudies
2014-01-01 | S-EPMC3869018 | BioStudies
2019-01-01 | S-EPMC6384646 | BioStudies