Modeling Cyclic Fatigue Hysteresis Loops of 2D Woven Ceramic Matrix Composites at Elevated Temperatures in Steam.


ABSTRACT: In this paper, the cyclic fatigue hysteresis loops of 2D woven SiC/SiC ceramic matrix composites (CMCs) at elevated temperatures in steam have been investigated. The interface slip between fibers and the matrix existing in matrix cracking modes 3 and 5, in which matrix cracking and interface debonding occurred in longitudinal yarns, is considered as the major reason for hysteresis loops of 2D woven CMCs. The hysteresis loops of 2D SiC/SiC composites corresponding to different peak stresses, test conditions, and loading frequencies have been predicted using the present analysis. The damage parameter, i.e., the proportion of matrix cracking mode 3 in the entire matrix cracking modes of the composite, and the hysteresis dissipated energy increase with increasing fatigue peak stress. With increasing cycle number, the interface shear stress in the longitudinal yarns decreases, leading to transition of interface slip types of matrix cracking modes 3 and 5.

SUBMITTER: Li L 

PROVIDER: S-EPMC5456755 | BioStudies | 2016-01-01

SECONDARY ACCESSION(S): 10.3390/ma9060421

REPOSITORIES: biostudies

Similar Datasets

2016-01-01 | S-EPMC5456581 | BioStudies
2016-01-01 | S-EPMC5456556 | BioStudies
2017-01-01 | S-EPMC5506978 | BioStudies
2017-01-01 | S-EPMC5459135 | BioStudies
2015-01-01 | S-EPMC5458855 | BioStudies
2019-01-01 | S-EPMC6678398 | BioStudies
2016-01-01 | S-EPMC5456649 | BioStudies
2016-01-01 | S-EPMC5512521 | BioStudies
2019-01-01 | S-EPMC6723977 | BioStudies
2019-01-01 | S-EPMC6749427 | BioStudies