Multifunctional Film Assembled from N-Doped Carbon Nanofiber with Co-N₄-O Single Atoms for Highly Efficient Electromagnetic Energy Attenuation.

ABSTRACT: Single-atom materials have demonstrated attractive physicochemical characteristics. However, understanding the relationships between the coordination environment of single atoms and their properties at the atomic level remains a considerable challenge. Herein, a facile water-assisted carbonization approach is developed to fabricate well-defined asymmetrically coordinated Co-N₄-O sites on biomass-derived carbon nanofiber (Co-N₄-O/NCF) for electromagnetic wave (EMW) absorption. In such nanofiber, one atomically dispersed Co site is coordinated with four N atoms in the graphene basal plane and one oxygen atom in the axial direction. In-depth experimental and theoretical studies reveal that the axial Co-O coordination breaks the charge distribution symmetry in the planar porphyrin-like Co-N₄ structure, leading to significantly enhanced dielectric polarization loss relevant to the planar Co-N₄ sites. Importantly, the film based on Co-N₄-O/NCF exhibits light weight, flexibility, excellent mechanical properties, great thermal insulating feature, and excellent EMW absorption with a reflection loss of - 45.82 dB along with an effective absorption bandwidth of 4.8 GHz. The findings of this work offer insight into the relationships between the single-atom coordination environment and the dielectric performance, and the proposed strategy can be extended toward the engineering of asymmetrically coordinated single atoms for various applications.

SUBMITTER: Xu J

PROVIDER: S-EPMC11233488 | biostudies-literature | 2024 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Multifunctional Film Assembled from N-Doped Carbon Nanofiber with Co-N4-O Single Atoms for Highly Efficient Electromagnetic Energy Attenuation.

Xu Jia J Li Bei B Ma Zheng Z Zhang Xiao X Zhu Chunling C Yan Feng F Yang Piaoping P Chen Yujin Y

Nano-micro letters 20240709 1

Single-atom materials have demonstrated attractive physicochemical characteristics. However, understanding the relationships between the coordination environment of single atoms and their properties at the atomic level remains a considerable challenge. Herein, a facile water-assisted carbonization approach is developed to fabricate well-defined asymmetrically coordinated Co-N4-O sites on biomass-derived carbon nanofiber (Co-N4-O/NCF) for electromagnetic wave (EMW) absorptio ...[more]

PMID: 38980475

Similar Datasets

Project description:Tunable porous composite materials to control metal and metal oxide functionalization, conductivity, pore structure, electrolyte mass transport, mechanical strength, specific surface area, and magneto-responsiveness are critical for a broad range of energy storage, catalysis, and sensing applications. Biotemplated transition metal composite aerogels present a materials approach to address this need. To demonstrate a solution-based synthesis method to develop cobalt and cobalt oxide aerogels for high surface area multifunctional energy storage electrodes, carboxymethyl cellulose nanofibers (CNF) and alginate biopolymers were mixed to form hydrogels to serve as biotemplates for cobalt nanoparticle formation via the chemical reduction of cobalt salt solutions. The CNF-alginate mixture forms a physically entangled, interpenetrating hydrogel, combining the properties of both biopolymers for monolith shape and pore size control and abundant carboxyl groups that bind metal ions to facilitate biotemplating. The CNF-alginate hydrogels were equilibrated in CaCl2 and CoCl2 salt solutions for hydrogel ionic crosslinking and the prepositioning of transition metal ions, respectively. The salt equilibrated hydrogels were chemically reduced with NaBH4, rinsed, solvent exchanged in ethanol, and supercritically dried with CO2 to form aerogels with a specific surface area of 228 m2/g. The resulting aerogels were pyrolyzed in N2 gas and thermally annealed in air to form Co and Co3O4 porous composite electrodes, respectively. The multifunctional composite aerogel's mechanical, magnetic, and electrochemical functionality was characterized. The coercivity and specific magnetic saturation of the pyrolyzed aerogels were 312 Oe and 114 emu/gCo, respectively. The elastic moduli of the supercritically dried, pyrolyzed, and thermally oxidized aerogels were 0.58, 1.1, and 14.3 MPa, respectively. The electrochemical testing of the pyrolyzed and thermally oxidized aerogels in 1 M KOH resulted in specific capacitances of 650 F/g and 349 F/g, respectively. The rapidly synthesized, low-cost, hydrogel-based synthesis for tunable transition metal multifunctional composite aerogels is envisioned for a wide range of porous metal electrodes to address energy storage, catalysis, and sensing applications.

Dataset Information

Multifunctional Film Assembled from N-Doped Carbon Nanofiber with Co-N₄-O Single Atoms for Highly Efficient Electromagnetic Energy Attenuation.

Publications

Multifunctional Film Assembled from N-Doped Carbon Nanofiber with Co-N<sub>4</sub>-O Single Atoms for Highly Efficient Electromagnetic Energy Attenuation.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets