Transistor application of alkyl-substituted picene.

ABSTRACT: Field-effect transistors (FETs) were fabricated with a thin film of 3,10-ditetradecylpicene, picene-(C14H29)2, formed using either a thermal deposition or a deposition from solution (solution process). All FETs showed p-channel normally-off characteristics. The field-effect mobility, μ, in a picene-(C14H29)2 thin-film FET with PbZr0.52Ti0.48O3 (PZT) gate dielectric reached ~21 cm2 V(-1) s(-1), which is the highest μ value recorded for organic thin-film FETs; the average μ value (<μ>) evaluated from twelve FET devices was 14(4) cm2 V(-1) s(-1). The <μ> values for picene-(C14H29)2 thin-film FETs with other gate dielectrics such as SiO2, Ta2O5, ZrO2 and HfO2 were greater than 5 cm2 V(-1) s(-1), and the lowest absolute threshold voltage, |Vth|, (5.2 V) was recorded with a PZT gate dielectric;