Transparent Thin-Film Transistors Based on Sputtered Electric Double Layer.

ABSTRACT: Electric-double-layer (EDL) thin-film transistors (TFTs) have attracted much attention due to their low operation voltages. Recently, EDL TFTs gated with radio frequency (RF) magnetron sputtered SiO₂ have been developed which is compatible to large-area electronics fabrication. In this work, fully transparent Indium-Gallium-Zinc-Oxide-based EDL TFTs on glass substrates have been fabricated at room temperature for the first time. A maximum transmittance of about 80% has been achieved in the visible light range. The transparent TFTs show a low operation voltage of 1.5 V due to the large EDL capacitance (0.3 µF/cm² at 20 Hz). The devices exhibit a good performance with a low subthreshold swing of 130 mV/dec and a high on-off ratio > 10⁵. Several tests have also been done to investigate the influences of light irradiation and bias stress. Our results suggest that such transistors might have potential applications in battery-powered transparent electron devices.

SUBMITTER: Cai W

PROVIDER: S-EPMC5506904 | biostudies-literature | 2017 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Transparent Thin-Film Transistors Based on Sputtered Electric Double Layer.

Cai Wensi W Ma Xiaochen X Zhang Jiawei J Song Aimin A

Materials (Basel, Switzerland) 20170420 4

Electric-double-layer (EDL) thin-film transistors (TFTs) have attracted much attention due to their low operation voltages. Recently, EDL TFTs gated with radio frequency (RF) magnetron sputtered SiO₂ have been developed which is compatible to large-area electronics fabrication. In this work, fully transparent Indium-Gallium-Zinc-Oxide-based EDL TFTs on glass substrates have been fabricated at room temperature for the first time. A maximum transmittance of about 80% has been achieved in the visib ...[more]

PMID: 28772789

Similar Datasets

A Sputtered Silicon Oxide Electrolyte for High-Performance Thin-Film Transistors.

Project description:Low operating voltages have been long desired for thin-film transistors (TFTs). However, it is still challenging to realise 1-V operation by using conventional dielectrics due to their low gate capacitances and low breakdown voltages. Recently, electric double layers (EDLs) have been regarded as a promising candidate for low-power electronics due to their high capacitance. In this work, we present the first sputtered SiO2 solid-state electrolyte. In order to demonstrate EDL behaviour, a sputtered 200 nm-thick SiO2 electrolyte was incorporated into InGaZnO TFTs as the gate dielectric. The devices exhibited an operating voltage of 1 V, a threshold voltage of 0.06 V, a subthreshold swing of 83 mV dec-1 and an on/off ratio higher than 105. The specific capacitance was 0.45 µF cm-2 at 20 Hz, which is around 26 times higher than the value obtained from thermally oxidised SiO2 films with the same thickness. Analysis of the microstructure and mass density of the sputtered SiO2 films under different deposition conditions indicates that such high capacitance might be attributed to mobile protons donated by atmospheric water. The InGaZnO TFTs with the optimised SiO2 electrolyte also showed good air stability. This work provides a new pathway to the realisation of high-yield low-power electronics.

| S-EPMC5429786 | biostudies-literature

Hydrophobic and stretchable Ag nanowire network electrode passivated by a sputtered PTFE layer for self-cleaning transparent thin film heaters.

Project description:We demonstrated hydrophobic, flexible/stretchable, and transparent electrodes made up of Ag nanowire (NW) networks passivated by a sputtered polytetrafluoroethylene (PTFE) layer to produce self-cleaning transparent thin film heaters (TFHs). Using carbon nanotubes and a PTFE mixed conducting target, we successfully sputtered a transparent PTFE layer on the Ag NW network using mid-frequency magnetron sputtering. The hydrophobic surface of the PTFE/Ag NW electrodes led to water-repelling and self-cleaning transparent Ag NW electrodes, which are beneficial for transparent TFH-based smart windows. Furthermore, hydrophobic PTFE/Ag NW electrodes coated on polyethylene terephthalate (PET) and polyurethane (PU) substrates showed outstanding flexibility and stretchability, respectively, due to the capping effect of the PTFE layer. Based on outer/inner bending and stretching test results, we demonstrated the superior mechanical properties of the PTFE/Ag NW electrode compared to a bare Ag NW electrode. Finally, we investigated the feasibility of the PTFE/Ag NW film coated on a PU substrate as a transparent and stretchable electrode for stretchable and self-cleaning transparent TFHs. The effective heat generation of the stretchable PTFE/Ag NW electrode indicates the potential for energy-efficient multi-functional PTFE/Ag NW-based TFHs attached to automobile windows.

| S-EPMC9080517 | biostudies-literature

Low-Temperature, Solution-Processed, Transparent Zinc Oxide-Based Thin-Film Transistors for Sensing Various Solvents.

Project description:A low temperature solution-processed thin-film transistor (TFT) using zinc oxide (ZnO) film as an exposed sensing semiconductor channel was fabricated to detect and identify various solution solvents. The TFT devices would offer applications for low-cost, rapid and highly compatible water-soluble detection and could replace conventional silicon field effect transistors (FETs) as bio-sensors. In this work, we demonstrate the utility of the TFT ZnO channel to sense various liquids, such as polar solvents (ethanol), non-polar solvents (toluene) and deionized (DI) water, which were dropped and adsorbed onto the channel. It is discussed how different dielectric constants of polar/non-polar solvents and DI water were associated with various charge transport properties, demonstrating the main detection mechanisms of the thin-film transistor.

| S-EPMC5503344 | biostudies-literature

Artificial Synaptic Devices Based on Natural Chicken Albumen Coupled Electric-Double-Layer Transistors.

Project description:Recent progress in using biomaterials to fabricate functional electronics has got growing attention for the new generation of environmentally friendly and biocompatible electronic devices. As a kind of biological material with rich source, proteins are essential natural component of all organisms. At the same time, artificial synaptic devices are of great significance for neuromorphic systems because they can emulate the signal process and memory behaviors of biological synapses. In this report, natural chicken albumen with high proton conductivity was used as the coupling electrolyte film for organic/inorganic hybrid synaptic devices fabrication. Some important synaptic functions including paired-pulse facilitation, dynamic filtering, short-term to long-term memory transition and spatial summation and shunting inhibition were successfully mimicked. Our results are very interesting for biological friendly artificial neuron networks and neuromorphic systems.

| S-EPMC4806348 | biostudies-other

Effect of Deposition Temperature on Zn Interstitials and Oxygen Vacancies in RF-Sputtered ZnO Thin Films and Thin Film-Transistors.

Project description:ZnO thin films were deposited using RF sputtering by varying the argon:oxygen gas flow rates and substrate temperatures. Structural, optical and electrical characterization of ZnO thin films were systematically carried out using X-Ray diffraction (XRD), scanning electron microscopy (SEM), UV-visible spectroscopy, X-Ray photoelectron spectroscopy (XPS) and Hall measurements. Film deposited at room temperature and annealed at 300 °C exhibited low O2 incorporation with localized defects and a high percentage of Zn interstitials. A large crystalline size and fewer grain boundaries resulted in a high Hall mobility of 46.09 cm2/V-s Deposition at higher substrate temperatures resulted in improvement in O2 incorporation through the annihilation of localized defects and decrease in oxygen vacancies and Zn interstitials. Urbach tails within the bandgap were identified using the absorption spectrum and compared with the % defects from XPS. Bottom-gate thin-film transistors were subsequently fabricated on a SiO2/p-Si substrate using the combination of RF sputtering, wet etching and photolithography. Variation in the substrate temperature showed performance enhancement in terms of the leakage current, threshold voltage, sub-threshold swing and ION/IOFF ratio. Thin-film transistor (TFT) devices deposited at 300 °C resulted in an O2-rich surface through chemisorption, which led to a reduction in the leakage current of up to 10-12 A and a 10-fold reduction in the sub-threshold swing (SS) from 30 V to 2.8 V. Further TFT optimization was carried out by reducing the ZnO thickness to 50 nm, which resulted in a field-effect mobility of 1.1 cm2/V-s and ION/IOFF ratio of 105.

| S-EPMC11547206 | biostudies-literature

Electric Field-aided Selective Activation for Indium-Gallium-Zinc-Oxide Thin Film Transistors.

Project description:A new technique is proposed for the activation of low temperature amorphous InGaZnO thin film transistor (a-IGZO TFT) backplanes through application of a bias voltage and annealing at 130 °C simultaneously. In this 'electrical activation', the effects of annealing under bias are selectively focused in the channel region. Therefore, electrical activation can be an effective method for lower backplane processing temperatures from 280 °C to 130 °C. Devices fabricated with this method exhibit equivalent electrical properties to those of conventionally-fabricated samples. These results are analyzed electrically and thermodynamically using infrared microthermography. Various bias voltages are applied to the gate, source, and drain electrodes while samples are annealed at 130 °C for 1 hour. Without conventional high temperature annealing or electrical activation, current-voltage curves do not show transfer characteristics. However, electrically activated a-IGZO TFTs show superior electrical characteristics, comparable to the reference TFTs annealed at 280 °C for 1 hour. This effect is a result of the lower activation energy, and efficient transfer of electrical and thermal energy to a-IGZO TFTs. With this approach, superior low-temperature a-IGZO TFTs are fabricated successfully.

| S-EPMC5057139 | biostudies-literature

Poly(3-hexylthiophene)-Based Organic Thin-Film Transistors with Virgin Graphene Oxide as an Interfacial Layer.

Project description:We fabricated and characterized poly(3-hexylthiophene-2, 5-diyl) (P3HT)-based Organic thin-film transistors (OTFTs) containing an interfacial layer made from virgin Graphene Oxide (GO). Previously chemically modified GO and reduced GO (RGO) were used to modify OTFT interfaces. However, to our knowledge, there are no published reports where virgin GO was employed for this purpose. For the sake of comparison, OTFTs without modification were also manufactured. The structure of the devices was based on the Bottom Gate Bottom Contact (BGBC) OTFT. We show that the presence of the GO monolayer on the surface of the OTFT's SiO2 dielectric and Au electrode surface noticeably improves their performance. Namely, the drain current and the field-effect mobility of OTFTs are considerably increased by modifying the interfaces with the virgin GO deposition. It is suggested that the observed enhancement is connected to a decrease in the contact resistance of GO-covered Au electrodes and the particular structure of the P3HT layer on the dielectric surface. Namely, we found a specific morphology of the organic semiconductor P3HT layer, where larger interconnecting polymer grains are formed on the surface of the GO-modified SiO2. It is proposed that this specific morphology is formed due to the increased mobility of the P3HT segments near the solid boundary, which was confirmed via Differential Scanning Calorimetry measurements.

| S-EPMC9736656 | biostudies-literature

Highly Transparent and Surface-Plasmon-Enhanced Visible-Photodetector Based on Zinc Oxide Thin-Film Transistors with Heterojunction Structure.

Project description:Highly transparent zinc oxide (ZnO)-based thin-film transistors (TFTs) with gold nanoparticles (AuNPs) capable of detecting visible light were fabricated through spray pyrolysis on a fluorine-doped tin oxide substrate. The spray-deposited channel layer of ZnO had a thickness of approximately 15 nm, and the thickness exhibited a linear increase with an increasing number of sprays. Furthermore, the ZnO thin-film exhibited a markedly smoother channel layer with a significantly lower surface roughness of 1.84 nm when the substrate was 20 cm from the spray nozzle compared with when it was 10 cm away. Finally, a ZnO and Au-NP heterojunction nanohybrid structure using plasmonic energy detection as an electrical signal, constitutes an ideal combination for a visible-light photodetector. The ZnO-based TFTs convert localized surface plasmon energy into an electrical signal, thereby extending the wide band-gap of materials used for photodetectors to achieve visible-light wavelength detection. The photo-transistors demonstrate an elevated on-current with an increase of the AuNP density in the concentration of 1.26, 12.6, and 126 pM and reach values of 3.75, 5.18, and 9.79 × 10-7 A with applied gate and drain voltages. Moreover, the threshold voltage (Vth) also drifts to negative values as the AuNP density increases.

| S-EPMC6862527 | biostudies-literature

Intrinsically stretchable and transparent thin-film transistors based on printable silver nanowires, carbon nanotubes and an elastomeric dielectric.

Project description:Thin-film field-effect transistor is a fundamental component behind various mordern electronics. The development of stretchable electronics poses fundamental challenges in developing new electronic materials for stretchable thin-film transistors that are mechanically compliant and solution processable. Here we report the fabrication of transparent thin-film transistors that behave like an elastomer film. The entire fabrication is carried out by solution-based techniques, and the resulting devices exhibit a mobility of ∼30 cm(2) V(-1) s(-1), on/off ratio of 10(3)-10(4), switching current >100 μA, transconductance >50 μS and relative low operating voltages. The devices can be stretched by up to 50% strain and subjected to 500 cycles of repeated stretching to 20% strain without significant loss in electrical property. The thin-film transistors are also used to drive organic light-emitting diodes. The approach and results represent an important progress toward the development of stretchable active-matrix displays.

| S-EPMC4518309 | biostudies-literature

Ultraviolet Photodetecting and Plasmon-to-Electric Conversion of Controlled Inkjet-Printing Thin-Film Transistors.

Project description:Direct ink-jet printing of a zinc-oxide-based thin-film transistor (ZnO-based TFT) with a three-dimensional (3-D) channel structure was demonstrated for ultraviolet light (UV) and visible light photodetection. Here, we demonstrated the channel structures by which temperature-induced Marangoni flow can be used to narrow the channel width from 318.9 ± 44.1 μm to 180.1 ± 13.9 μm via a temperature gradient. Furthermore, a simple and efficient oxygen plasma treatment was used to enhance the electrical characteristics of switching ION/IOFF ratio of approximately 105. Therefore, the stable and excellent gate bias-controlled photo-transistors were fabricated and characterized in detail for ultraviolet (UV) and visible light sensing. The photodetector exhibited a superior photoresponse with a significant increase of more than 2 orders of magnitude larger drain current generated upon UV illumination. The results could be useful for the development of UV photodetectors by the direct-patterning ink-jet printing technique. Additionally, we also have successfully demonstrated that a metal-semiconductor junction structure that enables plasmon energy detection by using the plasmonic effects is an efficient conversion of plasmon energy to an electrical signal. The device showed a significant variations negative shift of threshold voltage under different light power density with exposure of visible light. With the ZnO-based TFTs, only ultraviolet light detection extends to the visible light wavelength.

| S-EPMC7153598 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data