Friction-lowering capabilities and human subject preferences for a hydrophilic surface coating on latex substrates: implications for increasing condom usage.

ABSTRACT: Personal lubricants can increase user satisfaction with male condoms by reducing friction and yielding a slippery sensation. However, lubricants pose disadvantages of dilution in physiologic fluids and sloughing away over repeated articulations. To address these drawbacks, a latex surface modification, which becomes lubricious in the presence of physiologic fluid, has been developed and evaluated. This study assesses (i) the frictional performance of the lubricious coating compared to non-coated latex and latex lubricated by personal lubricant, (ii) the level of agreement between human-perceived slipperiness and machine-measured friction, and (iii) human preference for a hypothetical male condom containing the lubricious coating. Friction coefficient of the lubricious coating was 53% lower than that of non-coated latex and approximately equal to that afforded by personal lubricant. A touch test and survey of a small population sample (N = 33) revealed a strong correlation (R ² = 0.83) between human-perceived slipperiness and machine-measured friction. A majority of participants (73%) expressed a preference for a condom containing the lubricious coating, agreeing that an inherently slippery condom that remained slippery for a long duration would increase their condom usage. Such a coating shows potential to be an effective strategy for decreasing friction-associated pain, increasing user satisfaction and increasing condom usage.

SUBMITTER: Cooper BG

PROVIDER: S-EPMC6227966 | biostudies-literature | 2018 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Friction-lowering capabilities and human subject preferences for a hydrophilic surface coating on latex substrates: implications for increasing condom usage.

Cooper Benjamin G BG Chin Stacy L SL Xiao Ruiqing R Buch Karen K Kim Ducksoo D Grinstaff Mark W MW

Royal Society open science 20181017 10

Personal lubricants can increase user satisfaction with male condoms by reducing friction and yielding a slippery sensation. However, lubricants pose disadvantages of dilution in physiologic fluids and sloughing away over repeated articulations. To address these drawbacks, a latex surface modification, which becomes lubricious in the presence of physiologic fluid, has been developed and evaluated. This study assesses (i) the frictional performance of the lubricious coating compared to non-coated ...[more]

PMID: 30473805

Similar Datasets

Project description:Herein, we describe a one-step method for synthesizing cationic acrylate-based core-shell latex (CACS latex), which is used to prepare architectural coatings with excellent antimicrobial properties. Firstly, a polymerizable water-soluble quaternary ammonium salt (QAS-BN) was synthesized using 2-(Dimethylamine) ethyl methacrylate (DMAEMA) and benzyl bromide by the Hoffman alkylation reaction. Then QAS-BN, butyl acrylate (BA), methyl methacrylate (MMA), and vinyltriethoxysilane (VTES) as reactants and 2,2'-azobis(2-methylpropionamidine) dihydrochloride (AIBA) as a water-soluble initiator were used to synthesize the CACS latex. The effect of the QAS-BN dosage on the properties of the emulsion and latex film was systematically investigated. The TGA results showed that using QAS-BN reduced the latex film's initial degradation temperature but improved its thermal stability. In the transmission electron microscopy (TEM) photographs, the self-stratification of latex particles with a high dosage of QAS-BN was observed, forming a core-shell structure of latex particles. The DSC, TGA, XPS, SEM, and performance tests confirmed the core-shell structure of the latex particles. The relationship between the formation of the core-shell structure and the content of QAS-BN was proved. The formation of the core-shell structure was due to the preferential reaction of water-soluble monomers in the aqueous phase, which led to the aggregation of hydrophilic groups, resulting in the formation of soft-core and hard-shell latex particles. However, the water resistance of the films formed by CACS latex was greatly reduced. We introduced a p-chloromethyl styrene and n-hexane diamine (p-CMS/EDA) crosslinking system, effectively improving the water resistance in this study. Finally, the antimicrobial coating was prepared with a CACS emulsion of 7 wt.% QAS-BN and 2 wt.% p-CMS/EDA. The antibacterial activity rates of this antimicrobial coating against E. coli and S. aureus were 99.99%. The antiviral activity rates against H3N2, HCoV-229E, and EV71 were 99.4%, 99.2%, and 97.9%, respectively. This study provides a novel idea for the morphological design of latex particles. A new architectural coating with broad-spectrum antimicrobial properties was obtained, which has important public health and safety applications.

Dataset Information

Friction-lowering capabilities and human subject preferences for a hydrophilic surface coating on latex substrates: implications for increasing condom usage.

Publications

Friction-lowering capabilities and human subject preferences for a hydrophilic surface coating on latex substrates: implications for increasing condom usage.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets