Dibutyl Itaconate and Lauryl Methacrylate Copolymers by Emulsion Polymerization for Development of Sustainable Pressure-Sensitive Adhesives.

ABSTRACT: Renewable polymers possess the potential to replace monomers from petrochemical sources. The design and development of polymeric materials from sustainable materials are a technological challenge. The main objectives of this study were to study the microstructure of copolymers based on itaconic acid (IA), di-n-butyl itaconate (DBI), and lauryl methacrylate (LMA); and to explore and to evaluate these copolymers as pressure-sensitive adhesives (PSA). The copolymer synthesis was carried out through batch emulsion radical polymerization, an environmentally friendly process. IA was used in a small fixed amount as a functional comonomer, and LMA was selected due to low glass transition temperature (Tg). The structure of synthesized copolymers was studied by FTIR, 1H-NMR, Soxhlet extraction, and molecular weight analyses by GPC. Furthermore, the viscoelastic and thermal properties of copolymer films were characterized by DMA, DSC, and TGA. The single Tg displayed by the poly(DBI-LMA-IA) terpolymers indicates that statistical random composition copolymers were obtained. Moreover, FTIR and NMR spectra confirm the chemical structure and composition. It was found that a cross-linked microstructure and higher molecular weight are observed with an increase of LMA in the feed led. The Tg and modulus (G') of the copolymers film can be tuned with the ratio of DBI:LMA providing a platform for a wide range of applications as a biobased alternative to produce waterborne PSA.

SUBMITTER: Casas-Soto CR

PROVIDER: S-EPMC8840584 | biostudies-literature | 2022 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Dibutyl Itaconate and Lauryl Methacrylate Copolymers by Emulsion Polymerization for Development of Sustainable Pressure-Sensitive Adhesives.

Casas-Soto Carlos Rafael CR Conejo-Dávila Alain Salvador AS Osuna Velia V Chávez-Flores David D Espinoza-Hicks José Carlos JC Flores-Gallardo Sergio Gabriel SG Vega-Rios Alejandro A

Polymers 20220207 3

Renewable polymers possess the potential to replace monomers from petrochemical sources. The design and development of polymeric materials from sustainable materials are a technological challenge. The main objectives of this study were to study the microstructure of copolymers based on itaconic acid (IA), di-<i>n</i>-butyl itaconate (DBI), and lauryl methacrylate (LMA); and to explore and to evaluate these copolymers as pressure-sensitive adhesives (PSA). The copolymer synthesis was carried out ...[more]

PMID: 35160621

Similar Datasets

Project description:Recently, we reported time-resolved synchrotron small-angle X-ray scattering (TR-SAXS) studies during aqueous emulsion polymerization using a bespoke stirrable reaction cell (J. Am. Chem. Soc. 2021, 143, 1474-1484). This proof-of-concept study utilized a semifluorinated specialty monomer (2,2,2-trifluoroethyl methacrylate) to ensure high X-ray contrast relative to water. Herein, we extend this approach to emulsion polymerization of methyl methacrylate (MMA) in the presence or absence of sodium dodecyl sulfate (SDS) at 70 °C. Solution conductivity measurements for this anionic surfactant indicated a critical micelle concentration (CMC) of 10.9 mM at this temperature. Thus, SDS was employed at either 1.0 or 20.0 mM, which corresponds to well below or well above its CMC. Postmortem analysis by 1H NMR spectroscopy indicated MMA conversions of 93-95% for these three formulations. We demonstrate that the X-ray contrast between water and PMMA is sufficiently large to produce high-quality scattering patterns during TR-SAXS experiments. Such patterns were fitted using a hard-sphere scattering model to monitor the evolution in particle diameter. This enabled (i) determination of the time point for the onset of nucleation and (ii) the evolution in particle size to be monitored during the MMA polymerization. The final particle diameters obtained from such TR-SAXS studies were consistent with postmortem DLS analyses, while TEM studies confirmed that near-monodisperse latex particles were formed. Micellar nucleation occurs within just 2 min when the SDS concentration is well above its CMC, resulting in a high particle number concentration and relatively small latex particles. In contrast, when SDS is either absent or present below its CMC, particle nuclei are formed by homogeneous nucleation over significantly longer time scales (14-15 min). In the latter case, adsorption of SDS onto nascent particles reduces their coagulation, giving rise to a larger number of smaller particles compared to the surfactant-free polymerization. However, the characteristic time required for the onset of nucleation is barely affected because this is mainly controlled by the kinetics of homogeneous polymerization of the relatively water-soluble MMA monomer within the aqueous phase. These results suggest that the aqueous emulsion polymerization of several other (meth)acrylic monomers, and perhaps also vinyl acetate, may be amenable to TR-SAXS studies.

Project description:A series of poly(lauryl methacrylate)-poly(methyl methacrylate-stat-lauryl methacrylate) (PLMA x -P(MMA-stat-LMA) y ) diblock copolymer nanoparticles were synthesized via RAFT dispersion copolymerization of 90 mol % methyl methacrylate (MMA) with 10 mol % lauryl methacrylate (LMA) in mineral oil by using a poly(lauryl methacrylate) (PLMA) precursor with a mean degree of polymerization (DP) of either 22 or 41. In situ 1H NMR studies of the copolymerization kinetics suggested an overall comonomer conversion of 94% within 2.5 h. GPC analysis confirmed a relatively narrow molecular weight distribution (M w/M n ≤ 1.35) for each diblock copolymer. Recently, we reported an unexpected morphology constraint when targeting PLMA22-PMMA y nano-objects in mineral oil, with the formation of kinetically trapped spheres being attributed to the relatively high glass transition temperature (T g) of the PMMA block. Herein we demonstrate that this limitation can be overcome by (i) incorporating 10 mol % LMA into the core-forming block and (ii) performing such syntheses at 115 °C. This new strategy produced well-defined spheres, worms, or vesicles when using the same PLMA22 precursor. Introducing the LMA comonomer not only enhances the mobility of the core-forming copolymer chains by increasing their solvent plasticization but also reduces their effective glass transition temperature to well below the reaction temperature. Copolymer morphologies were initially assigned via transmission electron microscopy (TEM) studies and subsequently confirmed via small-angle X-ray scattering analysis. The thermoresponsive behavior of PLMA22-P(0.9MMA-stat-0.1LMA)113 worms and PLMA22-P(0.9MMA-stat-0.1LMA)228 vesicles was also studied by using dynamic light scattering (DLS) and TEM. The former copolymer underwent a worm-to-sphere transition on heating from 20 to 170 °C while a vesicle-to-worm transition was observed for the latter. Such thermal transitions were irreversible at 0.1% w/w solids but proved to be reversible at 20% w/w solids.

Dataset Information

Dibutyl Itaconate and Lauryl Methacrylate Copolymers by Emulsion Polymerization for Development of Sustainable Pressure-Sensitive Adhesives.

Publications

Dibutyl Itaconate and Lauryl Methacrylate Copolymers by Emulsion Polymerization for Development of Sustainable Pressure-Sensitive Adhesives.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets