Thermal degradation of defective high-surface-area UiO-66 in different gaseous environments.

ABSTRACT: UiO-66 is a versatile zirconium-based MOF, which is thermally stable up to 500 °C. In the present work, the thermal degradation of UiO-66 with a high number of defects has been studied in inert, oxidative and reductive environments. A sample of UiO-66 with a high BET surface area of 1827 m² g^-1 was prepared, which contains 2.3 missing linkers per hexa-zirconium node, as calculated by the thermogravimetric curve. The crystalline framework of this UiO-66 sample collapses at 250 °C, while thermal decomposition starts at 450 °C in the oxidative environment and at 500 °C in the reductive and inert environments. The BET surface area of the MOF is affected variably by heating under different gaseous conditions. Under inert conditions, porosity is maintained up to 711 m²