ABSTRACT: TiO₂ has been reported to have considerable capacity through appropriate surface modification. Previous studies of TiO₂-based supercapacitors mainly focused on anodized TiO₂ nanotubes and TiO₂ powder, even though the capacitance still lags behind that of carbon-base materials. In this work, a three-dimensional porous TiO₂/Ti (PTT) network was constructed by anodic oxidation and its capacitance was boosted by subsequent aluminum-reduction process. Activated Ti³⁺ was proved to be being successfully introduced into the surface of pristine PTT, resulting in the prominent enhancement of supercapacitive performance. An areal capacitance of 81.75 mF cm^-2 was achieved from Al-reduced PTT (Al-PTT) at 500 °C in 1 M H₂SO₄ electrolyte, which was among the highest value of pure TiO₂-based electrodes. Good electrochemical stability was also confirmed by the 3.12% loss of the highest capacity after 5000 CV cycles. More importantly, the activated Ti³⁺/Ti⁴⁺ redox couple in modified TiO₂ is solidly confirmed by being directly observed in CV curves. The capacitive mechanism of the redox reaction is also studied by electrochemical tests. The construction of a 3D porous network structure and efficient Ti³⁺ introduction provide an effective method to boost the supercapacitive performance of TiO₂-based materials for energy storage applications.

SUBMITTER: Wang Q

PROVIDER: S-EPMC9061586 | biostudies-literature | 2019 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Supercapacitive performance of TiO2 boosted by a unique porous TiO2/Ti network and activated Ti3.

Wang Qi Q Li Musen M Wang Zhou Z

RSC advances 20190308 14

TiO2 has been reported to have considerable capacity through appropriate surface modification. Previous studies of TiO2-based supercapacitors mainly focused on anodized TiO2 nanotubes and TiO2 powder, even though the capacitance still lags behind that of carbon-base materials. In this work, a three-dimensional porous TiO2/Ti (PTT) network was constructed by anodic oxidation and its capacitance was boosted by subsequent aluminum-reduction pro ...[more]

PMID: 35521169

Similar Datasets

Project description:Photocatalyst is the core of photocatalysis and directly determines photocatalytic performance. However, low quantum efficiency and low utilization of solar energy are important technical problems in the application of photocatalysis. In this work, a series of polyoxometalates (POMs) [H3PW12O40] (PW12)-doped titanium dioxide (TiO2) nanofibers modified with various amount of silver (Ag) nanoparticles (NPs) were prepared by utilizing electrospinning/photoreduction strategy, and were labelled as x wt% Ag/PW12/TiO2 (abbr. x% Ag/PT, x = 5, 10, and 15, respectively). The as-prepared materials were characterized with a series of techniques and exhibited remarkable catalytic activities for visible-light degradation tetracycline (TC), enrofloxacin (ENR), and methyl orange (MO). Particularly, the 10% Ag/PT catalyst with a specific surface area of 155.09 m2/g and an average aperture of 4.61 nm possessed the optimal photodegradation performance, with efficiencies reaching 78.19% for TC, 93.65% for ENR, and 99.29% for MO, which were significantly higher than those of PW12-free Ag/TiO2 and PT nanofibers. Additionally, various parameters (the pH of the solution, catalyst usage, and TC concentration) influencing the degradation process were investigated in detail. The optimal conditions are as follows: catalyst usage: 20 mg; TC: 20 mL of 20 ppm; pH = 7. Furthermore, the photodegradation intermediates and pathways were demonstrated by HPLC-MS measurement. We also investigated the toxicity of products generated during TC removal by employing quantitative structure-activity relationship (QSAR) prediction through a toxicity estimation software tool (T.E.S.T. Version 5.1.2.). The mechanism study showed that the doping of PW12 and the modification of Ag NPs on TiO2 broadened the visible-light absorption, accelerating the effective separation of photogenerated carriers, therefore resulting in an enhanced photocatalytic performance. The research provided some new thoughts for exploiting efficient and durable photocatalysts for environmental remediation.

Dataset Information

Supercapacitive performance of TiO₂ boosted by a unique porous TiO₂/Ti network and activated Ti³.

Publications

Supercapacitive performance of TiO<sub>2</sub> boosted by a unique porous TiO<sub>2</sub>/Ti network and activated Ti<sup>3</sup>.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets