Enhanced mechanical properties of hBN-ZrO₂ composites and their biological activities on Drosophila melanogaster: synthesis and characterization.

ABSTRACT: In this study, six compositions in the system [x(h-BN)-(100 - x)ZrO₂] (10 ≤ x ≤ 90) were synthesized by a bottom up approach, i.e., the solid-state reaction technique. XRD results showed the formation of a novel and main phase of zirconium oxynitrate ZrO(NO₃)₂ and SEM exhibited mixed morphology of layered and stacked h-BN nanosheets with ZrO₂ grains. The composite sample 10 wt% h-BN + 90 wt% ZrO₂ (10B90Z) showed outstanding mechanical properties for different parameters, i.e., density (3.12 g cm^-3), Young's modulus (10.10 GPa), toughness (2.56 MJ m^-3), and maximum mechanical strength (227.33 MPa). The current study further checked the in vivo toxicity of composite 10B90Z and composite 90B10Z using Drosophila melanogaster. The composite 10B90Z showed less cytotoxicity in this model, while the composite 90B10Z showed higher toxicity in terms of organ development as well as internal damage of the gut mostly at the lower concentrations of 1, 10, and 25 μg mL^-1. Altogether, the current study proposes the composite 10B90Z as an ideal compound for applications in biomedical research. This composite 10B90Z displays remarkable mechanical and biological performances, due to which we recommend this composition for various biomedical applications.

SUBMITTER: Gautam A

PROVIDER: S-EPMC9076398 | biostudies-literature | 2019 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Enhanced mechanical properties of hBN-ZrO2 composites and their biological activities on Drosophila melanogaster: synthesis and characterization.

Gautam Amarendra A Gautam Chandkiram C Mishra Monalisa M Mishra Vijay Kumar VK Hussain Ajaz A Sahu Swetapadma S Nanda Reetuparna R Kisan Bikash B Biradar Santoshkumar S Gautam Rakesh Kumar RK

RSC advances 20191211 70

In this study, six compositions in the system [x(h-BN)-(100 - x)ZrO2] (10 ≤ x ≤ 90) were synthesized by a bottom up approach, i.e., the solid-state reaction technique. XRD results showed the formation of a novel and main phase of zirconium oxynitrate ZrO(NO3)2 and SEM exhibited mixed morphology of layered and stacked h-BN nanosheets with ZrO2 grains. The composite sample 10 wt% h-BN + 90 wt% ZrO2 (10B90Z) showed o ...[more]

PMID: 35540076

Similar Datasets

Project description:The breakdown of the polymeric component of contemporary composite dental restorative materials compromises their longevity, while leachable compounds from these materials have cellular consequences. Thus, a new generation of composite materials needed to be designed to have a longer service life and ensure that any leachable compounds are not harmful to appropriate cell lines. To accomplish this, we have developed concurrent thiol-ene-based polymerization and allyl sulfide-based addition-fragmentation chain transfer chemistries to afford cross-linked polymeric resins that demonstrate low shrinkage and low shrinkage stress. In the past, the filler used in dental composites mainly consisted of glass, which is biologically inert. In several of our prototype composites, we introduced fluorapatite (FA) crystals, which resemble enamel crystals and are bioactive. These novel prototype composites were benchmarked against similarly filled methacrylate-based bisphenol A diglycidyl ether dimethacrylate / triethylene glycol dimethacrylate (bisGMA/TEGDMA) composite for their cytotoxicity, mechanical properties, biofilm formation, and fluoride release. The leachables at pH 7 from all the composites were nontoxic to dental pulp stem cells. There was a trend toward an increase in total toughness of the glass-only-filled prototype composites as compared with the similarly filled bisGMA/TEGDMA composite. Other mechanical properties of the glass-only-filled prototype composites were comparable to the similarly filled bisGMA/TEGDMA composite. Incorporation of the FA reduced the mechanical properties of the prototype and bisGMA/TEGDMA composite. Biofilm mass and colony-forming units per milliliter were reduced on the glass-only-filled prototype composites as compared with the glass-only-filled bisGMA/TEGDMA composite and were significantly reduced by the addition of FA to all composites. Fluoride release at pH 7 was greatest after 24 h for the bisGMA/TEGDMA glass + FA composite as compared with the similarly filled prototypes, but overall the F- release was marginal and not at a concentration to affect bacterial metabolism.

Dataset Information

Enhanced mechanical properties of hBN-ZrO₂ composites and their biological activities on Drosophila melanogaster: synthesis and characterization.

Publications

Enhanced mechanical properties of hBN-ZrO<sub>2</sub> composites and their biological activities on <i>Drosophila melanogaster</i>: synthesis and characterization.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets