Fused Filament Fabrication of a Dynamically Crosslinked Network Derived from Commodity Thermoplastics
Ontology highlight
ABSTRACT:
SUBMITTER: Prasanna Kar G
PROVIDER: S-EPMC9194902 | biostudies-literature | 2022 May
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:In this work, aligned discontinuous fibre composite (ADFRC) tapes were developed and investigated as precursors for a novel 3D printing filament. ADFRCs have the potential to achieve mechanical performance comparable to continuous fibre reinforced composites, given sufficient fibre length and high level of alignment, and avoid many of the manufacturing difficulties associated with continuous fibres, e.g., wrinkling, bridging and corner radii constraints. Their potential use for fused filament fabrication (FFF) techniques was investigated here. An extensive down-selection process of thermoplastic matrices was performed, as matrix properties significantly impact both the processing and performance of the filament. This resulted in four candidate polymers (ABS, PLA, Nylon, PETG) which were used to manufacture ADFRC tapes with a Vf of 12.5% using the high performance discontinuous fibre (HiPerDiF) technology and an in-house developed continuous consolidation module. Tensile stiffness and strength up to 30 GPa and 400 MPa respectively were recorded, showing that a discontinuous fibre filament has the potential to compete with continuous fibre filaments.
| S-EPMC7594080 | biostudies-literature
Project description:Thermoplastic parts manufactured via fused filament fabrication (FFF) have limited strength and toughness compared to other types of polymer additive and subtractive manufacturing. Low strength results from poor interlayer adhesion, making FFF parts not suitable for most engineering applications. Post processing solutions, such as annealing, enable healing of these interlayers, thus approaching injection molded parts. Prior work demonstrated a core-shell polycarbonate (PC)-acrylonitrile butadiene styrene (ABS) structured dual material filament to provide thermo-structural stability during annealing of the ABS component; however, annealing was limited to relatively low temperatures (135 °C) and required long annealing times (72 h). In the current work, a PC copolymer with a higher glass transition temperature (173 °C) than conventional PC is processed along with an extrusion-grade ABS into a PC-ABS core-shell filament. This improved dual material filament was printed, annealed, and evaluated via Izod impact testing, ultimately yielding 83% of bulk annealed ABS z-direction strength at an accelerated annealing time (8 h) and higher annealing temperature (155-175 °C). A demonstration part is printed with the dual material filament and annealed at 155 °C for 8 h, resulting in excellent dimensional accuracy, and a ductile failure at 73% higher ultimate load compared to the brittle failure of an as-printed part. This work highlights that material selection and design of a bicomponent filament geometry can lead to parts printed with FFF, with increased strength compared to other post-processing techniques at reduced processing times.
| S-EPMC10439886 | biostudies-literature
Project description:In addition to possessing the desirable properties of being a biodegradable and biocompatible polymer fabricated from renewable resources, poly (lactic acid) (PLA) has useful mechanical and thermal attributes that has enabled it to be one of the most widely-used plastics for medicine, manufacturing, and agriculture. Yet, PLA composites have not been heavily explored for use in 3D-printing applications, and the range of feasible materials for the technology is limited, which inhibits its potential growth and industry adoption. In this study, tunable, multifunctional antimicrobial PLA composite filaments for 3D-printing have been fabricated and tested via chemical, thermal, mechanical, and antimicrobial experiments. Thermally stable antimicrobial ceramics, ZnO and TiO2, were used as fillers up to 30 wt%, and poly (ethylene glycol) (PEG) was used as a plasticizer to tune the physical material properties. Results demonstrate that the PLA composite filaments exhibit the thermal phase behaviors and thermal stability suitable for 3D-printing. Additionally, PEG can be used to tune the mechanical properties while not affecting the antimicrobial efficacy that ZnO and TiO2 imbue.
| S-EPMC7918987 | biostudies-literature
Project description:The uptake of microfluidics by the wider scientific community has been limited by the fabrication barrier created by the skills and equipment required for the production of traditional microfluidic devices. Here we present simple 3D printed microfluidic devices using an inexpensive and readily accessible printer with commercially available printer materials. We demonstrate that previously reported limitations of transparency and fidelity have been overcome, whilst devices capable of operating at pressures in excess of 2000 kPa illustrate that leakage issues have also been resolved. The utility of the 3D printed microfluidic devices is illustrated by encapsulating dental pulp stem cells within alginate droplets; cell viability assays show the vast majority of cells remain live, and device transparency is sufficient for single cell imaging. The accessibility of these devices is further enhanced through fabrication of integrated ports and by the introduction of a Lego®-like modular system facilitating rapid prototyping whilst offering the potential for novices to build microfluidic systems from a database of microfluidic components.
| S-EPMC4822857 | biostudies-literature
Project description:In this paper, the fatigue response of fused filament fabrication (FFF) Acrylonitrile butadiene styrene (ABS) parts is studied. Different building parameters (layer height, nozzle diameter, infill density, and printing speed) were chosen to study their influence on the lifespan of cylindrical specimens according to a design of experiments (DOE) using the Taguchi methodology. The same DOE was applied on two different specimen sets using two different infill patterns-rectilinear and honeycomb. The results show that the infill density is the most important parameter for both of the studied patterns. The specimens manufactured with the honeycomb pattern show longer lifespans. The best parameter set associated to that infill was chosen for a second experimental phase, in which the specimens were tested under different maximum bending stresses so as to construct the Wöhler curve associated with this 3D printing configuration. The results of this study are useful to design and manufacture ABS end-use parts that are expected to work under oscillating periodic loads.
| S-EPMC6317007 | biostudies-other
Project description:In this paper, a series of polymer composites made from acrylonitrile-styrene-acrylate (ASA) and poly (ether ether ketone) (PEEK) were manufactured. ASA acts as a polymer matrix while PEEK is loaded in the form of micro-particles that act as a reinforcing filler. The composites were compounded by single screw extrusion and then, different specimens were manufactured either via injection moulding (IM) or fused filament fabrication (FFF). Two different types of PEEK (commercial and reused) in different concentrations (3 and 6 wt.%) were tested and their influence in the mechanical, structural, and thermal properties were studied. It was observed that reused PEEK enhanced the stiffness and tensile strength and thermal stability of the composites both, for injected and printed specimens. This evidences the suitability of these composites as potential candidates as novel materials with enhanced properties following an approach of circular economy.
| S-EPMC8838854 | biostudies-literature
Project description:This article analyzes temperature fields and their variations in fused filament fabrication (FFF) from the filament entering the hot-end to the printed parts, aiming at a deeper understanding of the thermal process of this additive manufacturing technology. A standard E3D print head assembly was mounted on a robot arm for printing. A stable filament feeding region was determined with an upper limit in the volume flow rate at different nozzle temperatures. Within the limit, the steady-state temperature fields inside the hot-end were studied by a computational fluid dynamics model. Simulations indicated that the temperature became less homogeneous at higher flow rates, leading to a lower extrudate temperature at the nozzle outlet. These outlet temperatures were analyzed, validated, and used as input to simulate temperature variations in printed parts with a self-developed open-access numerical model. An interlayer time similarity rule was found in printing single-walled geometries, which specifies temperature similarities at the same interlayer time. The findings provide new insights into FFF processes, pointing out opportunities for improved production efficiency and scalability to large-scale manufacturing.
| S-EPMC9831539 | biostudies-literature
Project description:Tough adhesives provide resistance against high debonding forces, and these adhesives are difficult to design because of the simultaneous requirement of strength and ductility. Here, we report a design of tough reversible/recyclable adhesive materials enabled by incorporating dynamic covalent bonds of boronic ester into commodity triblock thermoplastic elastomers that reversibly bind with various fillers and substrates. The spectroscopic measurements and density functional theory calculations unveil versatile dynamic covalent binding of boronic ester with various hydroxy-terminated surfaces such as silica nanoparticles, aluminum, steel, and glass. The designed multiphase material exhibits exceptionally high adhesion strength and work of debonding with a rebonding capability, as well as outstanding mechanical, thermal, and chemical resistance properties. Bonding and debonding at the interfaces dictate hybrid material properties, and this revelation of tailored dynamic interactions with multiple interfaces will open up a new design of adhesives and hybrid materials.
| S-EPMC8519568 | biostudies-literature
Project description:This paper reports a comparison between the advantages and disadvantages of fused filament fabrication (FFF) and computer numerical control (CNC) milling, when applied to a specific case of conservation of cultural heritage: the reproduction of four missing columns of a 17th-century tabernacle. To make the replica prototypes, European pine wood (the original material) was used for CNC milling, while polyethylene terephthalate glycol (PETG) was used for FFF printing. Neat materials were chemically and structurally characterized (FTIR, XRD, DSC, contact angle measurement, colorimetry, and bending tests) before and after artificial aging, in order to study their durability. The comparison showed that although both materials are subject to a decrease in crystallinity (an increase in amorphous bands in XRD diffractograms) and mechanical performance with aging, these characteristics are less evident in PETG (E = 1.13 ± 0.01 GPa and σ = 60.20 ± 2.11 MPa after aging), which retains water repellent (ca = 95.96 ± 5.56°) and colorimetric (∆E = 2.6) properties. Furthermore, the increase in flexural strain (%) in pine wood, from 3.71 ± 0.03% to 4.11 ± 0.02%, makes it not suitable for purpose. Both techniques were then used to produce the same column, showing that for this specific application CNC milling is quicker than FFF, but, at the same time, it is also much more expensive and produces a huge amount of waste material compared to FFF printing. Based on these results, it was assessed that FFF is more suitable for the replication of the specific column. For this reason, only the 3D-printed PETG column was used for the subsequent conservative restoration.
| S-EPMC10141658 | biostudies-literature
Project description:In this work, we present a series of nanocomposites for Fused filament fabrication (FFF) based on polycaprolactone (PCL) and chitin nanocrystals (ChNCs). The ChNCs were synthesized by acid hydrolysis using HCl or lactic acid (LA). The approach using LA, an organic acid, makes the ChNCs synthesis more sustainable and modifies their surface with lactate groups, increasing their compatibility with the PCL matrix. The ChNCs characterization by X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy, and transmission electron microscopy revealed that both ChNCs presented similar morphologies and crystallinity, while differential scanning calorimetry and thermogravimetric analysis proved that they can bear temperatures up to 210 °C without degrading, which allows their processing in the manufacturing of PCL composites by twin-screw extrusion. Therefore, PCL composites in the form of filaments containing 0.5-1.0 wt % ChNCs were produced and used as feedstock in FFF, and standard tensile and flexural specimens were printed at different temperatures, up to 170 °C, to assess the influence of the ChNCs in the mechanical properties of the material. The tensile testing results showed that the presence of ChNCs enhances the strength and ductility of the PCL matrix, increasing the elongation at break around 20-50%. Moreover, the vertically printed flexural specimens showed a very different bending behavior, such that the pure PCL specimens presented a brittle fracture at 7% strain, while the ChNCs composites were able to bend over themselves. Hence, this work proves that the presence of ChNCs aims to improve the interlayer adhesion of the objects manufactured by FFF due to their good adhesive properties, which is currently a concern for the scientific community and the industrial sector.
| S-EPMC11247426 | biostudies-literature