In vitro physicochemical characterization of five root canal sealers and their influence on an ex vivo oral multi-species biofilm community.

ABSTRACT:

Aim

To evaluate the physicochemical properties of five root canal sealers and assess their effect on an ex vivo dental plaque-derived polymicrobial community.

Methodology

Dental plaque-derived microbial communities were exposed to the sealers (AH Plus [AHP], GuttaFlow Bioseal [GFB], Endoseal MTA [ESM], Bio-C sealer [BCS] and BioRoot RCS [BRR]) for 3, 6 and 18 h. The sealers' effect on the biofilm biomass and metabolic activity was quantified using crystal violet (CV) staining and MTT assay, respectively. Biofilm community composition and morphology were assessed by denaturing gradient gel electrophoresis (DGGE), 16S rRNA sequencing and scanning electron microscopy. The ISO6876:2012 specifications were followed to determine the setting time, radiopacity, flowability and solubility. Obturated acrylic teeth were used to assess the sealers' effect on pH. Surface chemical characterization was performed using SEM with coupled energy-dispersive spectroscopy. Data normality was assessed using the Shapiro-Wilk test. One-way anova and Tukey's tests were used to analyze data from setting time, radiopacity, flowability and solubility. Two-way anova and Dunnett's tests were used for the data analysis from CV, MTT and pH. 16S rRNA sequencing data were analyzed for alpha (Shannon index and Chao analysis) and beta diversity (Bray-Curtis dissimilarities). Differences in community composition were evaluated by analysis of similarity (p < .05).

Results

The sealers significantly influenced microbial community composition and morphology. All sealers complied with ISO6876:2012 requirements for setting time, radiopacity and flowability. Although only AHP effectively reduced the biofilm biomass, all sealers, except BRR, reduced biofilm metabolic activity.

Conclusion

Despite adequate physical properties, none of the sealers tested prevented biofilm growth. Significant changes in community composition were observed. If observed in vivo, these changes could affect intracanal microbial survival, pathogenicity and treatment outcomes.

SUBMITTER: Saavedra FM

PROVIDER: S-EPMC9321831 | biostudies-literature | 2022 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

In vitro physicochemical characterization of five root canal sealers and their influence on an ex vivo oral multi-species biofilm community.

Saavedra Flavia M FM Pelepenko Lauter E LE Boyle William S WS Zhang Anqi A Staley Christopher C Herzberg Mark C MC Marciano Marina A MA Lima Bruno P BP

International endodontic journal 20220415 7

<h4>Aim</h4>To evaluate the physicochemical properties of five root canal sealers and assess their effect on an ex vivo dental plaque-derived polymicrobial community.<h4>Methodology</h4>Dental plaque-derived microbial communities were exposed to the sealers (AH Plus [AHP], GuttaFlow Bioseal [GFB], Endoseal MTA [ESM], Bio-C sealer [BCS] and BioRoot RCS [BRR]) for 3, 6 and 18 h. The sealers' effect on the biofilm biomass and metabolic activity was quantified using crystal violet (CV) staining and ...[more]

PMID: 35383959

Similar Datasets

Project description:The aim of the study was to analyze the chemical-physical properties and bioactivity (apatite-forming ability) of three recently introduced premixed bioceramic root canal sealers containing varied amounts of different calcium silicates (CaSi): a dicalcium and tricalcium silicate (1-10% and 20-30%)-containing sealer with zirconium dioxide and tricalcium aluminate (CERASEAL); a tricalcium silicate (5-15%)-containing sealer with zirconium dioxide, dimethyl sulfoxide and lithium carbonate (AH PLUS BIOCERAMIC) and a dicalcium and tricalcium silicate (10% and 25%)-containing sealer with calcium aluminate, tricalcium aluminate and tantalite (NEOSEALER FLO). An epoxy resin-based sealer (AH PLUS) was used as control. The initial and final setting times, radiopacity, flowability, film thickness, open pore volume, water absorption, solubility, calcium release and alkalizing activity were tested. The nucleation of calcium phosphates and/or apatite after 28 days aging in Hanks balanced salt solution (HBSS) was evaluated by ESEM-EDX, vibrational IR and micro-Raman spectroscopy. The analyses showed for NeoSealer Flo and AH Plus the longest final setting times (1344 ± 60 and 1300 ± 60 min, respectively), while shorter times for AH Plus Bioceramic and Ceraseal (660 ± 60 and 720 ± 60 min, respectively). Radiopacity, flowability and film thickness complied with ISO 6876/12 for all tested materials. A significantly higher open pore volume was observed for NeoSealer Flo, AH Plus Bioceramic and Ceraseal when compared to AH Plus (p < 0.05), significantly higher values were observed for NeoSealer Flo and AH Plus Bioceramic (p < 0.05). Ceraseal and AH Plus revealed the lowest solubility. All CaSi-containing sealers released calcium and alkalized the soaking water. After 28 days immersion in HBSS, ESEM-EDX analyses revealed the formation of a mineral layer that covered the surface of all bioceramic sealers, with a lower detection of radiopacifiers (Zirconium for Ceraseal and AH Plus Bioceramic, Tantalum for NeoSealer Flo) and an increase in calcium, phosphorous and carbon. The calcium phosphate (CaP) layer was more evident on NeoSealer Flo and AH Plus Bioceramic. IR and micro-Raman revealed the formation of calcium carbonate on the surface of all set materials. A thin layer of a CaP phase was detected only on AH Plus Bioceramic and NeoSealer Flo. Ceraseal did not show CaP deposit despite its highest calcium release among all the tested CaSi-containing sealers. In conclusion, CaSi-containing sealers met the required chemical and physical standards and released biologically relevant ions. Slight/limited apatite nucleation was observed in relation to the high carbonation processes.

Project description:BackgroundOnce the chemo-mechanical preparation of root canals is finished, achieving a complete seal of the root canal system becomes crucial in determining the long-term success of endodontic treatment. The important goals of root canal obturation are to minimize leakage and achieve an adequate seal. Thus, a material that possesses satisfactory mechanical characteristics, is biocompatible, and has the ability to penetrate the dentine tubules adequately is needed.AimThis study aimed to compare the penetrability and bond strength between two calcium silicate-based sealers and an epoxy resin-based sealer, as well as examine the relationship between penetrability and bond strength for the different sealers.Method and materialsThirty-nine recently extracted single-rooted human premolar teeth were instrumented and divided evenly into three groups (n = 13), according to the sealer used for obturation: AH Plus Jet, EndoSequence, and AH Plus Bioceramic Sealer. Three teeth (30 slices) were randomly selected out of each for analysis using confocal laser scanning microscopy to assess penetrability. The remaining ten teeth (90 slices) in each group were subject to push-out tests using a universal testing machine. All teeth were sectioned into nine transverse slices of 0.9 mm thickness for their respective tests (apical, middle, coronal).ResultsAH Plus Jet exhibited significantly lower penetrability and significantly higher bond strength compared to EndoSequence BC sealer (p = 0.002) and AH Plus Bioceramic Sealer (p = 0.006). There was no significant difference between EndoSequence BC sealer and AH Plus Bioceramic Sealer in terms of either penetrability or bond strength. No correlation was found between penetrability and bond strength.ConclusionsWithin the limitation of this study and regardless of the location in the canal, the bioceramic based root canal sealers appeared to perform better than the epoxy resin-based sealer in terms of dentinal penetration rate. Further studies are required to compare other biomechanical properties of bioceramic sealers including setting characteristics and bacterial leakage.

Dataset Information

In vitro physicochemical characterization of five root canal sealers and their influence on an ex vivo oral multi-species biofilm community.

Aim

Methodology

Results

Conclusion

Publications

In vitro physicochemical characterization of five root canal sealers and their influence on an ex vivo oral multi-species biofilm community.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets