Catalytic behavior of a ZnO/TiO₂ composite in the synthesis of polycarbonate diol.

ABSTRACT: ZnO/TiO₂ catalysts with different ZnO contents have been prepared through equal volume impregnation method, characterized by XRD, SEM, Py-IR, ICP, XPS, NH₃-TPD and N₂ adsorption/desorption, and evaluated in the synthesis of polycarbonate diol (PCDL) through transesterification. The results showed that titanium zinc oxide formed in these catalysts, and the content of acidic sites varied with the ZnO content, and ZnO/TiO₂ (10%) has the highest acid amount. The ZnO/TiO₂ (20%) with medium acidic sites showed the highest catalytic activity. The synthesis process of polycarbonate glycol was also optimized. Under the optimal reaction conditions, the yield of PCDL was 72.5%, and the M _n reached 4829 g mol^-1 with a PDI of 1.6.

SUBMITTER: Chong R

PROVIDER: S-EPMC9903354 | biostudies-literature | 2023 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Catalytic behavior of a ZnO/TiO2 composite in the synthesis of polycarbonate diol.

Chong Ran R Qian Fei F Sun Zhong-Hua ZH Wei Mei-Jun MJ Zhou Wei-You WY Zhang Jing J He Ming-Yang MY Chen Qun Q Qian Jun-Feng JF

RSC advances 20230207 8

ZnO/TiO2 catalysts with different ZnO contents have been prepared through equal volume impregnation method, characterized by XRD, SEM, Py-IR, ICP, XPS, NH3-TPD and N2 adsorption/desorption, and evaluated in the synthesis of polycarbonate diol (PCDL) through transesterification. The results showed that titanium zinc oxide formed in these catalysts, and the content of acidic sites varied with the ZnO content, and ZnO/TiO2 (10%) has the highest acid amoun ...[more]

PMID: 36762090

Similar Datasets

Temperature-Sensitive Template for Preparation of ZnO/CeO2 Composite Photocatalytic Materials and Its Catalytic Performance.

Project description:In this work, a series of thermosensitive ionic liquid functionalized polymers, PNx(IL)y, with controllable morphology and particle size were prepared by free radical polymerization. Then, using the polymer PN64(IL)8 with uniform morphology as a templating agent, the ZnO composite photocatalytic materials doped with rare earth metal Ce were prepared in combination with a microwave-assisted and templated hydrothermal reaction method. Series different Ce-doping amount photocatalytic materials ZnO-Ce-x‱ were characterized by XRD, SEM, TEM, XPS, and other methods. The results demonstrated that the templated materials PN64(IL)8 can prepare ZnO-Ce-2‱ with uniform petaloid ambulacra shape, good distribution of elements, and excellent photocatalytic performance. Photocatalytic degradation experiments of methyl orange (MO) showed that when the Ce-doping amount is only 2‱, the degradation rate of organic dyes can reach 96.5% by reacting the photocatalytic materials in water for 1 h. In addition, this kind of photocatalyst can be used for the degradation of high-concentration MO, as well as being easily recovered and effectively reused by simple filtration. Therefore, the structure of this kind of photocatalyst is controllable in the preparation process with an extremely low Ce-doping amount compared with current reports, and it has a good application prospect in the field of wastewater treatment technology.

| S-EPMC11313708 | biostudies-literature

Stimulated generation of photobiogas by morphologically tuned nanostructured ZnO and ZnO/TiO2.

Project description:The photocatalytic degradation (PCD) of ethanol in an inert atmosphere on catalysis was explored in a lab-scale experiment. A morphologically tuned nanostructured controlled ZnO and ZnO/TiO2 nanocomposites were synthesized using a simple hydrothermal process under the control of several functionally capping agents marking a milestone in photocatalysis. It is possible that this could be modified to produce photobiogas out of organic dye pollution. The photocatalysts were characterized by the use of X-ray diffraction (XRD), transmission electron microscopy (TEM), Brunauer, Emmett, and Teller (BET) surface area analyzer, Scanning electron microscope (SEM-EDX), and UV-Vis absorption spectroscopy. The photocatalytic activity of the ZnO and ZnO-TiO2 composite nanostructures was evaluated for the photodegradation of the Tartrazine (Tr) dye aqueous solution. Where the composite matrix exhibits higher photocatalytic activity than pure ZnO nanomaterials as a result of the synergistic interaction between ZnO and TiO2 particles. This is mainly due to its higher surface area than pure ZnO. Moreover, the photocatalytic activity of the tuned nanostructured materials is found to be enhanced by the effect of the capping agent and controlling the morphology. This increase is accompanied by a significant shift in surface shape and band gap energy. According to the findings, the designed morphologies of pure ZnO photocatalyst impacted the formation of photobiogas from the photocatalytic decomposition of ethanol as a model of organic pollutants in wastewater. However, when using composite ZnO/TiO2 photocatalysts, the rate of CH4 formation is significantly lower than when using ZnO photocatalysts alone. This may be attributed to the synergetic effect between ZnO and TiO2 particles which leads to a remarkable reduction in the newly formed band gap energy. This may result in a fast rate of recombination between the photogenerated charge carriers (e- and h+).

| S-EPMC9531480 | biostudies-literature

Synthesis, characterization and photocatalytic properties of nanostructured lanthanide doped β-NaYF4/TiO2 composite films.

Project description:The photocatalytic approach is known to be one of the most promising advanced oxidation processes for the tertiary treatment of polluted water. In this paper, β-NaYF4/TiO2 composite films have been synthetized through a novel sol-gel/spin-coating approach using a mixture of β-diketonate complexes of Na and Y, and Yb3+, Tm3+, Gd3+, Eu3+ as doping ions, together with the TiO2 P25 nanoparticles. The herein pioneering approach represents an easy, straightforward and industrially appealing method for the fabrication of doped β-NaYF4/TiO2 composites. The effect of the doped β-NaYF4 phase on the photocatalytic activity of TiO2 for the degradation of methylene blue (MB) has been deeply investigated. In particular, the upconverting TiO2/β-NaYF4: 20%Yb, 2% Gd, x% Tm (x = 0.5 and 1%) and the downshifting TiO2/β-NaYF4: 10% Eu composite films have been tested on MB degradation both under UV and visible light irradiation. An improvement up to 42.4% in the degradation of MB has been observed for the TiO2/β-NaYF4: 10% Eu system after 240 min of UV irradiation.

| S-EPMC9374679 | biostudies-literature

Hydrothermal synthesis of novel 1-aminoperylene diimide/TiO2/MoS2 composite with enhanced photocatalytic activity.

Project description:1-aminoperylene diimide/TiO2/MoS2 composite (NH2-PDI/TiO2/MoS2) with ordered structure was prepared by hydrothermal synthesis method. The composite was characterized by XRD, SEM, FTIR, XPS, BET, DRS, PL, EIS, Raman, photocurrent, and Mott-Schottky plots spectroscopy. The potential positions of the conduction and valence bands, and the band gap energy of the semiconductors were estimated. The composite exhibited higher photocatalytic activity compared with the mono-component systems. The apparent rate constants (k) were determined as 0.00616, 0.00352, 0.00738, 0.00517, 0.00752, and 0.00806 min-1 for TiO2, NH2-PDI, NH2-PDI/TiO2, MoS2, MoS2/TiO2, and NH2-PDI/TiO2/MoS2, respectively. The detection of radical scavengers confirmed that superoxide radicals, photogenerated holes, and photogenerated electrons were the main active substances for MB degradation. Between type II- heterojunction mechanism and Z-scheme mechanism, the latter could explain the enhanced photocatalytic activity of the composite better. The Z-scheme mechanism accumulates more electrons at CB level of NH2-PDI and hence generates more super oxide radicals.

| S-EPMC7738548 | biostudies-literature

Synthesis and Catalytic Performance of Bimetallic Oxide-Derived CuO-ZnO Electrocatalysts for CO2 Reduction.

Project description:Steering the selectivity of electrocatalysts toward the desired product is crucial in the electrochemical reduction of CO2. A promising approach is the electronic modification of the catalyst's active phase. In this work, we report on the electronic modification effects on CuO-ZnO-derived electrocatalysts synthesized via hydrothermal synthesis. Although the synthesis method yields spatially separated ZnO nanorods and distinct CuO particles, strong restructuring and intimate atomic mixing occur under the reaction conditions. This leads to interactions that have a profound effect on the catalytic performance. Specifically, all of the bimetallic electrodes outperformed the monometallic ones (ZnO and CuO) in terms of activity for CO production. Surprisingly, on the other hand, the presence of ZnO suppresses the formation of ethylene on Cu, while the presence of Cu improves CO production of ZnO. In situ X-ray absorption spectroscopy studies revealed that this catalytic effect is due to enhanced reducibility of ZnO by Cu and stabilization of cationic Cu species by the intimate contact with partially reduced ZnO. This suppresses ethylene formation while favoring the production of H2 and CO on Cu. These results show that using mixed metal oxides with different reducibilities is a promising approach to alter the electronic properties of electrocatalysts (via stabilization of cationic species), thereby tuning the electrocatalytic CO2 reduction reaction performance.

| S-EPMC11264205 | biostudies-literature

Facet-Dependent Diol-Induced Density of States of Anatase TiO2 Crystal Surface.

Project description:Owing to their fundamental importance and practical applications, anatase TiO2 crystals with well-defined {001} and {101} facets attracted intensive research interests. In this study, we systematically investigated solvent dependence of the photoreaction of the different coexposed crystal facets during noble metal photodeposition. By examining the deposition position in each solvent, we revealed that solvents play a pivotal role on the facet selectivity. On the basis of density functional theory calculations, the solvent molecules were found to modify both the crystal facet electronic structure and the {001}-{001} heterojunction. These modifications are not only the origin of diverse charge-carrier pathways but are also responsible for carrier accumulation at specific facets that increase their reductive power. These findings are vital for a better understanding of photocatalytic materials and an improved design for the next-generation materials.

| S-EPMC5537687 | biostudies-literature

Synthesis and characterization of TiO2/Mg(OH)2 composites for catalytic degradation of CWA surrogates.

Project description:Surface catalyzed reactions can be a convenient way to deactivate toxic chemical warfare agents (CWAs) and remove them from the contaminated environment. In this study, pure titanium oxide, magnesium hydroxide, and their composites TiO2/Mg(OH2) were prepared by thermal decomposition and precipitation of the titanium peroxo-complex and/or magnesium nitrate in an aqueous solution. The as-prepared composites were examined by XRD, XPS, HRTEM, and nitrogen physisorption. Their decontamination ability was tested on CWA surrogates and determined by high-performance liquid chromatography (HPLC) and gas chromatography coupled with mass spectrometry (GC-MS). Dimethyl methyl phosphonate (DMMP) was used as a G simulant for the nerve agents sarin (GB) and soman (GD) while 2-chloroethyl ethyl sulfide (2-CEES) and 2-chloroethyl phenyl sulfide (2-CEPS) were used as surrogates of sulfur mustard (HD). The activity of the as-prepared composites was correlated with acid-base properties determined by potentiometric titrations and pyridine adsorption studied by in situ DRIFTS. The mixing of Ti and Mg led to an increase of the surface area and the amount of surface -OH groups (with an increasing amount of Ti) that caused improved degradation of DMMP.

| S-EPMC9054062 | biostudies-literature

CuO/TiO2/ZnO NPs Anchored Hydrogen Exfoliated Graphene: To Comprehend the Role of Graphene in Catalytic Reduction of p-Nitrophenol.

Project description:The present study deals with sonochemically in situ synthesis of a novel functional catalyst using hydrogen exfoliated graphene (HEG) supported titanium dioxide (TiO2) and copper sulfate (CuSO4) doped with zinc oxide (ZnO) (abbreviated as Ti/Cu/Zn-HEG). The synthesis of the Ti/Cu/Zn-HEG nanocomposite (NCs) catalyst was confirmed through its characterizations by XRD, SEM-EDX, TEM, XPS, FTIR, and BET methods. It was assessed for catalytic conversion of a model aromatic compound para-nitrophenol (p-NP) in an aqueous solution. The p-NP is a nitroaromatic compound that has a toxic and mutagenic effect. Its removal from the water system is necessary to protect the environment and living being. The newly synthesized Ti/Cu/Zn-HEG NCs were applied for their higher stability and catalytic activity as a potential candidate for reducing p-NP in practice. The operating parameters, such as p-NP concentration, catalyst dosage, and operating time were optimized for 150 ppm, 400 ppm, and 10 min through response surface methodology (RSM) in Design-Expert software to obtain the maximum reduction p-NP up to 98.4% at its normal pH of 7.1 against the controls (using HEG, Ti/Cu-HEG, and Zn-HEG). Analysis of variance of the response suggested the regression equation to be significant for the process with a major impact on catalyst concentration and operating time. The model prediction data (from RSM) and experimental data were corroborated well as reflected through model's low relative error (RE < 0.10), high regression coefficient (R2 > 0.97), and Willmott d-index (dwill-index > 0.95) values.

| S-EPMC10652271 | biostudies-literature

Toxicity of ZnO and TiO2 to Escherichia coli cells.

Project description:We performed a comprehensive investigation of the toxicity of ZnO and TiO2 nanoparticles using Escherichia coli as a model organism. Both materials are wide band gap n-type semiconductors and they can interact with lipopolysaccharide molecules present in the outer membrane of E. coli, as well as produce reactive oxygen species (ROS) under UV illumination. Despite the similarities in their properties, the response of the bacteria to the two nanomaterials was fundamentally different. When the ROS generation is observed, the toxicity of nanomaterial is commonly attributed to oxidative stress and cell membrane damage caused by lipid peroxidation. However, we found that significant toxicity does not necessarily correlate with up-regulation of ROS-related proteins. TiO2 exhibited significant antibacterial activity, but the protein expression profile of bacteria exposed to TiO2 was different compared to H2O2 and the ROS-related proteins were not strongly expressed. On the other hand, ZnO exhibited lower antibacterial activity compared to TiO2, and the bacterial response involved up-regulating ROS-related proteins similar to the bacterial response to the exposure to H2O2. Reasons for the observed differences in toxicity and bacterial response to the two metal oxides are discussed.

| S-EPMC5378928 | biostudies-literature

TiO2/Karaya Composite for Photoinactivation of Bacteria.

Project description:TiO2/Karaya composite was synthesized by the sol-gel method for the photoinactivation of pathogens. This is the first time that we have reported this composite for an antimicrobial approach. The structure, morphology, and optical properties were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-rays (EDS), Fourier transform infrared spectroscopy (FTIR), and diffuse reflectance, and the surface area was characterized by the BET method. The XRD and EDS results showed that the TiO2/Karaya composite was successfully stabilized by the crystal structure and pore diameter distribution, indicating a composite of mesoporous nature. Furthermore, antibacterial experiments showed that the TiO2/Karaya composite under light was able to photoinactivate bacteria. Therefore, the composite is a promising candidate for inhibiting the growth of bacteria.

| S-EPMC9267801 | biostudies-literature