Modulating the Tg of Poly(alkylene succinate)s by Inserting Bio-Based Aromatic Units via Ring-Opening Copolymerization.

ABSTRACT: Two series of aliphatic-aromatic copolyesters derived from succinic and 2,5-furandicarboxylic acids, and di-O-2-(hydroxyethyl) resorcinol as diol substituent of either 1,4-butanediol or ethylene glycol, respectively, were obtained by ring opening polymerization(ROP) performed in bulk and catalyzed by Sn(Oct)₂. Cyclic oligomers of furandicarboxylate of di-O-2-(hydroxyethyl) resorcinol were successfully synthesized by high-dilution condensation, and then copolymerized with cyclic oligomers of either butylene or ethylene succinate. The synthesized resorcinol-containing succinate-furanoatecopolyesters had Mw oscillating between 50,000 and 30,000 g·mol-1 depending on composition, and they all displayed a nearly random microstructure. They showed an excellent thermal stability with onset decomposition temperatures near 300 °C. They are amorphous with Tg increasing monotonically with the content in resorcinol in both series with values ranging from -30 or -13 °C for butylene and ethylene-based copolyesters, respectively, up to around 45 °C. The resorcinol-containing succinate-furanoate copolyesters showed appreciable hydrolytic degradation when incubated for a few weeks in water under physiological conditions, a behavior that was notably enhanced in the presence of lipases.

SUBMITTER: Morales-Huerta JC

PROVIDER: S-EPMC6418826 | biostudies-literature | 2017 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Modulating the Tg of Poly(alkylene succinate)s by Inserting Bio-Based Aromatic Units via Ring-Opening Copolymerization.

Morales-Huerta Juan Carlos JC Martínez de Ilarduya Antxon A Muñoz-Guerra Sebastián S

Polymers 20171212 12

Two series of aliphatic-aromatic copolyesters derived from succinic and 2,5-furandicarboxylic acids, and di-O-2-(hydroxyethyl) resorcinol as diol substituent of either 1,4-butanediol or ethylene glycol, respectively, were obtained by ring opening polymerization(ROP) performed in bulk and catalyzed by Sn(Oct)₂. Cyclic oligomers of furandicarboxylate of di-O-2-(hydroxyethyl) resorcinol were successfully synthesized by high-dilution condensation, and then copolymerized with cyclic oli ...[more]

PMID: 30966003

Similar Datasets

Project description:Thermoplastic elastomers benefit from high elasticity and straightforward (re)processability; they are widely used across a multitude of sectors. Currently, the majority derive from oil, do not degrade or undergo chemical recycling. Here a new series of ABA triblock polyesters are synthesized and show high-performances as degradable thermoplastic elastomers; their composition is poly(cyclohexene-alt-phthalate)-b-poly(ε-decalactone)-b-poly(cyclohexene-alt-phthalate) {PE-PDL-PE}. The synthesis is accomplished using a zinc(ii)/magnesium(ii) catalyst, in a one-pot procedure where ε-decalactone ring-opening polymerization yielding dihydroxyl telechelic poly(ε-decalatone) (PDL, soft-block) occurs first and, then, addition of phthalic anhydride/cyclohexene oxide ring-opening copolymerization delivers semi-aromatic polyester (PE, hard-block) end-blocks. The block compositions are straightforward to control, from the initial monomer stoichiometry, and conversions are high (85-98%). Two series of polyesters are prepared: (1) TBPE-1 to TBPE-5 feature an equivalent hard-block volume fraction (f hard = 0.4) and variable molar masses 40-100 kg mol-1; (2) TBPE-5 to TBPE-9 feature equivalent molar masses (∼100 kg mol-1) and variable hard-block volume fractions (0.12 < f hard < 0.4). Polymers are characterized using spectroscopies, size-exclusion chromatography (SEC), thermal gravimetric analysis (TGA), differential scanning calorimetry (DSC) and dynamic mechanical thermal analysis (DMTA). They are amorphous, with two glass transition temperatures (∼-51 °C for PDL; +138 °C for PE), and block phase separation is confirmed using small angle X-ray scattering (SAXS). Tensile mechanical performances reveal thermoplastic elastomers (f hard < 0.4 and N > 1300) with linear stress-strain relationships, high ultimate tensile strengths (σ b = 1-5 MPa), very high elongations at break (ε b = 1000-1900%) and excellent elastic recoveries (98%). There is a wide operating temperature range (-51 to +138 °C), an operable processing temperature range (+100 to +200 °C) and excellent thermal stability (T d,5% ∼ 300 °C). The polymers are stable in aqueous environments, at room temperature, but are hydrolyzed upon gentle heating (60 °C) and treatment with an organic acid (para-toluene sulfonic acid) or a common lipase (Novozyme® 51032). The new block polyesters show significant potential as sustainable thermoplastic elastomers with better properties than well-known styrenic block copolymers or polylactide-derived elastomers. The straightforward synthesis allows for other commercially available and/or bio-derived lactones, epoxides and anhydrides to be developed in the future.

Dataset Information

Modulating the Tg of Poly(alkylene succinate)s by Inserting Bio-Based Aromatic Units via Ring-Opening Copolymerization.

Publications

Modulating the T<sub>g</sub> of Poly(alkylene succinate)s by Inserting Bio-Based Aromatic Units via Ring-Opening Copolymerization.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets