Recent Advances in the Development of Nano-Sculpted Films by Magnetron Sputtering for Energy-Related Applications.

ABSTRACT: In this paper, we overview the recent progress we made in the magnetron sputtering-based developments of nano-sculpted thin films intended for energy-related applications such as energy conversion. This paper summarizes our recent experimental work often supported by simulation and theoretical results. Specifically, the development of a new generation of nano-sculpted photo-anodes based on TiO2 for application in dye-sensitized solar cells is discussed.

SUBMITTER: Panepinto A

PROVIDER: S-EPMC7602882 | biostudies-literature | 2020 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Recent Advances in the Development of Nano-Sculpted Films by Magnetron Sputtering for Energy-Related Applications.

Panepinto Adriano A Snyders Rony R

Nanomaterials (Basel, Switzerland) 20201015 10

In this paper, we overview the recent progress we made in the magnetron sputtering-based developments of nano-sculpted thin films intended for energy-related applications such as energy conversion. This paper summarizes our recent experimental work often supported by simulation and theoretical results. Specifically, the development of a new generation of nano-sculpted photo-anodes based on TiO<sub>2</sub> for application in dye-sensitized solar cells is discussed. ...[more]

PMID: 33076579

Similar Datasets

Radio Frequency Magnetron Sputtering Deposition of TiO2 Thin Films and Their Perovskite Solar Cell Applications.

Project description:In this work, we report a physical deposition based, compact (cp) layer synthesis for planar heterojunction perovskite solar cells. Typical solution-based synthesis of cp layer for perovskite solar cells involves low-quality of thin films, high-temperature annealing, non-flexible devices, limitation of large-scale production and that the effects of the cp layer on carrier transport have not been fully understood. In this research, using radio frequency magnetron sputtering (RFMS), TiO2 cp layers were fabricated and the thickness could be controlled by deposition time; CH3NH3PbI3 films were prepared by evaporation &immersion (E &I) method, in which PbI2 films made by thermal evaporation technique were immersed in CH3NH3I solution. The devices exhibit power conversion efficiency (PCE) of 12.1% and the photovoltaic performance can maintain 77% of its initial PCE after 1440 h. The method developed in this study has the capability of fabricating large active area devices (40 × 40 mm(2)) showing a promising PCE of 4.8%. Low temperature and flexible devices were realized and a PCE of 8.9% was obtained on the PET/ITO substrates. These approaches could be used in thin film based solar cells which require high-quality films leading to reduced fabrication cost and improved device performance.

| S-EPMC4668551 | biostudies-literature

Fabrication of black aluminium thin films by magnetron sputtering.

Project description:Black aluminium thin films were prepared by direct current (DC) pulsed magnetron sputtering. The N2 concentration in the Ar-N2 mixture that was used as the deposition atmosphere was varied from 0 to 10%, and its impact on the film growth and optical properties was studied. A strong change in the film growth process was observed as a function of the N2 concentration. At a specific N2 concentration of ∼6%, the Al film growth process favoured the formation of a moth-eye-like antireflective surface. This surface morphology, which was similar to the structure of a cauliflower, is known to trap incident light, resulting in films with a very low reflectivity. A diffuse reflectivity lower than 4% was reached in the ultraviolet-visible-near infrared (UV-VIS-NIR) spectral range that corresponds to a value observed for an ultrahigh absorber. We found that for the preparation of black aluminium, the nitrogen content plays an important role in film formation and the resulting film morphology.

| S-EPMC9054304 | biostudies-literature

Optically Active TiO2:Er Thin Films Deposited by Magnetron Sputtering.

Project description:Titanium dioxide photoanodes for hydrogen generation suffer from a profound mismatch between the optical absorption of TiO2 and the solar spectrum. To solve the problem of low solar-to-chemical efficiency, optically active materials are proposed. In this work, TiO2 thin films containing erbium were deposited by radio frequency RF magnetron sputtering under ultrahigh vacuum conditions UHV. Morphology, structural, optical and electronic properties were studied. TiO2:Er thin films are homogenous, with uniform distribution of Er ions and high transparency over the visible VIS range of the light spectrum. However, a profound 0.4 eV blue shift of the fundamental absorption edge with respect to undoped TiO2 was observed, which can be attributed either to the size effect due to amorphization of TiO2 host or to the onset of precipitation of Er2Ti2O7 nanocrystals. Near-infrared NIR to VIS up-conversion is demonstrated upon excitation at 980 nm, while strong green photoluminescence at 525 and 550 nm occurs upon photon absorption at 488 nm.

| S-EPMC8348420 | biostudies-literature

Growth of nanostructured Cu<sub>3</sub>Al alloy films by magnetron sputtering for non-enzymatic glucose-sensing applications.

Project description:Enzymatic glucose sensors usually exhibit excellent sensitivity and selectivity but suffer from poor stability due to the negative influence of temperature and humidity on enzyme molecules. As compared to enzymatic glucose sensors, non-enzymatic counterparts are generally more stable but are facing challenges in concurrently improving both sensitivity and selectivity of a trace amount of glucose molecules in physiological samples such as saliva and sweat. Here, a novel non-enzymatic glucose sensor based on nanostructured Cu3Al alloy films has been fabricated by a facile magnetron-sputtering followed by controllable electrochemical etching approach. Since the metal Al is more reductive than Cu, by selectively etching aluminum in the Cu3Al alloys, nanostructured alloy films were obtained with increased surface contact area and electrocatalytic active sites which resulted in enhanced glucose-sensing performance. Thus, non-enzymatic glucose sensors based on nanostructured Cu3Al alloy films not only exhibited a high sensitivity of 1680 μA mM-1 cm-2 but also achieved a reliable selectivity to glucose without interference by other species in physiological samples. Consequently, this study sparked the potential for the development of non-enzymatic biosensors for the continuous monitoring of blood glucose levels with high sensitivity and impressive selectivity for glucose molecules.

| S-EPMC10198095 | biostudies-literature

Formation of Thin NiGe Films by Magnetron Sputtering and Flash Lamp Annealing.

Project description:The nickel monogermanide (NiGe) phase is known for its electrical properties such as low ohmic and low contact resistance in group-IV-based electronics. In this work, thin films of nickel germanides (Ni-Ge) were formed by magnetron sputtering followed by flash lamp annealing (FLA). The formation of NiGe was investigated on three types of substrates: on amorphous (a-Ge) as well as polycrystalline Ge (poly-Ge) and on monocrystalline (100)-Ge (c-Ge) wafers. Substrate and NiGe structure characterization was performed by Raman, TEM, and XRD analyses. Hall Effect and four-point-probe measurements were used to characterize the films electrically. NiGe layers were successfully formed on different Ge substrates using 3-ms FLA. Electrical as well as XRD and TEM measurements are revealing the formation of Ni-rich hexagonal and cubic phases at lower temperatures accompanied by the formation of the low-resistivity orthorhombic NiGe phase. At higher annealing temperatures, Ni-rich phases are transforming into NiGe, as long as the supply of Ge is ensured. NiGe layer formation on a-Ge is accompanied by metal-induced crystallization and its elevated electrical resistivity compared with that of poly-Ge and c-Ge substrates. Specific resistivities for 30 nm Ni on Ge were determined to be 13.5 ??·cm for poly-Ge, 14.6 ??·cm for c-Ge, and 20.1 ??·cm for a-Ge.

| S-EPMC7221967 | biostudies-literature

Multitarget Reactive Magnetron Sputtering towards the Production of Strontium Molybdate Thin Films.

Project description:X-ray photoelectron spectroscopy was used to study the direct synthesis of strontium and molybdenum oxide thin films deposited by multitarget reactive magnetron sputtering (MT-RMS). Sr and Mo targets with a purity of 99.9% and 99.5%, respectively, were co-sputtered in an argon-oxygen gas mixture. The chamber was provided with an oxygen background flow plus an additional controlled oxygen supply to each of the targets. We demonstrate that variation in the power applied to the Mo target during MT-RMS enables the production of strontium and molybdenum oxide films with variable concentrations of Mo atoms. Both molybdenum and strontium were found in the oxidized state, and no metallic peaks were detected. The deconvoluted high-resolution XPS spectra of molybdenum revealed the presence of several Mo 3d peaks, which indicates molybdenum bonds in a lower valence state. Contrary to the Mo spectra, the high-resolution strontium Sr 3d spectra for the same samples were very similar, and no additional peaks were detected.

| S-EPMC10056819 | biostudies-literature

Resistive Switching Characteristics of Li-Doped ZnO Thin Films Based on Magnetron Sputtering.

Project description:A kind of devices Pt/Ag/ZnO:Li/Pt/Ti with high resistive switching behaviors were prepared on a SiO2/Si substrate by using magnetron sputtering method and mask technology, composed of a bottom electrode (BE) of Pt/Ti, a resistive switching layer of ZnO:Li thin film and a top electrode (TE) of Pt/Ag. To determine the crystal lattice structure and the Li-doped concentration in the resulted ZnO thin films, X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) tests were carried out. Resistive switching behaviors of the devices with different thicknesses of Li-doped ZnO thin films were studied at different set and reset voltages based on analog and digital resistive switching characteristics. At room temperature, the fabricated devices represent stable bipolar resistive switching behaviors with a low set voltage, a high switching current ratio and a long retention up to 104 s. In addition, the device can sustain an excellent endurance more than 103 cycles at an applied pulse voltage. The mechanism on how the thicknesses of the Li-doped ZnO thin films affect the resistive switching behaviors was investigated by installing conduction mechanism models. This study provides a new strategy for fabricating the resistive random access memory (ReRAM) device used in practice.

| S-EPMC6515171 | biostudies-literature

Organic-Inorganic Perovskite Films and Efficient Planar Heterojunction Solar Cells by Magnetron Sputtering.

Project description:Organic-inorganic halide perovskites have been widely used in photovoltaic technologies. Despite tremendous progress in their efficiency and stability, perovskite solar cells (PSCs) are still facing the challenges of upscaling and stability for practical applications. As a mature film preparation technology, magnetron sputtering has been widely used to prepare metals, metallic oxides, and some semiconductor films, which has great application potential in the fabrication of PSCs. Here, a unique technology where high-quality perovskite films are prepared via magnetron sputtering for controllable composition, solvent-free, large-area, and massive production, is presented. This strategy transforms the perovskite materials from powder to thin films by magnetron sputtering and post-treatment (vapor-assisted treatment with methanaminium iodide gas and methylamine gas treatment), which is greatly favorable to manufacture tandem solar cells. The power conversion efficiency (PCE) of PSCs with perovskite films fabricated by magnetron sputtering is 6.14%. After optimization, high-performance perovskite films with excellent electronic properties are obtained and stable PSCs with excellent reproducibility are realized, showing a PCE of up to 15.22%. The entirely novel synthetic approach opens up a new and promising way to achieve high-throughput magnetron sputtering for large-area production in commercial applications of planar heterojunction and tandem PSCs.

| S-EPMC8596124 | biostudies-literature

Study of Gallium-Doped Zinc Oxide Thin Films Processed by Atomic Layer Deposition and RF Magnetron Sputtering for Transparent Antenna Applications.

Project description:Gallium-doped zinc oxide (GZO) films were fabricated using RF magnetron sputtering and atomic layer deposition (ALD). The latter ones demonstrate higher electrical conductivities (up to 2700 S cm-1) and enhanced charge mobilities (18 cm2 V-1 s-1). The morphological analysis reveals differences mostly due to the very different nature of the deposition processes. The film deposited via ALD shows an increased transmittance in the visible range and a very small one in the infrared range that leads to a figure of merit of 0.009 Ω-1 (10 times higher than for the films deposited via sputtering). A benchmarking is made with an RF sputtered indium-doped tin oxide (ITO) film used conventionally in the industry. Another comparison between ZnO, Al:ZnO (AZO), and Ga:ZnO (GZO) films fabricated by ALD is presented, and the evolution of physical properties with doping is evidenced. Finally, we processed GZO thin films on a glass substrate into patterned transparent patch antennas to demonstrate an application case of short-range communication by means of the Bluetooth Low Energy (BLE) protocol. The GZO transparent antennas' performances are compared to a reference ITO antenna on a glass substrate and a conventional copper antenna on FR4 PCB. The results highlight the possibility to use the transparent GZO antenna for reliable short-range communication and the achievability of an antenna entirely processed by ALD.

| S-EPMC9933467 | biostudies-literature

Enhanced Electrical Properties of Copper Nitride Films Deposited via High Power Impulse Magnetron Sputtering.

Project description:High Power Impulse Magnetron Sputtering (HiPIMS) has generated a great deal of interest by offering significant advantages such as high target ionization rate, high plasma density, and the smooth surface of the sputtered films. This study discusses the deposition of copper nitride thin films via HiPIMS at different deposition pressures and then examines the impact of the deposition pressure on the structural and electrical properties of Cu3N films. At low deposition pressure, Cu-rich Cu3N films were obtained, which results in the n-type semiconductor behavior of the films. When the deposition pressure is increased to above 15 mtorr, Cu3N phase forms, leading to a change in the conductivity type of the film from n-type to p-type. According to our analysis, the Cu3N film deposited at 15 mtorr shows p-type conduction with the lowest resistivity of 0.024 Ω·cm and the highest carrier concentration of 1.43 × 1020 cm-3. Furthermore, compared to the properties of Cu3N films deposited via conventional direct current magnetron sputtering (DCMS), the films deposited via HiPIMS show better conductivity due to the higher ionization rate of HiPIMS. These results enhance the potential of Cu3N films' use in smart futuristic devices such as photodetection, photovoltaic absorbers, lithium-ion batteries, etc.

| S-EPMC9415204 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data