Preparation of TiO2/WO3/C/N Composite Nanofibers by Electrospinning Using Precursors Soluble in Water and Their Photocatalytic Activity in Visible Light.

ABSTRACT: Extending the absorption range of TiO2 nanofibers to visible light is a great improvement of the photocatalytic property of TiO2. In this study, TiO2/WO3/C/N nanofibers were prepared by electrospinning using precursors soluble in water then annealing in argon. Titanium(IV) bis(ammonium lactato)dihydroxide (TiBALDH) and ammonium metatungstate (AMT) were used as the precursor for TiO2 and WO3 respectively. Different volume ratios of the precursors were added to a solution of PVP before electrospinning. The fibers were studied by XPS, SEM-EDX, TEM, FTIR, XRD, Raman spectroscopy and UV-VIS diffuse reflectance spectroscopy (DRS). The photocatalytic degradation of methylene blue by the fibers in visible light was investigated. The fibers had anatase TiO2 and monoclinic WO3. Based on UV-VIS DRS and Kubelka-Munk function the fibers could absorb visible light. Moreover, 100% TiBALDH had an indirect band gap of 2.9 eV, and the band gap decreased with increase in AMT, i.e., for 0% TiBALDH, band gap was 2.4 eV. The fibers degraded methylene blue dye in visible light, and 90% TiBALDH had the highest photocatalytic activity, i.e., it degraded 40% of the dye after 240 min.

SUBMITTER: Odhiambo VO

PROVIDER: S-EPMC7912636 | biostudies-literature | 2021 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Preparation of TiO2/WO3/C/N Composite Nanofibers by Electrospinning Using Precursors Soluble in Water and Their Photocatalytic Activity in Visible Light.

Odhiambo Vincent Otieno VO Mustafa Chra Rasool M CRM Thong Le Ba LB Kónya Zoltán Z Cserháti Csaba C Erdélyi Zoltán Z Lukác István Endre IE Szilágyi Imre Miklós IM

Nanomaterials (Basel, Switzerland) 20210201 2

Extending the absorption range of TiO2 nanofibers to visible light is a great improvement of the photocatalytic property of TiO2. In this study, TiO2/WO3/C/N nanofibers were prepared by electrospinning using precursors soluble in water then annealing in argon. Titanium(IV) bis(ammonium lactato)dihydroxide (TiBALDH) and ammonium metatungstate (AMT) were used as the precursor for TiO2 and WO3 respectively. Different volume ratios of ...[more]

PMID: 33535415

Similar Datasets

Project description:Metformin is a drug commonly used for the treatment of type 2 diabetes. However, it has been associated with damaging side effects when used over a long period of time. A potential solution to this problem is the implementation of a prolonged-release system for metformin, which would enhance the efficiency of the doses administered to patients. To achieve this, it is necessary to use materials compatible with humans. Electrospinning is an efficient technique that can be employed for this purpose, utilizing solvents that are safe for human use. Therefore, the objective of this study was to prepare and characterize a system for the prolonged release of metformin from zein and gelatin through coaxial electrospinning as well as to investigate its in vitro release. Metformin-loaded zein/gelatin coaxial nanofibers were prepared using the coaxial electrospinning technique and then characterized by morphological, structural, and thermal analysis. Morphologically, metformin-loaded zein/gelatin coaxial nanofibers were obtained with an average diameter of 322.6 ± 44.5 nm and a smooth surface. Fourier transform infrared spectroscopy (FTIR) analysis showed band shifts at a higher wavenumber due to drug-protein interactions by hydrogen bonding between N-H and C=O groups. Thermal gravimetric analysis (TGA) results suggested a possible interaction between materials due to an increase in the degradation temperatures of zein and gelatin when metformin was included. The transition of the crystallinity of metformin to the amorphous form was also confirmed by differential scanning calorimetry (DSC). Coaxial nanofibers exhibited an encapsulation efficiency of 66% and a profile release that showed an initial release of metformin (40%) in the first hour, followed by a gradual release until it reached equilibrium at 60 h and a cumulative release of 97% of metformin. It was concluded that using the coaxial electrospinning technique, it is possible to obtain nanofibers from polymeric solutions of zein and gelatin to encapsulate metformin, with a potential application as a prolonged-release system.

Dataset Information

Preparation of TiO2/WO3/C/N Composite Nanofibers by Electrospinning Using Precursors Soluble in Water and Their Photocatalytic Activity in Visible Light.

Publications

Preparation of TiO<sub>2</sub>/WO<sub>3</sub>/C/N Composite Nanofibers by Electrospinning Using Precursors Soluble in Water and Their Photocatalytic Activity in Visible Light.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets