Nanoporous Gold Biointerfaces: Modifying Nanostructure to Control Neural Cell Coverage and Enhance Electrophysiological Recording Performance.

ABSTRACT: Nanostructured neural interface coatings have significantly enhanced recording fidelity in both implantable and in vitro devices. As such, nano-porous gold (np-Au) has shown promise as a multifunctional neural interface coating due, in part, to its ability to promote nanostructure-mediated reduction in astrocytic surface coverage while not affecting neuronal coverage. The goal of this study is to provide insight into the mechanisms by which the np-Au nanostructure drives the differential response of neurons versus astrocytes in an in vitro model. Utilizing microfabricated libraries that display varying feature sizes of np-Au, it is demonstrated that np-Au influ-ences neural cell coverage through modulating focal adhesion formation in a feature size-dependent manner. The results here show that surfaces with small (≈30 nm) features control astrocyte spreading through inhibition of focal adhesion formation, while surfaces with large (≈170 nm and greater) features control astrocyte spreading through other mechanotransduction mechanisms. This cellular response combined with lower electrical impedance of np-Au electrodes significantly enhances the fidelity and stability of electrophysiological recordings from cortical neuronglia co-cultures relative to smooth gold electrodes. Finally, by leveraging the effect of nanostructure on neuronal versus glial cell attachment, the use of laser-based nanostructure modulation is demonstrated for selectively patterning neurons with micrometer spatial resolution.

SUBMITTER: Chapman CAR

PROVIDER: S-EPMC5471629 | biostudies-literature | 2017 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Nanoporous Gold Biointerfaces: Modifying Nanostructure to Control Neural Cell Coverage and Enhance Electrophysiological Recording Performance.

Chapman Christopher A R CAR Wang Ling L Chen Hao H Garrison Joshua J Lein Pamela J PJ Seker Erkin E

Advanced functional materials 20161212 3

Nanostructured neural interface coatings have significantly enhanced recording fidelity in both implantable and in vitro devices. As such, nano-porous gold (np-Au) has shown promise as a multifunctional neural interface coating due, in part, to its ability to promote nanostructure-mediated reduction in astrocytic surface coverage while not affecting neuronal coverage. The goal of this study is to provide insight into the mechanisms by which the np-Au nanostructure drives the differential respons ...[more]

PMID: 28626362

Similar Datasets

Project description:Monoliths of nanoporous gold (np-Au) were modified with self-assembled monolayers of octadecanethiol (C18-SH), 8-mercaptooctyl α-D-mannopyranoside (αMan-C8-SH), and 8-mercapto-3,6-dioxaoctanol (HO-PEG2-SH), and the loading was assessed using thermogravimetric analysis (TGA). Modification with mixed SAMs containing αMan-C8-SH (at a 0.20 mole fraction in the SAM forming solution) with either octanethiol or HO-PEG2-SH was also investigated. The np-Au monoliths modified with αMan-C8-SH bind the lectin Concanavalin A (Con A), and the additional mass due to bound protein was assessed using TGA analysis. A comparison of TGA traces measured before and after exposure of HO-PEG2-SH modified np-Au to Con A showed that the non-specific binding of Con A was minimal. In contrast, np-Au modified with octanethiol showed a significant mass loss due to non-specifically adsorbed Con A. A significant mass loss was also attributed to binding of Con A to bare np-Au monoliths. TGA revealed a mass loss due to the binding of Con A to np-Au monoliths modified with pure αMan-C8-SH. The use of mass losses determined by TGA to compare the binding of Con A to np-Au monoliths modified by mixed SAMs of αMan-C8-SH and either octanethiol or HO-PEG2-SH revealed that binding to mixed SAM modified surfaces is specific for the mixed SAMs with HO-PEG2-SH but shows a significant contribution from non-specific adsorption for the mixed SAMs with octanethiol. Minimal adsorption of immunoglobulin G (IgG) and peanut agglutinin (PNA) towards the mannoside modified np-Au monoliths was demonstrated. A greater mass loss was found for Con A bound onto the monolith than for either IgG or PNA, signifying that the mannose presenting SAMs in np-Au retain selectivity for Con A. TGA data also provide evidence that Con A bound to the αMan-C8-SH modified np-Au can be eluted by flowing a solution of methyl α-D-mannopyranoside through the structure. The presence of Con A proteins on the modified np-Au surface was also confirmed using atomic force microscopy (AFM). The results highlight the potential for application of carbohydrate modified np-Au monoliths to glycoscience and glycotechnology and demonstrate that they can be used for capture and release of carbohydrate binding proteins in significant quantities.

Dataset Information

Nanoporous Gold Biointerfaces: Modifying Nanostructure to Control Neural Cell Coverage and Enhance Electrophysiological Recording Performance.

Publications

Nanoporous Gold Biointerfaces: Modifying Nanostructure to Control Neural Cell Coverage and Enhance Electrophysiological Recording Performance.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets